  • 网络tabular alumina
板状刚玉板状刚玉
  1. 电熔法板状刚玉的制备及其性能

    Preparation of tabular alumina by electrical fusion and its properties

  2. 在基质部分引入板状刚玉细粉,浇注料随板状刚玉粉引入量的增多,用水量减少、常温强度增加。

    When tabular alumina powders are introduced into the matrix to replace andalusite powder , castable shows lower water-demand and higher cold mechanical strength following the increase of tabular alumina powder dosage .

  3. 电熔法板状刚玉与ALCOA板状氧化铝的比较

    The Comparison of Fusion Tabular Corundum with ALCOA Tabular Alumina

  4. 从原理上判断和估计了电熔板状刚玉结晶体和阔气孔的形成条件。

    The forming condition of crystal and closed pore in tabular alundum produced with electric melting is estimated and determined theoretically .

  5. 阐明了用电熔法生产板状刚玉的构思和工艺要点、板状刚玉的组成与结构。

    The conception and technology of producing tabular alundum with electric melting and the composition and structure of tabular alundum are expounded in this article .

  6. 从原理上判断和估计了电熔板状刚玉结晶体和阔气孔的形成条件。电熔铸锆刚玉砖玻璃相中铁钛铝硼的物理状态研究

    The forming condition of crystal and closed pore in tabular alundum produced with electric melting is estimated and determined theoretically . STUDY ON THE PHYSICAL STATES OF IRON , TITANIUM , ALUMINUM AND BORON IN GLASS PHASE OF FUSED CAST AZS BLOCK

  7. 通过优化基质中煅烧氧化铝或活性氧化铝、铝酸钙水泥、外加剂、板状刚玉细粉(或其他细粉)的组成,可明显改善浇注料的性能;

    Fine and superfine matrix components such as calcined and reactive aluminas , calcium aluminate cements , dispersing additives and superfine tabular alumina can contribute significantly to the improvement of the performance of refractory castable in the aspect of low water demand , setting control and strength development .

  8. 板状氧化铝和电熔法板状刚玉的晶体形貌

    The crystalline feature of ALCOA tabular alumina and tabular corundum by fusion method