结果表明，树脂含量在30%时S-157酚醛树脂/CBFTC复合材料的力学性能和烧蚀性能最佳；

Results showed that S-157 / CBFTC composite of optimal mechanical properties and ablative properties was obtained when the resin content was 30 % ;

分析了缠绕速度、加工温度以及树脂含量等因素对NOL环层间剪切强度的影响，研究发现在一定的缠绕速度和加工温度范围内，可制得性能良好的NOL环缠绕构件。

The effects of winding speed , processing temperature and resin content on the interlaminar shear strength of NOL rings were investigated . The results showed that the winding components with high-performance characteristic were fabricated in the certain ranges of winding speed and processing temperature .

研究了EA树脂含量对溶胶-凝胶过程的影响；

The effect of EA resin on the sol-gel process was studied .

利用SEM分析了树脂含量对复合材料表面形貌的影响。

The effect of the amount of furan resin on the morphology of composites was studied with the help of SEM .

在弱酸阶段随着甲醛与尿素摩尔比和pH值的下降，通过亚甲基键连接的尿素和高分子质量树脂含量增加，而通过亚甲基醚键连接的尿素的含量下降；

During the weak acid stage , methylene linkages in the polymeric resin increased and dimethylene ether linkages decreased as formaldehyde / urea molar ratio and pH decreased .

接触压力的增大导致接触电阻迅速减小，而随着PF树脂含量的增加，接触电阻有着非常快的增加趋势。

The contact resistance decreased with the increase of contacting pressure and increased with increasing PF content evidently .

考察了接触压力、PF树脂含量及模压工艺条件对接触电阻的影响。

The influences of contacting pressure , PF content and compression molding parameters on the contact resistance were investigated .

研究表明，只有当TP树脂含量不低于15%时，方可获得较明显的增韧效果。

The study shows that only when the content of TP resin is not blow 15 % , can the relatively obvious toughening effect be found .

结果表明：在低用量条件下，随MBS树脂含量增加，MBS/PVC抗冲击性能有所提高，光学性能略有下降。

Generally , when the content of MBS resin is low , the impact resistance increases with increase in MBS content , with slight decrease in transparency .

研究了摩阻材料的最低树脂含量和最佳树脂含量，并与FB酚醛树脂基体摩阻材料进行对比。

The lowest and optimum contents of the resin were studied , and were compared with those of the friction material using FB phenolic resin as matrix resin .

论文分析讨论了引发剂用量、羟基丙烯酸树脂含量，HEA含量等对胶黏剂性能的影响。

Effect of content of initiator , content of hydroxy acrylic resin and content of HEA on properties of PUR were discussed .

实验发现当EA树脂含量高于85%时，随着反应的进行体系会逐渐变浑浊，而EA树脂的含量低于85%时，体系始终是均一透明的。

It was found that when EA content is higher than 85 % , the so-gel system becomes turbid while EA content is lower than 85 % , the system is transparent and homogeneous .

其中，聚四氟乙烯树脂含量较低的微带天线由于材料间空隙增多，导致介电损耗增大，其VSWR大于2，回波损耗较大。

The antennas which had low resin content will increase holes in composites and result in high dielectric loss . And the VSWR value is large than 2 and high return loss .

随着羟基丙烯酸树脂含量增加，胶黏剂的剪切强度先增加后下降，在含量10%时达到峰值17.54MPa。

With an increasing content of hydroxy acrylic resin in PUR , shear strength first rose , then declined , reaching at the maximal shear strength ( 17.54MPa ) at content of20 % .

氟碳漆中氟碳树脂含量的分析方法研究

Research of Analysis Method for Fluorocarbon Resin Content in Fluorocarbon Lacquer

纤维增强摩阻材料中树脂含量的确定

Determination of the Resin Content in Friction Material Reinforced by Fiber

落叶松木材树脂含量快速测定方法

The quick determination method of resin content in larch wood

包混粉体中酚醛树脂含量的影响因素研究

Research of Influence Factors on Phenolic Resin Content of Coat Mix Powders

GB/T3855-1983碳纤维增强塑料树脂含量试验方法

Test method for resin content of carbon fiber reinforced plastics

用β射线技术在线监测复合材料预浸带树脂含量

The Resin Content on-line Monitoring in Composite Prepreg Tapes Using Beta-ray Technique

防弹用纤维复合材料最佳树脂含量研究

Study on the optimal resin content of high strength bulletproof glass fiber reinforced plastics

热压罐法复合材料成形吸胶系统的计算及预浸料树脂含量的选择

Calculation of Bleeding System in Composite Autoclave Forming and Selection of Prepreg Resin Content

混杂纤维摩阻材料最低与最佳基体树脂含量的确定

Research on the Lowest and Optimum Contents of Matrix Resin of Promiscuous Fiber Frictional Material

本研究用脂肪酶对磨木浆进行处理，以降低浆料中树脂含量。

Treatment of ground pulp with lipase was investigated to reduce resin content of pulp .

树脂含量对稀土摩阻材料摩擦磨损性能的影响

Influences of Resin Contents on Performance of Friction and Wear of Rare Earth Friction Materials

炭/酚醛预浸布树脂含量的β-射线连续监测

Continuous monitoring of resin content in carbon / phenolic prepreg cloth by β - ray method

本文介绍计算聚酯玻璃钢树脂含量和固化度的校正公式，该公式对实际工作有一定的指导意义。

The correlation formula for calculating the resin content and curing degree of UP FRP were introduced .

讨论了制膜液中吸水树脂含量、粒度，以及添加剂与膜性能的关系。

The effect of ARW content , size and additives on the performance of membrane were discussed .

另外，本文还考察了不同γ树脂含量对炭质中间相形成及性能的影响。

The effect of different content of γ - resin on creation and performance of carbon mesophase .

基于能量原理，研究了不同环氧树脂含量沥青混合料在大幅降温环境下的开裂趋势。

Energy method was applied to forecast the cracking trend of asphalt mixtures with different content of epoxy resin .