阳极氧化法

  • 网络Anodization;anodic oxidation;one-step anodization
阳极氧化法阳极氧化法
  1. 实验结果表明,要想制备获得高度规则有序的AAO模板,两步阳极氧化法优于一步阳极氧化法。

    The experiment results show that Two-Step Anodization method is better than One-Step Anodization method .

  2. 获得的结论如下:通过改进的两步阳极氧化法所制备的PAA呈六角密排结构、排列规律并且有序。

    The conclusions are as follows : The PAA prepared by the improved two-step anodization approach are hexagonally close-packed , orderly arranged .

  3. 采用电化学阳极氧化法在钛基体上制得了高度致密的、有序的、均匀的TiO2纳米管阵列。

    High-density , well-ordered and uniform titanium oxide nanotube arrays were prepared by electrochemical anodic oxidation .

  4. 溅射&阳极氧化法在釉面砖上制备多彩TiO2膜

    Preparation of multi-colored TiO_2 films on the ceramic substrate by sputtering-anodic oxidation method

  5. 阳极氧化法合成NH4NO3-GICs

    Systhesis of NH_4NO_3-GICs by Anodic Oxidation Method

  6. 在苯胺-硫酸电解液中,采用电化学阳极氧化法在纯铅表面电沉积制备聚苯胺(PAn)膜层。

    A polyaniline ( PAn ) film was deposited onto pure lead in aqueous solutions containing sulfuric acid and aniline by electrochemical anodic oxidation .

  7. 水解沉积&阳极氧化法形成Al-Ti复合氧化膜

    Formation of Al-Ti composite oxide films on aluminum by hydrolysis precipitation and anodizing

  8. 本文介绍Al电极TFT矩阵电路的优越性及其制造工艺&阳极氧化法制造Al2O3膜。

    The paper introduces advantages of aluminum electrode in amorphous-sili-con thin film transistor ( a-Si TFT ) matrix circuit and a simple manufacturing method of Al_2O_3 film by using of anodic oxidation process .

  9. 利用阳极氧化法对半导体材料逐次去层,采用四探针法测量其每层的电阻率及相应杂质浓度,可得出半导体材料的杂质分布N(x)。

    Semiconductor material is removed layer by layer with anode oxidation method . Resistivity and relevant impurity concentration in every layer is measured with four point probe method . The impurity distribution of semiconductor material N ( x ) is obtained .

  10. 采用常规阳极氧化法,研究电解液中各成分和电解规范对复合阳极氧化膜层性能的影响后,提出了添加SiC粉体硫酸溶液中铝的复合阳极氧化工艺。

    Based on the research on the effects of electrolyte composition and electrolytic process parameters on the properties of composite anodizing film with routine anodizing , composite anodizing process of aluminium in sulfuric acid solution added SiC powder was proposed .

  11. 通过电化学阳极氧化法,在纯钛片表面制备得到TiO2纳米管阵列。研究了TiO2纳米管阵列的热稳定性,并通过模拟体液浸泡研究了其生物活性。

    In this paper , TiO2 nanotube arrays was gained on the surface of pure Ti plate by electrochemistry anodic oxidation , investigated the heat stability of TiO2 nanotube arrays and its bioactivity by soak it into simulate body fluid .

  12. 在NaF和H3PO4水溶液体系中,用电化学阳极氧化法在钛板表面形成一层结构规整有序的高密度TiO2纳米管阵列。

    High density , well ordered and uniform titanium oxide nanotube arrays were fabricated on the surface of titanium substrate by electrochemical anodic oxidation in 0.5 M H_3PO_4 + 0.138 M NaF solution .

  13. 室温下采用电化学阳极氧化法在NaF、Na2SO4和H2SO4的混合溶液中用化学处理后的纯Ti片表面组装了一层结构高度有序的高密度TiO2纳米管阵列。

    High density , well ordered and uniform titanium oxide nanotube arrays were fabricated by anodizing process on a pure titanium sheet . Electrochemical anodization was carried out in NaF + Na_2SO_4 + H_2SO_4 electrolyte at room temperature .

  14. 围绕以上内容,我们主要开展了以下三个方面的工作:(1)本文采用阳极氧化法和浸渍电沉积法成功制备了Ru负载的Ti02纳米管阵列电极。

    In this dissertation , some works were carried out as follows : ( 1 ) The Ru / TiO2nanotube array electrodes were fabricated by electrochemical process of anodization , followed by a dipping and electrodeposition technique .

  15. 以氢氟酸为支持电解质,用阳极氧化法在钛片上直接制备出TiO2纳米管电极,纳米管顶部开口,分布均匀,管径为60-90nm。

    Vertically aligned nanotubes arrays of titanium oxide are fabricated on the surface of titanium substrate by direct anode oxidation with HF being the supporting electrolyte . The top-opened TiO_2 nanotubes are well aligned and organized into high-density uniform arrays , with diameter from 60 to 90 nm .

  16. 铝制品的阳极氧化法的机理分析

    Mechanism of the Anodic Oxidation Method for Aluminium and Its Alloys

  17. 阳极氧化法形成绝缘氧化铝膜工艺研究

    Study on Insulating Aluminium Foil by Anodizing SPLIT-PHASE METHOD

  18. 炭纤维阳极氧化法表面改性

    Surface modification of carbon fibers by anodic oxidation

  19. 阳极氧化法是制备二氧化钛纳米管的一种主要方法。

    Anodic oxidization is one of the most important methods to fabricate titania nanotubes .

  20. 阳极氧化法提高土壤中锌参比电极电位稳定性

    Improvement of potential stability by anodizing treatment of zinc reference electrode buried in soil

  21. 并对两步阳极氧化法的机制进行了讨论。

    The mechanism of two-step anodization was discussed .

  22. 通过阳极氧化法,在钛合金表面制备了多孔形貌的涂层。

    Through the anodic oxidation , the porous coating on titanium materials has been achieved .

  23. 铝的阳极氧化法的进展

    Progress in anodizing Techniques for Aluminum

  24. 利用二次阳极氧化法在纯铝表面构建出具有纳-纳双重层级结构的阳极氧化膜。

    Anodic oxide membranes with nano-nano hierarchical structures are fabricated on the surface of pure alumina by two-step anodization .

  25. 本文提出了用阳极氧化法测定阀金属烧结多孔体的表面积。

    The present paper outlines that the surface area of sintered porous metal for valve can be measured by anodic oxidation .

  26. 结论:阳极氧化法可使钛义齿表面呈均匀的金黄色,能增进义齿支架的美学效果。

    Conclusion : The golden color on the surface anodized titanium denture frameworks is uniform , improving the aesthetic appearance of titanium dentures .

  27. 本文采用电化学阳极氧化法,分别通过恒压模式和恒流模式,在纯钛表面原位构建了纳米管和纳米棒阵列。

    In this dissertation , titania nanotube and nanorod arrays on titanium surfaces were prepared by electrochemistry anodic oxidation under constant voltage and constant current condition .

  28. 本文分别用一步阳极氧化法和二步阳极氧化法制备了阳极氧化铝模板,并把两种方法制备的模板进行了比较。

    In this paper , we prepared AAO template with two methods & one-step anodization and two-step anodization , and made a compare between two methods .

  29. 全文包括如下三个方面的具体研究工作:①二氧化钛纳米管的制备:通过对已有经典电化学阳极氧化法的利用,我们成功制备了二氧化钛纳米管阵列。

    Full-text includes the following three specific research : ① Titania nanotube : by classical electrochemical anodic oxidation method , we have successfully prepared titania nanotube arrays .

  30. 利用阳极氧化法在酸性溶液中制备了孔洞高度有序的多孔氧化铝模板。

    The main results and conclusions can be summarized as follows : AAO template with highly ordered pores was fabricated in acidic solution by using anodization method .