苯丙乳液
- 网络BA-St-MMA;styrene acrylate;styrene-acrylate emulsion
![苯丙乳液](../cache/1421386.jpg)
-
本文介绍了苯丙乳液的最新研究进展,并在此基础上提出了改进苯丙乳液性能的方法。
The latest studying progress on styrene-acrylate emulsion was introduced in this article , and methods for improving properties of styrene-acrylate emulsion was given on the basis of above-listed progress .
-
将分散后的纳米TiO2浆料加入到普通的水性苯丙乳液涂料中,加入各种助剂配制出了性能优异的水性纳米TiO2涂料,并对涂料的性能进行了测试。
Waterborne coating containing nano TiO2 with excellent performances is prepared by adding above-mentioned nano TiO2 suspension and various additives in the common waterborne styrene-acrylate emulsion coating . The performances thereof are tested then .
-
自交联型苯丙乳液替代PVA作为印刷纸张表面施胶剂
Self-Cross-Linking Styrene-Acrylic Emulsion Instead of PVA as Printing Paper Surface Sizing Agent
-
纳米TiO2改性苯丙乳液内墙涂料的研究
Study on styrene-acrylic latex interior wall coating modified by nano-TiO_2
-
用八甲基环四硅氧烷(D4)改性丙烯酸丁酯(BA)-苯乙烯(St)乳液,得到了稳定的改性苯丙乳液。
The stable modified butyl-acrylate styrene emulsion was prepared with octamethylcyclotetrasiloxane ( D_4 ) .
-
研究了以两亲聚合物P(C9-AA)作乳化剂,制备大颗粒及具有一定稳定性的苯丙乳液的方法;
P ( C 9-AA ) was synthesized and used as emulsifiers to prepare large particles and stable poly ( styrene / acrylate / methyl methacrylate / acrylic acid ) emulsion .
-
在无机SiO2纳米粒子存在下的苯丙乳液共聚合
Emulsion Polymerization of Styrene and Butyl Acrylate in the Presence of Inorganic SiO_2 Nanoparticles
-
功能型纳米TiO2Z/nO/苯丙乳液内墙涂料的制备
Preparation of Functionally Nano Scale TiO_2 / ZnO / Styrene-Acrylate Compound Coatings for Interior Wall
-
PVA、苯丙乳液、囊化Ca(OH)2对涂层耐水洗性关系的研究
Study on the Relation of PVA , Styrene-acrylate Emulsion and Micro-emulsified Ca ( OH ) _2 Gelatine Capsule to Coating 's Resistivity Against Water
-
将实验室自制的抗菌纳米TiO2添加于苯丙乳液中,制成抗菌涂料。
Antimicrobial coating was made by addition of nano titania which was made in the laboratory into a styrene acrylic emulsion .
-
TEM分析表明所制得的纳米苯丙乳液具有以纳米TiO2粒子为核、以聚合物为壳的核壳结构。
The TEM photographs indicate that the composite exhibit a core-shell structure with nano - TiO_2 as core and organic polymer as shell .
-
实验数据显示,PA、6-异丙基酞嗪在苯丙乳液粘合剂中的扩散系数均略大于其在同浓度PVA粘合剂中的扩散系数。
The experimental data showed that the diffusion coefficients of PA and 6-isopropyl phthalazine in styrene-butyl acrylate latex were greater than those of PA and 6-isopropyl phthalazine in PVA under the same binder concentration .
-
本文首先研究了利用硅烷偶联剂改性纳米TiO2的方法以及在改性纳米TiO2粒子存在下的五元单体苯丙乳液共聚合。
In this paper , method of surface modification about TiO_2 nanoparticles via silane coupling agent and emulsion co-polymerization of styrene-acrylate in the presence of inorganic TiO_2 nanoparticles was studied firstly .
-
采用苯乙烯(ST)、丙烯酸丁酯(BA)、丙烯酸(AA)和N-羟甲基丙烯酰胺(N-MA)合成出共聚苯丙乳液;
Styrene-acrylic-based copolymer emulsion was synthesized by emulsion copolymerization of styrene ( ST ), butyl acrylate ( BA ), acrylic acid ( AA ) and N-hydroxy ( N-MA ) methyl acrylamide .
-
SC-1苯丙乳液流变性的研究
Study of rheology on SC-1 styrene-acrylate emulsion
-
在苯丙乳液和聚丙烯酸酯乳液改性水泥复合材料中加入PVA纤维后增强效果不是太明显,PVA纤维具有成团倾向,在水泥基体中分散性不好。
Mechanical properties in the styrene-acrylic emulsion and polyacrylate latex modified cement composites were not improved obviously after adding PVA fiber , Maybe PVA fiber had the tendency to conglobation , it had poor dispersion in the cement composites .
-
通过硅烷偶联剂改性纳米SiO2与丙烯酸丁酯、苯乙烯、甲基丙烯酸3种单体共聚,合成纳米SiO2/苯丙乳液,以其作为主要成膜物制得了乳胶漆。
Nano-SiO 2 / styrene-acrylate emulsion was synthesized by means of silane coupling agent modified nano-SiO2 copolymerizing with butyl acrylate , styrene and methylacrylic acid . Latex paint was prepared by using above obtained emulsion as main film substance .
-
研究了不同掺量的丁苯乳液(SBR)、丙烯酸酯乳液(PAE)和苯丙乳液(SAE)对自流平砂浆不同龄期下的抗压、抗折强度的影响。
The compressive and flexural strength of styrene-butadiene rubber ( SBR ), polyacrylic ester ( PAE ) and polystyrene-acrylate latex ( SAE ) modified self-levelling mortars with different polymer binder ratio at different ages were compared .
-
功能粉体经过硅烷偶联剂KH-570表面改性后,再与St、BA、MAA单体聚合反应.苯丙乳液固体质量分数为40%,功能粉体添加质量分数为0.5%。
This powder copolymerized with St , BA and MAA after surface treating by silicon coupling reagent KH - 570 . The solid content of the emulsion was 40wt % , and the percentage of the powder was 0 . 5wt % .
-
本文考察了阳离子型水性聚氨酯Cpu-412,阴离子型Apu-506,非离子型Npu-1012与LB-苯丙乳液共混状况;
Blending conditions of cationic aqua polyurethane Cpu-412 , anionic Apu-506 , nonionic Npu-1012 with LB-styrene-acrylate emulsion were observed .
-
为了制备高性能的苯丙乳液,研究了乳化剂、助剂DZ-1及丙烯酸对苯丙乳液黏度及触变指数等性能的影响。
In order to manufacture high performance styrene-acrylic ester emulsion , the effects of emulsifier , auxiliary agent DZ-1 and acrylic on its viscosity and thixotropy were studied in this paper .
-
乳化剂用量为1.0%,DZ-1用量为4.5%,酸用量为3.0%时合成的苯丙乳液黏度和触变指数较高。
The viscosity and the thixotropy were higher when the content of emulsifier was 1.0 % , the content of DZ-1 was 4.5 % and the content of acrylic was 3.0 % .
-
本实验研制的表面施胶剂属于SAE类,在传统苯丙乳液合成方法基础上采用乳液聚合添加功能性单体进行改性,并进行表面施胶应用研究。
So , a new polymer-emulsion surface sizing agent ( belongs to styrene acrylic emulsions , SAE ) was synthesized in lab , and on the foundation of the traditional styrene-acrylic resin emulsion , adopting emulsion polymerization and adding functional monomer to modify the traditional emulsion .
-
在30℃和0.5Hz条件下最高能达到0.25,这主要是由于苯丙乳液的玻璃态温度是22℃;改性的硅粉和硅粉是最有效提高水泥砂浆储存模量的外加掺料,能提高大约50%-80%。
The research results show that all these admixtures may improve the loss tangent of cement mortar , styrene-acrylic is most effective and may be up to 0.25 , and due to the glass temperature of styrene-acrylic is 22 ℃;
-
苯丙乳液的最低成膜温度及其影响因素分析
Influence factors of minimum film forming temperature of styrene-acrylate polymer emulsion
-
新型苯丙乳液聚合的研究
Study on a New Type of Styrene - Acrylate Emulsion Polymerization
-
木器漆用核壳苯丙乳液的制备和性能研究
Preparation and Performance Research of Core-Shell Styrene-Acrylic Emulsion for Wood Coatings
-
苯丙乳液/硅溶胶复合体系的流变性研究
Rheological Properties of Styrene-acrylate Copolymer Latex / Silica Sol Composite System
-
硅溶胶/苯丙乳液杂化复合木材的制备与性能
Preparation and Performance of Silica Sol / Styrene-acrylic Emulsion Composite Wood
-
苯丙乳液对汽车工业滤纸性能的影响
Influence of Styrene-acrylic-based Copolymer Emulsion on Property of Auto-industry Filter Paper