晶体取向

  • 网络crystal orientation;crystallographic orientation;crystalline orientation
晶体取向晶体取向
  1. X射线二维衍射数据与晶体取向分布函数的关系研究

    Relationship between X-ray two-dimensional diffraction data and crystal orientation distribution function

  2. 用X-ray衍射仪分析了合金丝内晶粒的晶体取向;

    The crystal orientation of Cu-Al-Ni SMA wires is analyzed with X-ray Diffraction ( XRD ) .

  3. 利用X射线衍射分析方法,对湿压磁场成型的永磁铁氧体生坯晶体取向度进行了研究。

    Degree of preferred orientation of hard Sr ferrite compacts molded with magnetic field was studied by X ray diffraction analysis .

  4. 芳砜纶纤维上片状Mg(OH)2晶体取向膜的制备静电纺丝&从无规纳米纤维膜到取向连续长纱

    Assembly of Lamellar Magnesium Hydroxide Nano Crystal onto Modified Polysulfonamide Fabric Electrospinning : From Randomly Oriented Nanofiber Mats to Aligned Continuous Yarns

  5. 薄膜生长基底对FeS2晶体取向的影响

    Effect of substrate structures on crystal orientation of the FeS_2 thin films

  6. 水泥石&集料界面过渡层中CH晶体取向机理的探讨

    A Hypothesis about the Mechanism of Orientation of CH Crystal in Interface Layer between Cement Paste and Aggregate

  7. 用X射线衍射(XRD)分析晶体取向,偏振相位移技术分析薄膜残余应力。

    X-ray diffraction ( XRD ) and the polarization phase shift technique were employed to characterize the microstructure and residual stress of Cu-W films , respectively .

  8. 用扫描电镜(SEM)观察金刚石膜形貌、用X射线衍射表征晶体取向,用三点弯曲的方法来测量金刚石膜的断裂强度。

    The deposited films were characterized by scanning electron microscopy and X-ray diffraction . The fracture strength of diamond films was tested by three point bending method .

  9. 近年来国际上对SAW器件用石英晶体取向的研究极为活跃,出现了许多旨在改善SAW器件性能的新切型。

    Recently research on quartz crystal direction for SAW devices is stimulating all over the world . Many new cuts aiming at improving the performances of SAW devices have been discovered .

  10. LB膜模板诱导晶体取向生长

    Oriented Crystal Growth Induced by the LB Films Template

  11. X射线衍射分析表明在等径角轧制过程中,随着通道间隙的减小,晶体取向变化加大,(0002)基面取向减弱。

    By XRD patterns , it is found that the change of crystal orientation increases and ( 0002 ) basal plane orientation decreases with channel clearance decreasing during ECAR .

  12. Fe-C自生复合材料中石墨晶体取向的测定

    Orientation of Graphite Flake in In-Situ Composites of Fe-C Eutectic Alloy

  13. 采用原子力显微镜和X射线衍射仪研究了Al2O3基体上磁控溅射Au/NiCr/Ta多层金属膜基础上化学镀Au膜的生长形貌、晶体取向和残余应力,并与磁控溅射Au膜进行了对比。

    Au / NiCr / Ta multi-layered metal films were deposited on Al_2O_3 substrate by magnetron sputtering and then Au film was chemically plated .

  14. 作者利用X射线衍射所测极图及ODF来分析铸造铝基碳化硅质点增强复合材料中Al基体相及SiC增强相的晶体取向。

    The authors used pole figures and OUFs to analyze the crystallite orientations of SiC and the matrix of a cast SiC particulate reinforced Al-Si alloy composite .

  15. 同时还对蓝宝石衬底中产生的小角晶界进行了EBSD分析,研究了小角晶界两侧的晶体取向偏差。

    The small angle grain boundary of sapphire was also researched by the EBSD .

  16. 晶体取向和载荷模式对Ni3Al合金单晶体疲劳行为的影响

    Effects of crystal orientation and load mode on fatigue behavior in ni_3al alloy single crystals

  17. 研究表明:1.氧化亚铜不同晶面的氧离子浓度不同,通过控制电解溶液的pH值可以控制氧化亚铜薄膜的形貌和晶体取向。

    The density of oxygen on different crystallographic planes of cuprous oxide is different . By adjusting the solution pH , the orientation and surface morphology of the cuprous oxide films can be controlled .

  18. 用晶体取向分布函数(ODF)研究了Zr-4合金冷轧板的退火织构。

    The annealing texture of Zr-4 alloy cold rolling plate is studied with the crystal orientation distribution function ( ODF ) .

  19. 与合金内部的WC晶粒相比,韧性区内WC晶粒度更细,晶体取向发生改变;

    Compared with WC crystal grain inside the gradient cemented carbide , WC crystal grain in surface ductile zone is smaller and the grain orientation is changed .

  20. 应用TEM和晶体取向分布函数方法研究和分析了预变形和退火工艺对高纯铝箔立方织构的影响。

    The effect of pre deformation and annealing on cube texture of high parity aluminium foils has been investigated by means of TEM and method of orientation distribution functions ( ODFs ) .

  21. 用扫描电境(SEM)观察金刚石膜的形貌,用XRD表征晶体取向,用极图和取向分布函数法计算金刚石膜的不同织构,利用三点弯曲法测量金刚石膜的断裂强度。

    The different textures of CVD diamond films were analyzed using the methods of pole figure and orientation distribution function . The fracture strength of the diamond films was tested by three-point bending method .

  22. 晶种层和膜层的扫描电子显微镜和X射线衍射等表征结果表明,使用二次原位法同样可以实现分子筛膜层晶体取向和微观结构的调控。

    The characterization of the seed layer and final membrane by scanning electron microscopy ( SEM ) and X-ray diffraction ( XRD ) shows that the control and optimization of membrane orientation and microstructure can be achieved by using the in situ nucleation and secondary growth .

  23. 利用XRD层析法和SEM研究了集料与硅酸盐水泥石界面区的组成、CH晶体取向指数等。

    The composition and structure of the interfacial zone between aggregate ( white marble , limestone , granite ) and paste of portland cement as well as the orientation coefficient of portlandite ( I_ ( CH )) were preliminarily studied by XRD and SEM method .

  24. 本文中,还采用了电子背散射衍射(EBSD)测试方法,数据结果提供了更详细的晶体取向信息,阐述了非常有趣的结构特征,例如辐照区域内明显不同的晶粒尺寸和取向。

    Electron back-scattering diffraction ( EBSD ) results provide more detailed local crystal orientation information and illustrate interesting features of the structure of the lines , with regions of distinctly different grain sizes and orientations .

  25. 考察了镍基单晶合金DD3板试样在厚度为0.5.1.0,2.0mm、晶体取向为[001]、[011],[111]和[112]以及试验温度为1000、950.850和760℃下的变形和破坏规律。

    The deformation and fracture characteristics of nickel-base single crystal superalloys at high temperatures , which are in plates with different thickness and in different crystallographic orientations , have been studied .

  26. 当固液界面位于铸型内距出口端2~3mm时,可获得表面光洁、晶体取向度小于10°的连铸铜单晶。

    When the solid liquid interface is located in the mould and 2 ~ 3 mm distant from the mould exit , single crystal Cu rod with mirror smooth surface can be obtained , its deviation of crystal orientation is less than 10 ° .

  27. 不同晶体取向下纳米压痕的多尺度模拟

    Multi-scale simulation of the deformation in nano-indentation under different crystal orientations

  28. 晶体取向对铜单晶体循环硬化行为的影响

    Effect of orientation on cyclic hardening behavior of copper single crystals

  29. 连续铸造铜单晶的晶体取向与竞争生长

    Orientation and Competitive Growth of Single Crystal Copper by Continuous Casing

  30. 晶体取向显微成象的应用倾转晶体电子衍射图的自动标定

    The application of crystal orientation map in electron backscatter diffraction