环氧丙烯酸酯树脂

  • 网络epoxy acrylate resin
环氧丙烯酸酯树脂环氧丙烯酸酯树脂
  1. 环氧丙烯酸酯树脂(AE)质硬;

    Epoxy acrylate resin ( AE ) shows high hardness ;

  2. 含氟单体对环氧丙烯酸酯树脂性能的影响

    Effect of fluorine-containing monomer on properties of epoxy acrylate resin

  3. 新型紫外光固化TMA环氧丙烯酸酯树脂性能研究介绍了一种金属电镀件罩光用的热固性环氧改性丙烯酸清漆的配制。

    Study on the Preparation of a New Type of UV Curable TMA Epoxy Acrylic Resin ; A thermosetting epoxy modified acrylic clear top finish for metal electroplated parts is formulated .

  4. 研制了一种由环氧丙烯酸酯树脂、多元醇丙烯酸酯交联剂、光引发剂和填料等组成的紫外光固化腻子,在太阳光下只需10~15min即可固化。

    A UV Light curing putty , which is composed of epoxy / acrylic resin , acrylic polyol crosslinker , light initiator and fillers , has been developed . It can be cured only in 10 ~ 15 min under sunlight .

  5. 紫外光固化罩光漆用环氧丙烯酸酯树脂的合成及应用

    Synthesis and Application of Epoxy Acrylic Resin for UV-Curing Varnish

  6. 光固化环氧丙烯酸酯树脂有机-无机杂化体系

    UV Curable Hybrid Organic-Inorganic System Based on Epoxy Acrylate Resin

  7. 光固化型CTPE改性环氧丙烯酸酯树脂的研究

    Study on photocurable carboxy-terminated epoxy acrylate resin

  8. 结果表明:马来酸酐改性的环氧丙烯酸酯树脂涂料对金属有较好的附着力,显示了较好的流平性;

    The experimental results indicated : epoxy acrylate resin modified with maleic anhydrides had good adhesion to metals and good leveling property ;

  9. 采用正交实验设计,以N-乙烯基吡咯烷酮、丙烯酸丁酯为活性单体,环氧丙烯酸酯树脂为预聚物,纳米氮化硅粉体为无机填料制备出性能较好的紫外光固化纳米复合树脂。

    The title hybrid resin with good performance has been prepared by using orthogonal experiment design and based on N-vinyl pyrrolidone and butyl acrylate as reactive monomers , epoxy acrylic resin as prepolymer and nano silicon nitride powder as inorganic filler .

  10. 环氧(甲基)丙烯酸酯树脂的制备及应用研究

    A Study of Synthesis and Application of Epoxy ( Meth ) Acrylate Resin

  11. 采用丙烯酸类单体改性F51型酚醛环氧树脂的方法,合成具有光固化特性的酚醛环氧丙烯酸酯树脂,再用马来酸酐进行改性,在分子链上引入羧基,使树脂具有良好的碱溶性。

    By using acrylic acid to modify the F-51 novolac epoxy resin , novolac epoxy acrylate with photosensitive character can be synthesized , which is then induct the carboxyl groups in its molecular chain for good ability of alkali developable by using maleic anhydride .

  12. 根据亲水亲油平衡值(HLB)设计了以马来酸酐改性环氧丙烯酸酯的方案,合成了具有良好水分散性的羧基化环氧丙烯酸酯树脂。

    Based on the principle of HLB , a scheme of epoxy acrylate modified with maleic anhydride was designed , and carboxylated acrylate epoxy with good water dispersity was synthesized successfully .

  13. 本文以丙烯酸和F-44环氧树脂为原料,合成了一种既含有环氧基又含有丙烯酸基的光敏酚醛环氧丙烯酸酯树脂。

    The title photosensitive phenolic epoxy acrylate resin has been prepared based on acrylic acid and F-44 epoxy resin as basic materials , which contains epoxy as well as acrylic groups .