旋涂

研究了溶液浓度、旋涂工艺、热处理工艺等工艺参数对ZnO薄膜晶体结构和表面形貌的影响。

We studied the effect of the solution concentration , spin coating condition , and the thermal process ( pre-heated and post-annealed temperature ) on the structure of ZnO films .

该一系列聚合物在普通的有机溶剂里都具有很好的溶解性，可以通过旋涂或喷墨等方法来制备薄膜和器件。

So it is possible to prepare films and devices by solution methods such as spin coating or ink jet printing .

使用旋涂法将其成膜于Si（100）基片之上。

The films formed on the 100 oriented Si substrate .

用溶剂蒸发法和旋涂法将聚合物涂在SAW基片表面。

The polymer was coated on the piezocrystal by two methods of solvent evaporation and spin coating .

旋涂法制备SnO＿2薄膜的XRD、AES研究

XRD 、 AES Research for SnO_2 thin Films Fabricated by Spin

采用sol-gel旋涂法在抛光硅111晶面生长了高度C轴取向的ZnO薄膜。

ZnO thin films with high c-axis orientation were prepared on polished Si 111 substrates by using spin coating method .

掺杂对于旋涂热解法制备TiO2薄膜的影响

Characterization of Doped TiO_2 Film Prepared by Spin-Coating and Pyrolysis

用偶氮染料乙基红（EthylRed，简称ER）掺杂到聚甲基丙烯酸甲酯（PMMA）并用重复旋涂法制成了聚合物薄膜。

Azo dye ethyl red doped polymer ( PMMA ) films were prepared by the spin-coating method .

旋涂SiO2乳胶薄膜形成的Si&SiO2系统的特性研究

The Properties of Si-SiO_2 System Formed by Spun-on Emulsion

采用溶胶-凝胶旋涂法在普通载玻片衬底上制备出Al3+掺杂ZnO（AZO）薄膜。

The A13 + doped ZnO thin films were prepared on glass substrates by Sol-Gel Spinning method .

旋涂-热解法制备WO3薄膜

Preparation of the WO_3 Film by the Spin Coating-Pyrolysis Method

通过旋涂将甲苯稀释的PDMS涂覆在基底表面。

PDMS diluted by toluene was spin-coated on the surface of the Ag .

分别采用TiO2P25纳米粉体涂膜法，分散TiO2P25粉体法，溶胶凝胶法和旋涂法制备了染料敏化TiO2膜。

The TiO2 film was prepared by daubing P25 powder , dispersing P25 power , sol-gel and spin coating .

旋转浓缩-蓄热氧化法处理涂装废气的中试研究掺杂对于旋涂热解法制备TiO2薄膜的影响

Pilot study on treatment of painting exhaust-gas by RC-RTO system Characterization of Doped TiO_2 Film Prepared by Spin-Coating and Pyrolysis

本论文还探讨了利用旋涂法制备TiO2薄膜时，影响薄膜质量、光催化性能的若干因素。

Then some factors that influence the quality and photocatalytic activity of TiO_2 film made by spinning coating are discussed .

采用溶胶-凝胶旋涂法制备ITO薄膜，并将制得的ITO薄膜在空气中用相同的退火温度和不同的退火时间间隔下进行热处理。

ITO films annealed at same annealing temperatures and different annealing time intervals in air by a sol-gel spin coating process .

实验结果表明，用旋涂法实现的PMMA固化后再与多孔硅复合而制得的样品的结果最好，它与原始的多孔硅样品相比，发光峰发生了蓝移而且发光强度下降很小。

Photoluminescence of porous silicon and PS / PMMA composites was investigated . The result shows that the spin coating method is better relatively .

介绍了一种改进旋涂法&DDS涂膜法（Deposit-Dip-Spin-coating），主要用来制备纳米粉体原子力显微镜（AFM）分析样品。

Deposit-dip-spin ( DDS ) coating method , a composite nano-powder sample preparation method for atomic force microscope ( AFM ) measurement is introduced .

本文先制备溶胶，再用旋涂法在载玻片或多孔硅上旋涂溶胶，然后在500℃下退火得到结合牢固的、锐钛相结构的TiO2薄膜。

First sol is prepared , spin coating sol on substrate , then anneal it in 500 ℃ and gain TiO_2 film with anatase structure .

使用旋涂方法在K9玻璃和抛光的单晶硅基片上制备薄膜；

Thin films were prepared on K9 glass and polished single - crystal silicon by spin-coating method .

所制备的AZO薄膜旋涂次数小于7时，薄膜的透光率均达到95%以上，且随膜厚的增加变化不大。

When the number of spin-coating is less than 7 , the transmittance of AZO films shows little changes with thickness , all above 95 % .

研究了PMMA的旋涂成膜工艺，解决了层间互溶、应力开裂、光刻起皱等薄膜表面质量问题；

The spin coating process of PMMA membrane is studied , and the surface-quality problems such as the dissolve among layers , stress crack and lithography crinkle are solved .

溶胶&凝胶旋涂法制备Bi-2212薄膜。

Spin-coating sol-gel method was employed to prepare Bi-2212 film .

采用溶胶凝胶旋涂法在Si（111）衬底上生长了ZnO薄膜，并用荧光光谱、原子力显微镜和XRD对ZnO薄膜样品进行了分析。

Zinc oxide films were prepared on Si ( 111 ) substrates by sol-gel spin-coating technique . Structure , photoluminescence , and surface morphology of ZnO thin films processed at various temperatures and times were investigated .

接着采用旋涂法制备了涂有该聚合物薄膜的QCM传感器，测试了该传感器在室温下对DMMP的敏感特性。

Then the polymer films were prepared on QCM sensors , and the sensitivity to DMMP vapors was researched .

采用水热合成技术，制备了ZrO2胶体，用旋涂法镀制了单层ZrO2介质膜以及添加了有机粘合剂PVP的复合ZrO2-PVP薄膜。

ZrO_2 sol was obtained by using hydrothermal synthesis . Thin ZrO_2 films and ZrO_2-PVP composite films were prepared with spin coating method .

具体工作主要有：探讨旋涂工艺和热处理温度对PLED的影响。

As follow : The effects of spin-coating and heat-treatment parameters on the propertied of PLEDs were discussed .

但旋涂1次的AZO薄膜，它的载流子浓度要低一个数量级，电阻率高一个数量级。

But for the AZO thin films under only one spin-coating , an order of magnitude decrease in carrier concentration and an order of magnitude increase in resistivity are detected .

退火处理前后的旋涂薄膜的吸收光谱的性状和X射线衍射数据说明该化合物的固体薄膜为无定形薄膜，而且高温下退火4h没有明显变化。

The observed absorption features and X-ray diffraction patterns suggested an amorphous state of the spin-coating films , and the annealing treatment at 80 ℃ for 4 h did not change the amorphous property .

本文的研究主要有以下两个部分：一、采用溶胶-凝胶旋涂法制备ITO薄膜，并将制得的ITO薄膜在空气中用相同的退火时间间隔和不同的退火温度条件下进行热处理。

This study is mainly the following two parts : 1 . ITO films annealed at same annealing time intervals and different annealing temperatures in air by a sol-gel spin coating process .