轴承钢

在对影响轴承钢疲劳寿命的夹杂物分析的基础上，采用钡合金对轴承钢进行脱氧和夹杂物的变性处理。

Synopsis Based on the analysis of effect of various inclusions on fatigue life of bearing steel , this paper introduces the results of deoxidation and inclusions modification with adding barium alloy into the steel .

轴承钢中TiN夹杂物控制工艺及理论研究

Process and Mechanism of the Formation and Removal of TiN Inclusion Existed in Ball Bearing Steel

RH工艺生产轴承钢脱氧和去除夹杂物研究

Study on Deoxygenation and Inclusion Removal of Bearing Steel in RH Degasser

60吨VAD炉加Al线精炼轴承钢

Refining of bearing steel by feeding AI wire to the 60t VAD furnace

EAFCAB低碱度渣处理轴承钢脱氧效果的研究

Deoxidation effects of EAF-CAB basic slag treatment on ball-bearing steel

TiC薄膜对轴承钢表面滚动接触疲劳寿命和力学性能的影响

Effects of TiC films on the rolling contact fatigue life and mechanical properties of bearing steel

本文研究了轴承钢采用LF炉精炼时，各工艺因素对氧含量的影响。

This thesis studied the influence of ladle furnace refining process on oxygen content of bearing steel .

同时还提出了适合本厂精炼轴承钢的低碱度渣系组成，及LF炉埋弧泡沫渣组成。

For the refining of bearing steel , the use of the low basicity slag was suggested .

电炉白渣法冶炼的轴承钢中的点状夹杂主要是Al和Ca的氧化物，此外还有少量Mg的氧化物。

The essential globular inclusion in bearing steel smelted with white slag process in electric fur-nace are oxides of Al and Ca and small amount of Mg .

VD炉内轴承钢中碳还原渣中CaO的热力学及影响因素分析

Thermodynamics of Cao in slag reduced by carbon during VD process of bearing steel and its effect factors

用电渣熔铸的方法成功制备了WC颗粒增强轴承钢复合材料，并对其磨损性能进行了研究。

The wear resistance of WC particulate reinforced bearing steel composites prepared by electroslag smelting and casting was studied .

CBN刀具超精车削轴承钢时切削参数的选择

The Selection of Cutting Parameters in Extra & fine Turning for Shaft Bearing with CBN tool

CBN磨削和车削淬硬轴承钢的表面完整性

The Surface Integrity of Turned and Ground Hardened Bearing Steel with CBN Grits and CBN Tool

轴承钢TD渗金属及其最终热处理的工艺优化问题研究

Process Optimization Research between Metallic Cementation of TD Method and the Final Heat Treatment of Bearing Steel

Cr-Mo新轴承钢的热处理工艺与性能

Heat Treatment Technology and Properties of New Cr-Mo Bearing Steel

高碳铬轴承钢超长寿命S-N关系的概率特性

Probabilistic character for S-N relations of high carbon-chromium bearing steel in super-long cycle life region

电弧炉（EBT）-钢包炉（VD）-连铸生产轴承钢的工艺和质量

Production Process and Quality of Bearing Steel by Arc Furnace ( EBT ) - VD Ladle Furnace-Continuous Caster

热力学计算表明：轴承钢中TiN主要是在凝固过程中形成。如果要用钢中残余氧含量来氧化去除钢中残余钛，需要的初始氧含量为30×10-6。

It is shown from thermodynamics calculation that TiN can be formed during solidification and the initial oxygen content is 30 × 10-6 at least for the residual titanium removing from molten steel .

喷吹工艺对轴承钢GCr15断裂力学性能影响的研究

Study on the effect of SL technology on the fracture mechanical properties

GCr15轴承钢的接触疲劳寿命影响因素

Research on effect of bearing steel contact fatigue life

50tEAF-LF（VD）-CC流程冶炼轴承钢的氮含量控制

Control of Nitrogen Content in Bearing Steel Steelmaking by a 50t EAF-LF ( VD ) - CC Flowsheet

淬硬轴承钢GCr15磨削白层结构特性的实验研究

Experimental Study on Characterization of White Layer Formed in Grinding Process of Harden Bearing Steel

采用新改进的阴极弧金属等离子体源，对9Cr18轴承钢进行了金属等离子体浸没离子注入（PIII）处理。

The 9 Cr 18 bearing steel surface was modified with metal plasma immersion ion implantation ( PIII ) .

锭型对喷Ca-Si粉处理的轴承钢中点状夹杂分布的影响

Influence of ingot figure on distribution of globular inclusions in bearing steel treated by Ca-Si injection

上钢五厂与SKF公司生产轴承钢的冶金质量和接触疲劳寿命的试验研究

Metallurgical quality and contact fatigue life of bearing steels made by Shanghai No. 5 steel works and SKF company

轴承钢（GCr15）液态模锻磨球的工艺实验研究

Experimental Research on squeeze casting process of bearing steel ( GCr15 ) abrasive ball Inner Mongolia Polytechnic University

研究了不同锭型对喷CaSi粉处理的轴承钢中点状夹杂物分布的影响。

Influence of ingot form on the distribution of globular inclusions in bearing steel treated by CaSi injection has been studied .

本文介绍低氧轴承钢的精炼工艺及结果，其工艺过程是EAF→低真空或非真空下吹氩搅拌→模铸。

This paper reports the refining process of ultra-low-oxygen ball bearing steel . The process is EAF → argon stirring in a VAD ladle with low vacuum or without vacuum → ingot casting .

结果表明VD炉中，轴承钢中的碳能还原渣中的CaO生成[Ca]从而与钢中Al2O3结合生成点状的铝酸钙夹杂。

It was showed that the carbon dissolving in liquid steel might reduce CaO in slag to [ Ca ] which could also react with Al 2O 3 and turn into dot calcium aluminate inclusions in the steel .

采用20tEAF初炼、25tLF精炼、小方坯连铸工艺生产高碳铬轴承钢。

The small square blank continuous casting technology with steelmaking in 20 t EAF and refining in 25 t LF is adopted in the production of high carbon chromium bearing steel .