门尼焦烧

结果表明，加入SDT/S和TP/S会缩短门尼焦烧时间，但能提高硫化平坦模量和改善抗硫化返原能力；

The results showed that the Mooney scorch time was reduced , and the plateau modulus and the reversion resistance was improved by adding SDT / S and TP / S ;

结果表明，纳米氧化锌减量（25%）替代间接法氧化锌，钢丝粘合胶和胎肩胶的门尼焦烧时间延长，而气密层胶的门尼焦烧时间缩短；

The results showed that the replacement of indirect zinc oxide by nano-zinc oxide with 25 % loss in weight resulted in the extended Mooney scorch time for steel-bonded compound and shoulder compound , and the reduced Mooney scorch time for inner liner compound ;

表面活性剂单独使用或与ZnO、MgO并用均可硫化氟丁橡胶CR-1211，且能明显延长混炼胶的门尼焦烧，改善橡胶的加工性，提高硫化胶的物理机械性能。

Cationic surfactants could vulcanize CR - 1211 either alone or together with ZnO and MgO , with much better scorch resistance and processability , as well as better mechanical properties of vulcanizate .

聚合产物具有稳定的门尼粘度，焦烧时间、抗张强度、扯断伸长率、永久变形、定伸应力等物理性能。

The polymerization product has a stable Mooney viscosity , scorch time , tensile strength , elongation at break , permanent deformation , modulus and other physical properties .

结果表明，试验温度对胶料的门尼粘度、门尼焦烧时间和硫化特性均有一定影响。

The results showed that the test temperature had certain influence on the Mooney viscosity , Mooney scorch time and curing behavior of rubber compound ;

用纳米氧化锌减量替代间接法氧化锌，胶料的门尼粘度下降，门尼焦烧时间延长，硫化特性基本保持不变；

The results showed that the Mooney viscosity of compound decreased , the Mooney scorch time extended and the curing behavior changed little by using nano-zinc oxide in reduced weight instead of indirect zinc oxide ;