铁红

ICP-AES法测定氧化铁红中的二氧化硅

ICP-AES determination of silicon dioxide in iron oxide red

铁泥氧化制备颜料铁红的研究

Study on preparing iron oxide red from waste iron mud by oxidation

Fe（OH）3凝胶两步法水热制备均分散针形铁红胶粒

Preparation of Uniform Acicular Hematite Particles by Two Steps Hydrothermal Method from Fe ( OH ) _3 Gel

由对苯二甲酸（PTA）废料酯化合成的聚酯树脂再与重芳烃、锌粉、铁红、石墨及固化剂等制得防腐抗静电油罐涂料。

An anticorrosive and antistatic coating for storage tank was prepared with PTA wastes and heavy arenes .

通过红外光谱、热分析、表面Zeta电位测试分析研究其改性作用，结果表明：改性剂通过物理吸附和化学吸附作用于超细铁红粒子表面；

The surface modification mechanism of the modifier was studied by testing samples with IR , Thermal analysis and zeta potential .

着重研究了纳米Fe2O3对铁红醇酸底漆的改性作用和纳米Fe2O3加入方式。

The function of nanometer Fe_2O_3 for iron red alkyd primer and way of adding into coating are mainly introduced .

溶解进入浸出液中的Fe、Mg可综合回收制备铁红及达国标（GB9004-88）优等级轻质氧化镁等产品。

The ions of magnesium and iron dissolved in the leach liquor may be comprehensively utilized to produce iron oxide red and high class light magnesium oxide examined by the national standard ( GB9004-88 ) .

即用稀酸浸出的方法将蛇纹石中的MgO溶解以大幅降低最终精矿中MgO含量从而获得低镁优质精矿；同时，对进入浸出液的Mg、Fe等综合回收产出铁红、轻质氧化镁等产品。

The MgO of serpentine is dissolved by diluted sulfuric acid so as to reduce MgO content of the final concentrate greatly . The ions of magnesium and iron dissolved in leaching solution can be utilized to produce iron oxide red and light magnesium oxide comprehensively .

同时将铁回收为铁红产品（含Fe2O3≤65%），铁的实收率高达88%。

At the same time , the iron is recovered in the form of iron oxide ( iron red , content of Fe_2O_3 ≥ 65 % ), the yield of iron is 88 % .

用红土取代酚醛防锈漆中氧化铁红，辅以钛酸酯偶联剂，制出F53-33铁红酚醛防锈漆。

Iron red replaced by red clay , titanate as coupling agent , F53-33 iron red phenolic anti-rust paint qualified has been prepared .

东化公司的GH602环氧铁红底漆是双组份、胺加成物固化的环氧底漆，GH102环氧陶瓷面漆是双组份、胺加成物固化的环氧面漆。

Donghua 's GH602 Iron-red Epoxy Primer is a two-part amine-adduct cured epoxy primer ; and GH102 Ceramic Epoxy Topcoat is a two-part amine-adduct cured epoxy topcoat .

为保持铁红的针形结构，锻烧温度不能超过600OC，在500℃时锻烧2小时为宜。

In order to keep acicular structure of ferric red the calcining temperature can not exceed 600 ℃ . It is suitable for ferric yellow to calcine two hours in 500 ℃ .

从萃铟余液中生产高纯铁红的研究

Producing High Purity Ferric Oxide from Waste Solution in Indium Metallurgy

用硫酸亚铁全液相合成颜料铁红的研究

Complete liquid phase synthesis of ferric oxide pigment & a study

用焙烧分解法生产铁红等产品

Use the Roasting Decomposition Method to Produce Iron Red and Other Products

硫酸盐湿法铁红晶种生成过程研究

Study on iron red crystal seed formation from sulphate by wet process

水性铁红丙烯酸防锈漆的研究

Study on aqueous iron red acrylic anti - rust paint

氨法铁红晶种转化机理探讨

Discussion on Mechanism of Seed Crystal Conversion of Ammonium Process Red Iron Oxide

含少量镍、铜的铁红渣的综合利用

Comprehensive Utilization of Iron Oxide Slag Containing Trace Amount of Nickel and Copper

某铁红回收厂选别流程优化研究

Study on Ore Dressing Process Optimization in One of Iron Oxide Recovery Plant

米糠油改性环氧酯铁红防锈底漆的研究

Study on Rice Bran Oil Modified Epoxy Ester Iron Oxide Red Antirust Primer

制备均分散铁红微粉的新方法

A New Method of Preparing Uniform Hematite Superfine Powder

由米糠油合成铁红环氧酯底漆的研究

Synthesis of epoxy ester priming paint of iron oxide red from rice bran oil

氧化作用会使钢铁生锈。铝粉铁红聚酯防锈漆

Aluminium powder red iron oxide polyester anti-rust paint

氨法铁红晶种成因分析及氧化合成铁红的历程探讨

Forming of seed crystal in ammonia-process red iron oxide production and the oxidizing process

磷酸镁铵沉淀法处理铁红含氨氮废水

Wastewater treatment of iron oxide red containing NH_4 ~ + - N by magnesium ammonium phosphate

钛酸酯偶联剂在红土制铁红酚醛防锈漆中的应用研究

Application of titanate coupling agent in iron red phenolic anti - rust paint with red clay

那里的土壤呈锈红色。铝粉铁红聚酯防锈漆

The soils have a rusty red tint . aluminium powder red iron oxide polyester anti-rust paint

这种以硫酸渣为原料制备高挡铁红的工艺尚属首次报导。

This process of the iron red that is made from sulfuric acid slag is first reported .

无矿化剂作用下，锆铁红陶瓷颜料的开始形成温度约为1100℃；

The formation of iron zircon pink pigment starts at approximately 1100 ℃ when lacking of mineralizer .