当KH-550与氧氯化锆的物质的量比不低于21时，涂膜PC板的透过率较高，表面较平整；

When the molar ratio of KH-550 to zirconium oxychloride is above 2 , the transparency and surface morphology are excellent .

10000吨氧氯化锆生产工艺的改进研究和经济效益分析

The improvement of 10 thousand tons of zirconium oxychloride production and its economic analysis

本文以氧氯化锆为原料用Sol－Gel技术在多孔陶瓷管上制备了ZrO2膜，文中考察了草酸氧锆溶胶的粒子大小和流动特性；

Zirconia membranes formed on porous ceramic tubes were prepared by Sol-Gel Technique , by using zirconyl chloride as starting material .

以廉价的氧氯化锆（ZrOCl2.8H2O）为锆源，十六烷基三甲基溴化铵（CTAB）为模板剂，制备了介孔氧化锆。

Mesoporous zirconia was prepared by a convenient process with cetyltrimethylammonium bromide ( CTAB ) as templates , and zirconyl chloride octahydrate ( ZrOCl_2 · 8H_2O ) as zirconium resource .

氧氯化锆（ZrOCl2·8H2O）溶胶-凝胶法制备纳米二氧化锆粒子的存在着在制备过程中会发生团聚、后处理程序复杂、影响粉体性能等缺点。

Nano-sized ZrO_2 powder has been prepared by ZrOCl_2 · 8H_2O in sol-gel process in which the powders would agglomerate and would impact their functions . On the other , the process after reaction is complex .

合成有机锆最佳工艺条件为氧氯化锆用量3%，反应时间20min。

In the preparation of organic zirconium complex , the optimum technical parameters are zirconium oxychloride ratio 3 % , reaction period 20 min.

以碳化锆为原料，采用碱熔-水洗-酸浸-结晶工艺制备氧氯化锆，制得的氧氯化锆产品中ZrO2含量达到36.20%。

Zirconium oxychloride with purity of 36.20 % was prepared from zirconium carbide by the process of alkali fusing , water washing , hydrochloric acid leaching and product crystallization .

本文以氧氯化锆和硝酸锰以及硝酸铈为主要原料，采用Sol-Gel（溶胶-凝胶）和共沉法，结合不同的干燥技术制备了不同配比的MnOx/ZrO2和Cu/ZrO2超细纳米催化剂。

In this paper , using mostly ZrOCl_2 · 8H_2O and Mn ( NO_3 ) _2 、 Ce ( NO_3 ) _2 , nano - MnO_x / ZrO_2 and Cu / ZrO_2 catalysts held differ proportion were prepared by the way of Sol-Gel method and co-precipitation .

以C18TAB为模板剂，氧氯化锆和四氯化锡为原料，采用共沉淀法成功合成了不同掺锡量的有序多孔氧化锆。

Tin-doped ordered porous zirconium oxides are successfully synthesized by co-precipitation method using zirconyl chloride and tin chloride as Zr / Sn sources and octadecyltrimethylammonium bromide ( C18TAB ) as template .

氧氯化锆前驱体离子交换法制备氧化锆溶胶

Preparation of zirconia sol by anion exchange method from zirconyl chloride

碱石灰法从铌钽矿富锆尾矿制备氧氯化锆

Preparation Zirconium Oxychloride from Concentrated Zr Tails of Nb-Ta Ore by Lime

利用氧氯化锆副产稀碱液制备五水偏硅酸钠

The preparation of sodium metasilicate pentahydrate from dilute lye of

氧氯化锆是合成锆化学品的重要原料。

Zirconium oxychloride is the important raw material to produce Zirconium chemicals .

碳化锆碱熔制备氧氯化锆的研究

Preparation of Zirconium Oxychloride via Alkali Fusing of Zirconium Carbide

氧氯化锆的生产及其在现代新能源中的应用

The production of zirconium oxychloride and its application in new energy resource

氧氯化锆前驱体氧化锆溶胶的制备与研究

Preparation and Characterization of Stable Zirconia Sol

以氧氯化锆为前驱体，采用溶胶-凝胶法快速制备锆溶胶，凝胶后经煅烧制得氧化锆粉体，分析了锆溶胶的制备、稳定和氧化锆粉体的特性。

The zirconium sol was rapidly prepared by sol-gel method with zirconium oxychloride as precursor reagent .

氧氯化锆水溶液用氨水水解，生成水合氧化锆絮状沉淀，再经过洗涤、陈化、干燥、破碎、筛分、活化处理等几步工艺制成水合氧化锆树脂。

The solution of zirconium oxychloride is hydrolyzed by aqueous ammonia , and hydrated zirconia flocculent is deposited .

水转料中二氧化硅含量降低了，氧氯化锆的使回收率提高了；

The reduction of SiO 2 content in water transformed material improved the recovery rate of zirconium oxychloride ;

一步水热法是将氧氯化锆和氨水按比例混和后，直接加入高压反应釜中进行水热反应的工艺。

ZnO green phosphor preparation process by the thermal oxidation of zinc sulfide with zirconium oxychloride as additive is investigated .

本课题以氧氯化锆、尿素为原料，研究了在水溶液体系中制备纳米氧化锆的改良工艺路线。

This study researched improved process route of nano-zirconia in aqueous solution using zirconium oxychloride and urea as the raw materials .

以氧氯化锆为原料，采用离子交换法制备氧化锆溶胶。

The preparation of zirconia sol by anion exchange method from zirconyl chloride as raw material was introduced in this paper .

以甲醛、苯酚、氧氯化锆为原料合成了高残碳锆酚醛树脂。

Phenolic resin modified with zirconium and with high char yield was synthesized with formaldehyde , phenol and zirconyl chloride as raw materials .

在氧氯化锆溶液中加入Er3+盐和Yb3+盐得到的稀土掺杂纳米二氧化锆在远红外下可发出荧光。

If adding the compounds of Er ~ ( 3 + ) and Yb ~ ( 3 + ) in zirconium oxy-chloride solution , the obtained adulterated nano-zirconia shows far-IR activated fluorescence .

采用动态水热法，以江西产天然粉石英、河北井陉产石灰为原料，加入少量的氧氯化锆为添加剂合成硬硅钙石晶体。

Xonotlite was obtained based on dynamic hydrothermal process by using natural powder quartz of Jiangxi Province and lime of Jingjing County , Hebei Province as major raw materials . Zirconium oxychloride was used as an additive .

以三氯化铝、氧氯化锆为原料，经离子交换溶胶-凝胶法在α-Al2O3中空纤维载体制备了Al2O3/ZrO2膜。

A method of using aluminium chloride and zirconyl chloride as precursors by ion exchange sol-gel route for preparation of Al2O3 / ZrO2 composite membranes on α - Al2O3 hollow fiber substrate was introduced in this paper .

介绍以铝矾土提取硫酸铝废渣和氧氯化锆副产废碱液为原料生产泡花碱，然后利用一次造粒法生产五水偏硅酸钠新工艺确定影响产品质量指标工艺因素。

A new process in which a foam alkali can be produced by taking aluminum sulfate residue and waste alkali liquid of zirconium oxychloride as its raw materials , and then sodium metasilicate pentahydrate being made by one shot slag forming is introduced .