试验发现，加成型室温硫化硅橡胶硫化过程产生气泡的主要原因是氢基硅油与H2O分子的反应。

Result showed that air bubble when the rubber curing came from the reaction of Si-H and H_2O .

结果表明，含乙烯基的MQ硅树脂对加成型室温硫化硅橡胶的增强作用明显，硅橡胶的透明性很好。

The silicone rubbers reinforced by MQ silicone resins had high transparency .

MQ硅树脂增强加成型室温硫化硅橡胶

Reinforcement of addition-curing type room temperature vulcanizing silicone rubber by MQ silicone resin

MQ硅树脂对加成型室温硫化硅橡胶性能的影响

Effects of MQ Silicone Resin on the Properties of Addition-cured Room Temperature Vulcanization Silicone Rubber

以自制MQ硅树脂改善加成型室温硫化硅橡胶的性能，结果表明，MQ硅树脂可以增大加成型室温硫化硅橡胶的交联度，延长其固化时间，有效地改善其力学性能；

Self-made MQ silicone resin was used to improve the properties of addition-cured ambient vulcanization silicone rubber . With the increasing of the MQ silicone resin , the crosslinkage of the silicone rubber was enhanced , setting time was prolonged and mechanical properties were improved .

空间级加成型室温硫化硅橡胶粘结剂的研究

Study on Space Grade Addition Cured RTV Silicone Rubber

综述了近年来加成型室温硫化硅橡胶在力学性能改进、铂催化剂改进以及在医学、电子电气、航空航天领域中的应用开发方面的研究进展。

The improvement of mechanical properties , platinum catalyst and application of addition-cured ambient vulcanization silicone rubber were reviewed , and the application developments of addition-cured ambient vulcanization silicone rubber in the field of medicine , electricity and electron , aerospace were introduced .

本文采用乙烯基硅油、氢基硅油、填料、铂催化剂、乙烯基硅树脂、抑制剂和端烯丙基聚醚表面润湿剂制备了加成型室温硫化硅橡胶；

In this paper , addition-cured room temperature vulcanization silicone rubber was prepared , which contained the following components : vinyl polysiloxane with vinyl groups both on terminals and in molecule , hydrogen polysiloxane , Pt-catalyst , Vinyl-containing silicone resin , filler , retarder and surfactant .