利用水淬法模拟其服役状况并用有限差分方法对产生的非稳态热应力进行了分析。

The circumstance of service was simulated by water quenching and the thermal stress was analyzed .

本论文以液态钢渣为模拟对象，研究液态钢渣的离心粒化设备水淬法处理技术。

This paper takes steel slag as simulation object , and studies the processing technique of centrifugal graining equipment water quenching method for molten steel slag .

采用直接水淬法成功制备直径5mm球状Zr65Al7.5Cu17.5Ni10大块非晶态合金。

Bulk amorphous Zr 65 Al 7.5 Cu 17.5 Ni 10 alloy was produced by a direct water-quenching method .

水淬法放玻璃水已成为冷修放水的关键技术。

Draining glass melt by water quench has become a key technology to cold repair .

同时简单介绍了熔体水淬法、爆炸焊接法等制备技术。

Some preparation technology , such as the method of water quenching the molten alloy and explosive welding , are briefly introduced .

简述高炉熔渣水淬法处理工艺流程及特点，重点介绍图拉法的工艺特点和应用情况。

The disposals process of water quenching for blast furnace slag and its characteristics were stated briefly , and the technical characteristics of TYNA and its application were introduced mainly .

最后使用水淬法测试了复合材料的抗热震性能并分析复合材料抗热震机理。首先考察了烧结温度、保温时间和烧结压力对材料性能的影响。

At last , thermal shock resistance of composite was tested by water quenching method , and the mechanism was investigated and discussed . Firstly , the effect of sintering temperature , holding time and sintering pressure was investigated .

在离心粒化设备上进行了铝熔液水淬法的模拟粒化试验，结果表明：采用离心粒化设备水淬法的粒化处理是可行的，一般对流动性比较好的处理效果更好。

This equipment was tested by simulation experiment for molten aluminium by water quenching . The experiment indicates that using the centrifugal graining equipment water quenching method for quenching and graining is feasible , and it fit for processing the fluidity is relatively good .

用水淬熄法研究了Ti-B4C-C系自蔓延高温合成（SHS）反应火焰喷涂TiC-TiB2复相陶瓷涂层的反应过程与机理。

Using the self-propagating high-temperature synthesis ( SHS ) technology , the procedure and mechanism of reactive flame spraying TiC-TiB_2 multiphase ceramic coatings with Ti-B_4C-C system were studied by means of water quenching method .