远红外陶瓷

远红外陶瓷远红外陶瓷
  1. 本论文以对苯二甲酸二甲酯(DMT)、乙二醇(EG)为原料,远红外陶瓷粉作改性剂,采用间歇式聚合方法合成远红外功能聚酯。

    This article provides a process for preparation of farinfrared ceramic functional polyester by means of interrupted stepwise from dimethyl terephthalate , ethylene glycol , farinfrared ceramics powder as modifier .

  2. 分别采用固相合成法和液相共沉淀法制备远红外陶瓷粉体,采用X射线小角散射法测试其颗粒分布和平均粒度,采用XRD分析其物相和SEM观察其显微结构形貌。

    Liquid phase codeposition method and solid phase synthesis are adopted separately to prepare far-infrared radiating ceramic powders . Particle size distribution and average diameter are tested by small-angle X-ray scattering . Phase composition is analyzed by XRD and microstructure is observed by SEM .

  3. 介绍了远红外陶瓷材料发射辐射的机理。

    The machanism of the far infrared ceramic radiation was introduced .

  4. 纳米远红外陶瓷粉体材料的研究与应用

    Study on Nanometre Far - infrared Ceramic Powders and Application

  5. 纳米远红外陶瓷粉体的制备工艺与性能研究

    Studies on the processing techniques and properties of nanometre far-infrared ceramic powders

  6. 远红外陶瓷对家兔实验性骨折愈合的影响

    Far-infrared pottery macromolecule bandage for fracture healing of rabbits experimentally

  7. 燃烧效率燃烧室效率常温远红外陶瓷材料提高燃油燃烧效果的研究

    Study on Improving Combustion Efficiency of Oil by Using Room-temperature Far-infrared Ceramic Materials

  8. 远红外陶瓷介质对花椰菜与青椒生长的影响

    Effect of Far infrared Ceramics Medium on Promoting the Growth of Cauliflower and Green Pepper

  9. 着重论述了烧结温度和烧结助剂对远红外陶瓷性能的影响。

    The influence of temperature and agglutinant on the properties of the far infrared radiation ceramics was discussed .

  10. 本研究分别采用固相合成法和液相共沉淀法制备远红外陶瓷粉体。

    Liquid phase codeposition method and solid phase synthesis are adopted separately to prepare far-infrared radiating ceramic powders in this study .

  11. 研究了远红外陶瓷介质浸泡水对花椰菜和青椒生长发育的影响。

    It was researched that far infrared ceramics medium soaked in water could affect the growth and development of cauliflower and green pepper .

  12. 本文采用一种新的数字图像相关方法测量带有半导体电热膜的远红外陶瓷热胀系数。

    A new digital image correlation method ( DICM ) measurement is utilized to investigate the thermal expansion coefficient of the far-infrared ceramic coated the semiconductor galvanothermy membrane .

  13. 探讨远红外陶瓷材料用于燃油节能、降低大气污染的机理,提出了远红外陶瓷材料及电气石制成各种涂料的特性及应用,这是治理大气环境污染的新途径。

    The function of using Far-infrared ceramic material in saving fuel and decrease air pollution , is discussed . The new way of treatment for environment pollution by application of far-infrared ceramic material and tourmaline coating is suggested .

  14. 对远红外陶瓷作用原理进行阐述和对远红外纤维的保健功能原理进行论述。通过对远红外腈纶与羊毛混纺产品的开发,提出了该类产品的使用价值。

    The paper elaborates the action of far infrared ceramic and the health care function of far infrared fibre , and raises the using value of far infrared acrylic fibre and wool blending product with the develop of them .

  15. 结果表明,液相共沉淀法制备的远红外陶瓷粉体的平均粒度达到95纳米,且颗粒大小分布窄,而固相合成法制备的远红外陶瓷粉体颗粒粗大且不均匀。

    The results show that far-infrared ceramic powders average diameter by liquid phase codeposition method is 95.nm and narrow distribution . While the granules of far-infrared powders by solid phase synthesis are gross and particle size difference long adds .

  16. 结果表明,远红外陶瓷介质水对花椰菜和青椒有促进生长、提高产量的作用,花椰菜平均单球重达630g,与对照差异极显著;

    This result indicated that far infrared ceramics medium soaked in water could promote growth and increase yield of cauliflower and green pepper . The average mass of single cauliflower reached 630 g , and the comparative difference was very marked .

  17. 远红外辐射陶瓷纤维&X1对人体血液流变学和血液动力学影响的研究

    Effect of Far-Infrared Radiation from Porcelain Fibre-x_1 on Human Hemorheology and Hemodynamics

  18. 远红外功能陶瓷的防污性能研究

    Study on anti - fouling performance of far infrared ceramics

  19. 阐述了远红外辐射陶瓷(粉)的组成及制备方法。

    The composition and preparation method of far infrared radiation ceramics were described .

  20. 谷物干燥远红外复合陶瓷材料的研究

    Study on Far-infrared Composite Ceramics Material for Grain Drying

  21. 低温远红外辐射陶瓷材料研究

    Study on Low-temperature Far-IR Radiant Ceramic Materials

  22. 目的:观察应用远红外辐射陶瓷作为盖髓剂进行盖髓术的临床疗效。

    Objective : to observe the clinical effect of far-infrared radiation ceramic applied in pulp capping .

  23. 一种新型的具有表面复合层的煤气远红外多孔陶瓷板的结构和性能

    The Structure and Properties of a new Infrared Radiation Porous Ceramic Plate Having Composite Layer Used on Gas Stoves

  24. 对工业废渣粉煤灰在远红外功能陶瓷的应用进行了相关实验和讨论分析。

    In this paper , the application of fly ash , the industrial waste , on the far-infrared functional ceramics was discussed .

  25. 方法:深龋患者90例110个恒牙应用自行研制的远红外辐射陶瓷作为盖髓剂进行直接盖髓术12个牙,间接盖髓术98个牙。

    Method : 90 cases of 110 teeth with deep carries was pulp capping with self prepared far-infrared radiation ceramic in which 12 teeth is directly pulp capping and 98 teeth are indirectly pulp capping .

  26. 基于远红外辐射特性陶瓷坯体的干燥机理

    Principle of drying ceramic of far-infrared radiation

  27. 锆钛系远红外谷物干燥复合陶瓷辐射器的研发

    Study on Zirconium and Titanium Far-infrared Grain Drying Compound Ceramics Radiant

  28. 确定了锆钛系远红外谷物干燥复合陶瓷辐射板的原料配方。

    The material 's formula of Zirconium and Titanium far-infrared grain drying compound ceramics radiant was made certain .

  29. 制备出了符合国家日用瓷质量标准、且具有高的远红外辐射性能的远红外日用陶瓷釉。

    The daily-used ceramic glaze with high far-infrared radiation was prepared , which measured up to the national daily-used ceramic qualities standard .

  30. 本文首先介绍远红外技术的基本知识,远红外辐射体材料和陶瓷远红外辐射体的各种结构形式。

    First , this paper presented the fundamental knowledge of far-infrared technology , the far-infrared radiant materials and the various construction forms of radiant ceramics .