金刚石镀钛层的研究

Research of diamond titanium coating

用镀Ti金刚石制成的铜基合金磨块对花岗岩的磨削比与不镀钛金刚石相比提高30%。

The grinding ratio of samples made from Ti-clad diamond is 30 % higher than that without clad diamond .

通过AFM、SEM和TEM等分析方法，研究了镀钛（碳化钛）层的结构特征；

The structure characteristics of Ti-coated diamond are investigated by means of AFM , SEM , TEM and XRD .

镀钛层与金刚石之间的结合强度随镀覆温度提高而增加，经1023～1073K、1h真空微蒸发镀钛后，界面结合强度高于150MPa。

The interface bonding strength between diamond and the coating increases with the rising of depositing temperature and reaches above 150 MPa after coating at 1023-1073 K for Ih .

由于镀层的保护作用，镀钛金刚石的热稳定性提高，在空气中的起始氧化温度为1230K，明显高于未镀覆金刚石。

The coating also can protect diamond from oxidizing . The start oxidation temperature of coated diamond grits reaches as high as 1230 K.

本文利用真空炉中钎焊的方法，采用Ni-Cr合金钎料，适当控制钎焊温度，保温时间和冷却速度，实现了镀钛金刚石与钢基体的高强度连接。

In this paper , vacuum furnace brazing test was carried out using Ni-Cr alloys as brazing filler metals . Proper brazing temperature , heat preservation time and cooling speed helped to realize a strong bonding between Ti-coated diamond and steel substrate .

测定了蒸镀钛（VE-Ti）、离子镀钛（IP-Ti）、氮化钛（TiN）和添加钇改性的氮化铁（Ti（Y）N）镀层在两种酸性腐蚀介质中的极化曲线；

The polarization curves , separately in two kinds of acid corrosion medium , of the coatings of vacuum vapor Ti ( VE-Ti ), ionic Ti ( IP-Ti ), TiN and [ Ti ( N ) N ] modified by adding yttrium are measured ;

镀覆合金的超硬磨料，如镀钛&铬合金的金刚石；真空微蒸发镀覆之后再经电镀形成的多层复合镀超硬磨料，如复合镀Ti-Ni的金刚石等。

The superhard abrasives include diamond with single-layer coating such as Ti-coated or W-coated diamond , superhard abrasives with alloy-coating such as Ti / Cr coated diamond , superhard abrasives with electroplated coating layer after the vacuum micro evaporation coating , such as Ti / Ni compound coated diamonds .

离子镀钛和氮化钛镀层的电化学腐蚀特征

The Characteristics of Electrochemical Corrosion of Ionic Ti & TiN Coating

镀钛超硬材料微粉及应用

Ti Coated Superhard Abrasive Micro - powder and its Industrial Uses

关于镀钛金刚石产品发展的若干问题

Some Problems in the Development of Ti Clad Diamond Products

金刚石表面熔盐法镀钛的研究

Research on Ti-plated diamond surface by molten salt process

在离子注入刚结束时，氮离子注入纯铁镀钛样品表面并没有氮化钛化合物的出现。

The nitrogen ion implanted Ti-layer coated iron samples were studied during vacuum annealing .

金刚石表面镀钛对金刚石锯片性能的影响

Effect of Ti - coated on diamond surface on properties of diamond saw blade

离子镀钛和氮化钛膜的结构与耐蚀性

Correlation of structure of ion plated Ti and tin films with its corrosion resistance

镀钛金刚石与结合剂间的结合状态

Bonding States Between Ti-Coated Diamonds and Matrices

纯铜离子渗镀钛层的耐蚀性STEACS组血浆T。

Plasma level of T.

介绍了合肥电子储存环新凸轨注入系统中将采用的超高真空陶瓷镀钛真空室的研制状况。

Status of developing a coated ceramic chamber for the new injection bump system of the HLS ring is presented .

循环沉积10次镀硅、镀钛的样品，镀层厚度适中，抗拉强度值也最高。

The tensile strength of the compacts sintered from 10 times deposited samples is the highest for the proper thickness of the coating .

镀钛金刚石工具工业应用结果表明，镀钛使金刚石锯片工作面上脱落的金刚石减少，完好和微破碎形态的金刚石增加；

The industrial application confirms that applying the coated diamond in metal bond tools changes the wear stages of the diamond on the working face .

如果你相信鬃毛或叉状顶部与常见的木质顶部会使击球距离产生显著的变化，那么我有一座表层镀钛的桥，你要不要买？

If you believe the frictional differences between prongs or bristles and the usual wooden platform will result in a noticeable change in distance , I have a titanium-faced bridge I 'd like to sell you .

试验了采用表面镀钛金刚石制造的金刚石锯片的干切情况。（3）研究了采用预合金粉末合理设计胎体配方及金刚石参数。胎体粉末预合金化，能有效改善金刚石锯齿的烧结工艺和机械性能。

Tested the dry-cutting situation of the diamond saw-blades which manufactured by Ti coated diamonds . ( 3 ) Used pre-alloyed powders to design reasonable matrix formula , which can improve the sintering and mechanical properties of diamond saw-blades effectively .