常压塔顶316L不锈钢换热器管束的腐蚀失效分析

Corrosion of heat exchanger pipe bundle of 316L stainless steel for distillation tower overhead

通过宏观、金相观察、X射线衍射及SEM等方法分析了炼油厂常压塔顶316L不锈钢换热器管束的腐蚀形态及原因。

By means of macro inspection , X ray diffraction , scanning electron microscope , optical microscopy and EDS , corrosion of heat exchanger pipe bundle of 316L stainless steel for a distillation tower overhead was analyzed .

18-8不锈钢换热器裂纹失效研究与分析

Research and Analysis of 18-8 Stainless Steel Heat Exchanger Crack Failure

Cl~-引起的不锈钢换热器失效及其防护

Stainless Steel Heat Exchanger Failure Caused by Cl - and Protection

不锈钢换热器管束断裂原因初探

Preliminary Study on Cracking Causes of Stainless Steel Heat Exchanger Tubes

不锈钢换热器管板产生裂纹的原因分析

Cause Analysis on Cracking of Stainless Steel Heat Exchanger Tubesheet

双相不锈钢换热器设计制造技术

Technique of Heat Exchanger 's Design and Manufacture with Duplex Stainless Steel

氧化塔内置盘管式不锈钢换热器的失效分析

Failure Analysis of Built-In Coil Heat Exchangers of Stainless Steel in Oxidation Towers

介绍了不锈钢换热器的腐蚀情况。

The corrosion status of the heat exchanger of the stainless steel was described .

不锈钢换热器板片泄漏原因分析

Leak analysis on stainless steel radiator board

不锈钢换热器的焊缝腐蚀与选型

Corrosion of Welding Line & Choice of the Type for Heat - exchanger of Stainless Steel

本文以己内酰胺装置中不锈钢换热器为研究背景，运用不锈钢腐蚀研究理论及成果对三台典型的不锈钢换热设备的失效形式进行了腐蚀分析与对策研究。

The corrosion behavior and protective methods of three typical stainless steel heat exchangers in hexanolactam apparatus were studied in this paper .

不锈钢波纹管换热器的腐蚀与防护

Corrosion and protection of the ripple pipe heat exchanger of stainless steel

介绍一种不锈钢盘管式换热器，主要用于家用小型中央空调。

Presents a kind of new heat exchanger for the domestic central air-conditioning system .

多层不锈钢波纹管换热器的研制与运行测试

Development and trial run of heat exchanger of multi-layer stainless steel bellows tube bank

鉴于此，研制了多层不锈钢波纹管换热器，可使管内流体产生扰动，形成内壁的涡旋流，破坏边界层和污垢层的厚度，并增加换热系数。

Therefore a heat exchanger of multi-layer stainless steel bellows tube bank is developed , which can produces flow disturbance in the tube and prevents fouling and plugging and increases the heat exchange coefficient .

相对于传统的管壳式换热器，小型不锈钢板翅式换热器传热效果好、体积小、费用低，因此不锈钢板翅式换热器在工业上得到广泛的应用。

Compared with traditional shell and tube heat exchangers , compact plate-fin heat exchangers made of brazed stainless steel have advantages of superior heat transfer capability , small size and low cost , and it has been widely used in industry .