本质晶粒度

  • 网络Inherent grain size
本质晶粒度本质晶粒度
  1. 当W(Ti)e>0.031%时,试验用钢的奥氏体本质晶粒度可达7级以上,晶粒粗化温度提高到980℃以上。

    When ω( Ti ) e content is more than 0.031 % , the austenite inherent gain size and the grain coarsening temperature of the steel could be up to grade 7 and 980 ℃ respectively .

  2. 本文还研究了不同预处理工艺对奥氏体本质晶粒度的影响。

    The influence of different pretreatment process on the austenitic essence grain was studied too .

  3. 60Si2MnRE钢中夹杂物、微观组织和本质晶粒度的研究

    The Study of the Occluded Foreign Substance , Microscopic Structure and Grain Fineness Number in Substance of the 60Si_2MnRE Steel