镀铬
- chromate treatment;chrome-plating;chroming;chromium-plating
-
研究了钨表面镀前处理及预镀铬、镍,然后镀金的工艺条件;
The paper studied the pre treatment for electroplating the surface of tungsten and technical conditions for chromate treatment , nickel and gold plating , determined the functions of cladding material .
-
通过对摩托车活塞环的激光表面处理试验研究,发现激光处理的活塞环硬化层厚度和硬度与镀铬环相当,避免了镀铬环镀层剥离的缺点。
The paper studies the laser surface treatment of motorcycle piston ring . The experimental result : The hardness and thickness of hardened layer of laser treatment piston ring are equivalent to chromate treatment , the laser treating ring avoid the shortcoming of decollement .
-
能量色散X荧光光谱法测定碳钢表面的镀铬层厚度
Determination of the thickness of chromium coating on carbon steel by EDXRF
-
BF4~-离子选择性电极测定三价镀铬液中的H3BO3
Determining h_3bo_3 in three-valence chromium-plating solution with bf_4 ~ - ion-selective electrode
-
PLC和VVVF在镀铬自动生产线上的应用
Applications of PLC VVVF in Automatic Production Line of Chromium Plating
-
CS镀铬液的稳定性是人们关注的重要问题。
The stability of CS chromeplate liquid is the important problem of people attention .
-
镀铬层在Na2S溶液中的耐蚀性研究
Study on Corrosion Resistance of Chromium Coating In Na_2S Solution
-
作者采用液膜处理镀铬废水中的有毒Cr~(6+)离子,使之达到国家废水排放标准。
The poison C_r ~ ( 6 + ) in chromium - plating waste wate is handled by liquid membrane , in order to accord with the drain standard .
-
提出了用EDTA为络合剂的三价铬镀铬新工艺。
This is a review on trivalent Cr plating with EDTA as complexing agent .
-
镀铬阳极选用3CoCr合金的阳极保护作用导致钴离子释出量少量增加。
Selection of Cr plating anodes 3 Co release from Co-Cr alloy slightly increased which induced by the Co-Cr alloy anodic protection .
-
以Cr(Ⅲ)尿素体系为基础,选择了合适的添加剂,建立了新的甲酸甲醇尿素体系三价铬镀铬工艺。
Based on Cr (ⅲ) - urea system , a new formic acid-methanol-urea Cr (ⅲ) plating system is established through choosing proper additives .
-
该方法可用于镀铬溶液和铬酸钝化液中Cr(Ⅵ)和Cr(Ⅲ)含量的测定。
The method can be applied to the determination of Cr (ⅵ) and Cr (ⅲ) in chromium plating bath and chromic acid passivation bath .
-
络合滴定法测定镀铬液的H2SO4
Complexometric Titration of H_2SO_4 in Chromium Plating Solution
-
以Zn-Ni合金为底层的装饰性镀铬工艺研究
A Study on Decorative Cr Plating Process with Zn-Ni as Its Undercoat
-
直接金驼褪色光度法测定镀铬溶液中Cr(Ⅵ)三价铬硫酸盐溶液镀硬铬的辅助配位剂研究
Determination of Cr (ⅵ) in Chrome Plating Solution by Direct Brown 1 Discoloring Spectrophotometry Effect of auxiliary coordination agent in the deposition of chromium from chromic sulfate electrolyte
-
本文论述了镀铬钢领的走熟特性及PTFE(聚四氟乙烯)涂层的作用、配方和涂镀方法。
In this paper , the authors deal with the running-in properties of the chrome plated ring , and the behavior , prescription and operation of PTFR coating .
-
CrO3-H2SO4镀铬液中CrO3含量的快速测定的研究
Studies on Rapid Determination of cro_3 content in cro_3-h_2so-4 type Cr-plating bath
-
CrO3-H2SO3镀铬液中测定CrO4含量的两种方法比较
A comparison of two methods of determining CrO_s content in CrO_3-H_2SO_4 Cr plating bath
-
研究结果表明:镀铬层在Na2S溶液中的腐蚀过程有钝化产生;
Experimental results indicate that corrosion and passivation occur simultaneously at the chromium coating in Na_2S solution .
-
分析了镀铬废水的絮凝效果、Cr(III)溶液絮凝前后杂质的含量及硫酸铬的纯度,选定了最佳pH。
The flocculation effect of chrome plating wastewater , the content of impurities in Cr ( III ) wastewater before and after flocculating and the purity of chromic sulfate were analyzed , and the optimal pH was determined .
-
稀土阳离子在镀铬中的作用介绍了这种转化膜形成的可能机理:膜是由稀土阳离子和由氧还原生成的OH-在铝合金表面通过生成沉淀而形成的;
The possible formation mechanism of REM conversion coating is introduced : The formation of the film centers on the precipitation of the canons of REM and OH ~ - obtained from reduction reaction of O_2 onthe surface of aluminum alloy .
-
虽然他们的工作也许很重要,不过他们就是对车柱上的特殊曲线、肩线上的镀铬和前卫的N辐铝合金轮毂说“不”的人。
Essential though their job may be , they are the ones who say " no " to the special curve in the roof pillar , the extra bit of chrome on the shoulder line , or the fancy spokes on the aluminum wheels .
-
介绍松孔镀铬气缸套的特点、工艺过程及其在金城江机务段东风7D型机车上的运用效果。
The feature , technology process of production and application in DF7D locomotive at Jinchengjiang Locomotive Depot of cylinder liner chromed after excessive wear were presented .
-
制备了纯镀铬和Cr&Al2O3复合镀层,通过若干检测性实验,显微硬度测试,扫描电镜观察和摩擦磨损实验等来研究复合镀层的表面形貌和性能。
The surface of pure chromium coatings and Cr / Al_2O_3 composite coatings were observed and analyzed by scanning electron microscope ( SEM ), hardness was evaluated by micro-hardness instrument , frictional wear was tested by friction wear testing machine .
-
恢复涂层设计尺寸而打磨部件的镀铬层时,本体金属的打磨过热会造成在镀铬层下形成UTM和OTM。
When grinding chrome to finish dimensions , overheating the base metal can create UTM and OTM formations under the chrome .
-
建立了以硫酸亚铁铵作滴定剂,电位滴定法测定镀铬溶液中铬酐(CrO3)含量的方法。
The method determining the chromium trioxide concentration in the Cr-electroplating solution is set up by the electrometric itration with the ferrous ammonium sulfate as the titrant .
-
化学镀Ni-P合金非晶态镀层具有硬度高、耐磨及抗蚀性能好的性能,将这一工艺用于液压缸活塞杆以替代镀铬,取得满意的效果。
Chemical plating of Ni-P alloy uncrystalloid plating features high hardness , excellent wear-resistance and erosion-resistance . Satisfactory effect is achieved when using this process to plate piston rod of hydraulic cylinder instead of using chrome plating .
-
本文描述了一台专用的真空摩擦试验装置,并给出了真空度为10~(-3)托下,PTFE-花岗石、PTFE镀铬铜和PTFE钢球三种摩擦副材料的f-v实验曲线;
The paper describes a special equipment for vacuum friction test , and presents f-v test curves for combinations of PTFE-granite , PTFE-chromium plating steel and PTFE-steel ball in a vacuum of 10-3 Torr .
-
选用BH-88硫酸盐三价铬镀铬工艺。
BH-88 trivalent chromium sulfate plating process was chosen .
-
必须严格遵循排氢程序包括镀铬、磺胺基镍镀层和LHE镀镉检查、剥离和各阶段的回火刻蚀检查程序。
Processes that must be followed with relief baking include chrome , sulfamate-nickel , and LHE cadmium plating ; stripping operations ; and many nital etch inspections .