补强剂

  • 网络Reinforcing agent;I-H-N
补强剂补强剂
  1. 探讨补强剂种类和用量对酚醛树脂硫化BIIR胶料性能的影响。

    The effect of the type and addition level of reinforcing agent on the properties of ( phenolic ) resin-cured BIIR was investigated .

  2. 通过对粘土进行物理和化学改性,可制成橡胶补强剂,其补强效果接近或达到白炭黑水平。

    A reinforcing agent of rubber has been developed by the physical and chemical modification of clay .

  3. 由于补强剂Le粒径较大且表面活性不高,只能采用和白炭黑并用。

    Filler Le Can only adopted with silica as a larger particle size and little surface activity .

  4. 在相同的条件下,纯Al2O3陶瓷的摩擦系数和磨损率较大,而含有增韧补强剂的Al2O3基陶瓷材料的摩擦系数和磨损率较低。

    The friction coefficient and the wear rate of pure Al_2O_3 ceramic were higher than most of Al_2O_3-based ceramics with reinforcing and toughening additives under the same conditions .

  5. SiC晶须和Y-TZP两种补强剂的共同作用,对莫来石强度和断裂韧性的提高具有叠加或协同效应。

    Interaction of Y-TZP and SiC whiskers has a superposition or coordination effect on the improvement of strength and fracture toughness of mullite .

  6. 新型橡胶补强剂Fz-1复合炭黑的应用研究

    Using Study on Fz-1 Complex Carbon Black of New Rubber Reinforcing Agent

  7. 探讨了硫化剂、补强剂和耐热添加剂对甲基乙烯基硅橡胶(MVQ)硫化胶耐热性能的影响。

    The influence of curatives , reinforcing fillers and anti-heat agent on the heat resistance of MVQ vulcanizate was investigated .

  8. 新型橡胶补强剂超细活性陶土SFAC在胶辊中的应用试验

    Application Experiments of New Reinforcer Superfine Actived Clay ( SFAC ) in Rubber Rollers

  9. 新型补强剂&超细活性陶土SFAC

    New Reinforcing Agent-Super Fine Active Clay

  10. 以三聚硫氰酸(TCY)作为丙烯酸酯橡胶的硫化剂,研究了润滑剂、补强剂、酸受体等配合剂对丙烯酸酯橡胶加工及其硫化胶性能的影响。

    The effects of lubrication agents , strengthening agents , acid acceptors on processing technology and properties of acrylate rubber were studied .

  11. 以甲基丙烯酸锌(ZDMA)为补强剂,研究硫化剂DCP用量、ZDMA用量和硫化时间对ZDMA/NR复合材料物理性能的影响。

    The effects of the addition levels of curing agent DCP and zinc methylacrylate ( ZDMA ) and the curing time on the physical properties of ZDMA / NBR composite were investigated .

  12. 天然矿物作为硅橡胶补强剂的研究

    A Study of Natural Mineral as Reinforcing Filler of Silicone Rubber

  13. 表面改性在硅橡胶补强剂制备中的应用

    Surface modification and its application in preparation of silicone rubber reinforcing filler

  14. 新型橡胶补强剂的研究

    A Study on a New Type of Rubber Reinforcer

  15. 新型橡胶补强剂的研制及其应用

    Development of New Rubber Reinforcing Agents and Their Application

  16. 补强剂对三氯溴甲烷改性天然胶乳力学性能的研究

    Research on Mechanics Performance of Trichlorobromomethane Modified Natural Rubber Latex for Reinforcing Agent

  17. 填充补强剂在橡胶基质中分散状态的研究

    Research on dispersed states of the bulking and strengthening agents in the rubber matrix

  18. 研究了硫化时间、补强剂对鼠标垫力学性能的影响。

    This paper studies the effect of curing time and filling on mechanical property of mouse pad .

  19. 结果表明,液态石蜡是改善餐具防水性能的最佳防水剂,海藻酸钠是较好的补强剂。

    The results showed that the best waterproof agent is paraffin ; the best intensifier is sodium alginate .

  20. 对比了粘土/丁苯橡胶纳米复合材料与传统橡胶填充补强剂填充胶料的力学性能。

    The mechanical properties of Clay / SBR nanocomposite were compared with those of SBR which was filled with traditional fillers .

  21. 橡胶及特种电缆补强剂,工业塑料功能填料,油墨、食品、药品、化妆品填料。

    Rubber reinforcing agent and special cables , industrial plastic packing function , ink , food , medicines , cosmetics packing .

  22. 结果表明,补强剂的种类对氟硅橡胶与各类金属粘接的扯离强度有一定的影响;

    The result showed that the types of active filler affected the tear strength of fluorosilicone rubber at the various rubber-metal interfaces ;

  23. 研究证明了在用于橡胶、塑料填充补强剂和催化剂载体等方面,纳米纤维状白炭黑更优于传统白炭黑。

    As the carrier of catalyzer and the filler to reinforce rubber and plastics , nano-fibriform silica shows better performance than traditional silica .

  24. 介绍淀粉的结构、改性淀粉的制备及改性淀粉作为橡胶补强剂的应用情况。

    The structure of the starch , the preparation of modified starch and application of modified starch as rubber reinforcing agent were presented .

  25. 透明白炭黑通常作为丁苯橡胶的补强剂,制成浅透明色的硫化胶鞋底。

    Transparent carbon white is usually used strengthening agent in the shallow transparent rubber , which can make up the vulcanized shoe sole .

  26. 与炭黑的对比试验结果表明,所研制的几种新型补强剂均可替代通用炭黑应用于橡胶制品。

    The test of comparison to carbon blacks showed that the developed new reinforcing agents might replace the general-purpose carbon blacks in rubber products .

  27. 说明在本实验条件下,硼酸铝晶须不适宜作为牙科可切削氟硅云母玻璃陶瓷的补强剂。

    We considered that the aluminum borate whisker was not appropriate for our dental machinable mica based glass-ceramic as a reinforcing agent . 3 .

  28. 并将所得乾粉作为矽橡胶补强剂,讨论其补强机理及不同乾燥产品对其补强性能的影响。

    The products prepared were applied to silicon rubber as a reinforcing agent , while the reinforcing mechanisms and the effects of it were investigated .

  29. 莫来石晶须不但具有莫来石质材料的性能,而且作为长径比大的完整单晶体具有更加优良的力学性能,是一种优异的陶瓷基复合材料和金属基复合材料增韧补强剂。

    Mullite whiskers have not only excellent performances of mullite but also good mechanical properties as a integrity single crystal with the high aspect ratio .

  30. 随着填料细微化技术,特别是表面改性技术的发展,纳米碳酸钙开始作为橡胶补强剂得到研究和应用。

    With the development of technology in superfine filler production and especially in surface modification , calcium carbonate used as reinforcing filler has caught great attention .