收缩温度

差示扫描量热（DSC）分析鸡骨胶原纤维收缩温度为65.9℃；

The shrinkage temperature of chicken bone collagen fibre was 65.9 ℃ by DSC analysis .

CO2超临界流体介质中酶脱毛后铬鞣的革，在本实验条件下其收缩温度达到95℃左右，高于常规酶脱毛后铬鞣的革。

The shrinkage temperature of the leather tanned with chrome after enzyme unhairing in SCF-CO_2could reach 95 ℃, higher than that in the contrasted conditions .

基于模糊PID皮革收缩温度测定仪控制系统设计

Design Detection Instrument for Shrinking Temperature of Leather Based on Fuzzy PID

本文研究了在不同p~H值、浓度、温度条件下，胶原与N（β羟乙基）恶唑烷（OX2）作用后其收缩温度Ts升高的基本规律。

The Ts in creasing of collagen has been studied at various pH values , concentrations and temperatures during the interaction .

差示扫描量热测定ASC和PSC的热收缩温度分别为99.6℃和81.7℃。

The shrinkage temperature of ASC and PSC was 99.6 ℃ and 81.7 ℃ respectively by means of differential scanning calorimetry .

用1%的Cr2O3即可制得收缩温度高于100℃、物理机械指标符合国家标准的成革。

The physical properties of the leather produced by 1 % Cr 2O 3 and 2 % degraded product can satisfy the national standards .

收缩温度介于70～85℃之间。

The shrinkage temperature is between 70 ℃ and 85 ℃ .

钢筋混凝土结构收缩温度应力的分析及构造措施

Analysis of temperture stress and shrinkage of reinforced concrete and structrual measures

毛被松散、灵活、有光泽，成革收缩温度在80℃以上。

The Ts of finished leather is over 80 ℃ .

甲醛鞣液浓度对兔皮收缩温度的影响

The Influence of the Formaldehyde Concentration on the Contracted Temperature of Hare Hide

加热介质对皮革收缩温度的影响

The influence of heating mediums on leather shrinkage temperature

皮革收缩温度的计算机测定研究

Study on Computerized Measurement of Leather Shrinkage Temperature

皮革收缩温度的检测与实现

Measuring and implementing of shrinkage temperature of leather

混凝土收缩温度应力及构造措施

Temperature Stress of Concrete Shrinkage and Constructional Measures

戊二醛改性后脱细胞真皮基质的收缩温度大大提高，但是抗撕裂能力减弱；

The acellular dermal matrix modified by glutaraldehyde increased in shrinkage temperature while tear resistance declined ;

新型无铬鞣剂的分子尺寸与鞣革收缩温度关系的研究

Study on Relationship of Shrinkage Temperature and Molecular Size of Novel Chrome - free Tanning Agent

试验表明：有助于铬的吸收，不降低收缩温度，使铬鞣革更加柔软。

The results showed that absorption of chrome and softness of chrome-tanned leathers were improved and shrinkage temperatures didn 't decrease .

同时对鞣后革的收缩温度、物理机械性能等进行了测试。

At the same time , the shrinkage temperature ( Ts ), physical and machine properties of the leather have been tested .

试验表明阴离子型聚氨酯树脂复鞣剂可提高铬鞣革的收缩温度及力学强度。

The results showed that anion aqueous PU resin retanning agent can improve the shrinkage temperature and mechanics strength of chrome tanned leather .

结果显示，该白湿皮粒面细致、革身丰满、收缩温度达到78℃。

The results show that wet-white leathers treated , with the shrinkage temperature to 78 ? ℃, give fine grains and better fullness .

环氧化合物改性后脱细胞真皮基质的拉伸强度大幅度提高，收缩温度也相应提高。

And the acellular dermal matrix modified by epoxy compound is improved a lot in tensile strength and a certain increase in shrinkage temperature .

管材扩张后能恢复原位，其热收缩温度为105~130℃，纵向收缩率为5.9%，满足使用要求。

The tube could involute after expansion and satisfy the use requirement with thermal contraction temperature being 105-130 ℃ and longitudinal shrinkage being 5.9 % .

实验中主要以坯革的收缩温度和废液含铬量作为考察指标。

The Shrinkage Temperature ( Ts ) of the wet - blue leather and the amount of chrome in exhausted solution are main object to be examined .

用有机酸铬液鞣革收缩温度高，铬吸收好，废液含铬量低，尤以加洒石酸钠及邻苯二甲酸钠的鞣液的鞣革综合效果最好。

The addition of salts of organic acids in chrome tanning results in higher shrinkage temperature , better take-up of chrome and lower quantities of Chrome oxide in spent liquors .

以上各品质性状，除皮板的规定负荷伸长率随年龄增长而下降外，其余各性状均随年龄增长而增加（皮厚、有花面积所占比例和收缩温度在6月龄羔皮又有所下降）。

Except stretched rate descended following growth of age , the other quality properties increased ( depth of lambskin , rate of floriferous area and contract temperature in 6 months descended ) .

应用栲胶搭配三种合成鞣剂对山羊皮进行鞣制，发现栲胶搭配改性嗯唑烷鞣制能提高革收缩温度98℃以上，但所得革力学性能较差，无法达到山羊服装革的性能要求；

The shrinkage temperature of leather tanned with mimosa extract and Oxazolidine reached 98 ℃, but its physical test results were so bad that were not able to meet the requirement of goat clothing leather .

试验结果表明，利用本工艺生产的獭兔皮毛皮成品质轻、板薄、柔软，具有良好的可塑性，毛被松散、灵活、有光泽，收缩温度在80℃以上。

Beaver rabbit skin fur was manufactured using the technique with these virtues , including light weight , thin skin , tenderness , loose hair-covering , brightness and so on , and its shrinkage temperature was over 80 ℃ .

单独稀土鞣革的收缩温度为62℃.植鞣的收缩温度为83℃，而两者结合鞣为102℃，并且这种结合鞣革有良好的手感及强度。

The leather tanned with rare earth has a shrinkage temp , 62 ℃ and 83 ℃ with vegetable tanning extract and then 102 ℃ with rare earth - vegetable tannin extract . The combination tanning leather has also good handle and strength .

栲胶搭配氨基树脂鞣剂鞣制所得革收缩温度能够超过85℃，革粒面较细致且富有弹性，抗张强度能达到山羊服装革的性能要求，但在撕裂强度和伸长率方面存在缺陷；

Leather tanned with mimosa extract and amine resin syntan got the shrinkage temperature up to 85 ℃ and successfully meet the requirement of tensile strength of goat clothing leather with good grain and elasticity , but was weak at elongation ratio and tearing load .

但用水蒸气作为加热介质测收缩温度时，革样出现脱鞣现象不明显，此时测得的结果能较准确地体现革样的耐湿热稳定性。

The results prove that water and glycerol were less appropriate than steam to be used as heating medium to measure the leather shrinkage temperature , they do greater harm to the effects of tanning , the stability to wet and heat and physical-mechanical properties .