金红石型结构
- 网络Rutile type structure;Rutile structure
-
实验表明550℃以上制备的样品为多晶薄膜,并保持四方相金红石型结构;
The results show that the films grown above 550 ℃ were polycrystalline , and retain the rutile structure .
-
采用常压热分解CVD法制得的SnO2薄膜均为四方相金红石型结构的多晶薄膜。
All films prepared by this method are polycrystalline films with rutile structure .
-
对两种不同晶型的纳米TiO2进行紫外可见光谱的测试,结果表明在波长300~330nm的范围内,金红石型结构的纳米TiO2对紫外光有强的吸收。
Comparing with two kinds of different crystalline of nano-TiO_2 particles from the ultraviolet spectroscope , it was showed that the rutile nano-TiO_2 particles have stronger UV adsorption in the range of 300 ~ 330nm ( wavelength ) .
-
金红石型氧化物晶体结构与性能的分子动力学研究TiOCl2溶液低温水解合成金红石型氧化钛纳米粉
Molecular dynamics ( MD ) study of the physical and structural properties of oxide in rutile Preparation of Nanocrystal TiO_2 with Rutile Structure at Lower Temperature from TiOCl_2 Solution
-
在不同电解质溶液条件下,得到3种不同类型结构组成的氧化膜:单一TiO2的锐钛型结构、TiO2锐钛型+金红石型的混合相结构、单一TiO2金红石结构。
Three kinds of TiO2 coating , pure anatase type TiO2 , mixed phases of rutile type TiO2 and anatase type TiO2 , pure rutile type TiO2 were obtained .