不烧砖

镁铝尖晶石不烧砖的研制与应用

Development and application of magnesia-alumina spinel unburned brick

结合攀钢活性石灰回转窑的生产实际，研制开发了镁铝尖晶石不烧砖。

The magnesia-alumina spinel unburned brick was developed in accordance with the actual production situation of active lime rotary kiln of Pangang Metallurgy Material Co.

Al2O3SiCC不烧砖抗渣性能的热力学分析

Thermodynamic Analysis on the Slag Resistance of A1_2O_3-SiC-C Unburned Bricks

结果表明，氯氧镁水泥能明显提高不烧砖（110℃×24h和1600℃×3h）耐压强度；

The results show that magnesium oxychloride cement can improve cold crushing strength ( 110 ℃× 24h , 1600 ℃× 3h ) of unburnt brick significantly .

采用氯氧镁水泥为结合剂制备铝镁质无碳不烧砖，研究了MgCl2·6H2O和镁砂含量对材料物理性能的影响。

Using magnesium oxychloride cement as binder , carbon-free unburnt alumina magnesia based brick is prepared . Effects of MgCl_ ( 2 )· 6H_ ( 2 ) O and magnesia on physical properties of brick are studied in this paper .

高铝质不烧砖的生产及其在水泥窑上的应用

Production of high alumina unfired brick and its application on cement kiln

铝镁碳不烧砖在我厂钢包上的应用

Applications of Unburned AMC Bricks on Ladles of Our Plant

添加物对磷酸盐结合高铝不烧砖性能的影响

The effects of additives on the properties of phosphate-bonded unburned alumina bricks

钢包用无碳不烧砖的研制

Study on carbon - free unfired brick for ladles

矾土-尖晶石钢包不烧砖的蚀损研究

Study on corrosion of bauxite-spinel unfired bricks for ladle

氯氧镁水泥结合铝镁质无碳不烧砖性能的研究

Study on Properties of Carbon - free Unburnt Brick Bonded by Magnesium Oxychloride Cement

研究结果表明：这些添加物都有望提高不烧砖的高温性能。

The study shows that those additives are useful to improve the properties of unburned bricks under high temperature .

随着镁砂含量的增加，不烧砖高温下低熔相量减少，镁铝尖晶石生成量增加，材料的组织结构变疏松，常温耐压强度逐渐降低。

With the increase of magnesia content , liquid phase content in brick decreases at high temperature and spinel formation increases which further leads to loosening and gradually lowered strength of brick .