将Al、Pb粉末按照Al225Pb（at%，下同）的配比进行了机械合金化，并对AlPb合金的物相、晶粒尺寸、点阵常数作了测定和分析。

The powders of Al-2.25Pb ( at % , hereinafter same ) were performed by mechanical alloying . Phase transformation , crystalline grain size and lattice constant of Al-Pb milled powders were determined and analyzed .

在其它工艺条件不变的情况下，后者的平均晶粒尺寸小于前者。

In the situation that other technical conditions keep unchanged , the average crystalline grain size for the latter is smaller than for the former .

其中，b峰和c峰对冷却速度敏感，晶粒尺寸越小，峰的强度越大。

Peak b and c are sensitive to cooling rate .

激光烧蚀制备纳米Si晶粒尺寸均匀性与靶衬间距的关系

Relation between target-substrate separation and size-uniformity of Si nanoparticles prepared by laser ablation

半固态喷射沉积TiCp／7075铝合金的晶粒长大规律

Grain growth law of semi-solid state tic_p / 7075 Al alloy prepared by spray deposition

陶瓷α-Al2O3晶粒度的测定技术分析

Measuring Technique of the Grain Size of Ceramic α - Al_2O_3

锻烧工艺对α-Al2O3晶粒的影响

Effect of Calcining Process on α - alumina Crystal Size

溶剂热法合成YAG晶粒的形成过程

Formation process of YAG grains synthesized by solvothermal method

在LED分拣设备中，晶粒的位置信息是至关重要的，它为整个的分拣工作提供了基本参数信息。

In the LED sorting equipment , the dies location information is essential and works for the entire basic parameter information .

合理地解释了反应温度、溶液中的pH值对制得的氧化锌微晶的形态、晶粒粒度的影响。

The effects of reaction temperature and the pH of solutions on the morphology and the particle size are reasonably explained .

燃烧合成法中诸因素对纳米晶Y2O3晶粒尺寸的影响

Influences of Different Factors on the Grain Size of the Nanocrystalline Y_2O_3 in Combustion Synthesis

MgO的晶粒大小和晶格畸变与水化活性的关系

Relationship between Crystalline Size and Lattice Distortion of MgO and its Activity

剩磁曲线分析表明Cu的加入不能明显降低晶粒间交换耦合作用。

The analysis for the remanence curves show that the addition of Cu can not decrease the intergranular interaction obviously .

抑制硬质合金烧结中WC晶粒长大的研究

Inhibition of WC Grain Growth during Sintering of Cemented Carbide

由SEM照片观察到分子筛膜表面平整，分子筛晶粒均匀，膜厚约为20μm；

As observed from SEM photos , the surface of membrane was flat and the thickness was 20 μ m.

LD2合金锻件淬火粗大晶粒形成规律的研究

Study on the Formation of Coarse grains in Forged LD_2 Alloy Pieces after Quenching

La改性的Ni/α-Al2O3催化剂中活性组分晶粒大小和粒度分布

Investigation of crystal size and particle size distribution of active component in the La modified nickel catalyst

双相TiAl基合金断裂应变与晶粒大小的关系

Relationship between fracture strain and grain size of two-phase TiAl-base alloys

微合金元素V抑制形变诱导铁素体相变的进行，阻碍铁素体晶粒长大，起到细化晶粒的作用。

Vanadium restrains the deformation induced ferrite transformation but hinders the grain growth of ferrite and acts as a grain refinement .

分解后的两相组织晶粒细小，使衍射峰宽化，扫描电镜观察以及Xray衍射分析表明：分解产物随等温时间延长粗化不明显。

The SEM and X-ray diffraction analysis showed that the coarsening of decomposed structure was not evident even after long time treatment .

电池用EMD的晶粒度和物相组成

Crystal Size and Phase Components of Electrolytic Manganese Dioxide Used in Battery

共沉淀制备ZrO2（MgO）前驱物的相及晶粒的发育

Evolution of Phase and Grain of Precursor of MgO-ZrO_2 Fabricated by Coprecipitation

扩散火焰法控制TiO2纳米晶粒径和晶型的研究

Control of Size and Crystal Form of TiO_2 Nanocrystalline Synthesized by Co-flow Diffusion Flames

并利用品的X射线衍射谱测出了微粒样品的相结构、晶格常数值和晶粒线度值。

The phase structure , the lattice constant , crystal grain diameter of the samples was obtained by the X-ray diffractions ( XRD ) spectra .

小晶粒SAPO-34分子筛的合成I.化学合成法

Synthesis of Small Crystal SAPO-34 Molecular Sieve I. Chemical Method

双层细晶粒Glass／Al／BiGaDyIG薄膜的磁光性能

Magneto-optical Properties of Double Layer Glass / Al / BiGaDyIG Fine Grain Thin Film

通过改变原料WC的晶粒度及组成来制取非均匀结构硬质合金。

The cemented carbide with inhomogeneous grain structure is prepared by different kind of raw material WC .

前文已简述模拟二维正常晶粒生长所采用的基本蒙特卡罗（MonteCarlo）方法。

The fundamental Monte Carlo methods for simulating normal grain growth in two dimensions had been briefly introduced in our last paper .

另外，从烧结样品SEM断面形貌图中可以看出，有晶粒异常长大。

Additionally , from the fractured surface of sintered samples , it can be seen that the grain grows abnormal , with big grain .

微量Sc和Zr对Al-Mg合金铸态组织的晶粒细化作用

Effect of trace Sc and Zr on grain refinement of as cast Al Mg alloys