中间退火

本文研究中间退火处理对薄SiO2膜电击穿特性和高频电容-电压特性的影响。

In this paper the effects of intermediate annealing process on electrical breakdown properties and hight frequency capacitance - voltage characteristics of thin oxide films are studied .

用SEM的波谱（WD）分析手段，定性研究了合金元素铌在Zr-Sn-Nb-Fe合金中的存在方式及其与中间退火工艺的关系。

The existing form of alloying element Nb in two kinds of Zr-Sn-Nb-Fe alloys and its dependence on intermediate annealing were qualitatively investigated by means of WD in SEM .

确定了1145电缆箔生产中Fe、Si杂质含量和中间退火工艺对电缆箔力学性能的影响。

The influence of Fe , Si content and middle annealing process upon cable foil mechanical properties were studied .

中间退火对薄SiO2膜电击穿特性的影响

EFFECTS OF INTERMEDIATE ANNEALING PROCESS ON ELECTRICAL BREAKDOWN CHARACTERISTICS OF THIN OXIDES Electrical Breakdown Characteristics of Thin Films of SiO_2

3004铝合金铸轧法生产罐材中间退火的ODF分析

ODF Analysis of Middle Annealing of 3004 Aluminum Alloy Sheet for Can - Making Made by Melt-Rolling Process

中间退火及轧制工艺对Al-Mg-Li合金塑性开裂及晶粒细化的影响

Effects of intermediate annealing and rolling on plastic failure and grain refinement of Al-Mg-Li alloy

提高1050A铝合金空调管中间退火合格率的措施

Measures of Improving Qualification Rate of Intermediate Annealed Air-Conditioner Pipe of 1050 A Aluminum Alloy

合金经均匀化、热轧、中间退火、冷轧成2.2mm厚的板材。

Then , the homogenized alloy was hot rolled , annealed and cold rolled into a sheet with thickness of 2.2 mm .

线坯未经中间退火就非常顺利地从φ15mm一直拉伸到φ0.15mm，总延伸率达99.99%，氧含量约45ppm，漆包产品具有优异的性能。

The wire blank can be smoothly stretched from φ 15 mm to φ 0.15 mm without annealing . The total specific elongation reaches to 99.99 % , and oxygen content is about 45 ppm , The glazed product possesses excellent characteristics .

氮基气氛保护金属针布钢丝拉拔中间退火

Intermediate Annealing with Nitrogen Gas Protection for MCC Wire 's Drawing

中间退火工艺对5182铝合金带材性能的影响

Effects of annealing process on properties of 5182 aluminum alloy strips

无氧铜细丝拉丝中间退火工艺与组织性能

Microstructure and Properties of Copper-free Wire Subjected to Intermediate Annealing

中间退火对3003铝合金板组织和晶粒度的影响

Effect of medium annealing on microstructure and grain of 3003 aluminum alloy

结果表明中间退火可以延长疲劳寿命。

The experiments showed that the intermediate annealing can prolong the fatigue life .

3004铝合金中间退火的织构变化与显微结构研究

A Study on Texture and Microstructure during Intermediate Annealing in Aluminium 3004 Alloy

中间退火使疲劳损伤钢延寿的微观力学解释

Micro-mechanics explanation of prolonging remains life by intermediate annealing for fatigue damage steel

合金的最佳中间退火温度随碳含量的增加而升高。

The optimal middle annealing temperature increases with the increase of the carbon content .

而最佳中间退火温度受合金成分的影响。

The optimum middle annealing temperature depends on the chemical composition of the alloys .

3104制罐板中间退火冷却方式改变对性能的影响

The Effect of Changing Cooling Model of Intermediate Annealing on Properties of 3104 Can Stock

在相变点附近±100℃以内进行中间退火。

± 100 ℃ within was carried on the intermediate annealing nearby the phase tranformation point .

不要把回火与中间退火或去应力退火混淆。

The term " tempering " should not be confused with either process annealing or stress relieving .

讨论了中间退火对轧制时立方取向稳定性的作用。

The effect of intermediate annealing is discussed in terms of the stability of cube orientation during rolling .

用此微观力学模型和公式也可以解释中间退火延寿机理。

The micro mechanics of prolonging remains life can be explained by the micro fracture mechanics models and formulas .

中间退火前后冷轧变形量对3003铝合金阴极箔比电容的影响

Effects of cold deformation before and after intermediate annealing on specific capacitance of cathode foils of 3003 aluminum alloy

本文介绍了氮基气氛保护金属针布钢丝拉拔中间退火的设备、仪器、工艺及试验结果。

This treatise introduces equipment , instruments , technology and experimental results of intermediate annealing with nitrogen gas protection .

研究了用合格的铸轧坯料生产覆塑用铝箔的过程中，中间退火工艺对覆塑用箔材表面质量、力学性能的影响；

The influences of foil rolling and middle annealing process on surface quality and mechanical properties of aluminium foil were studied .

通过工序间切边代替中间退火和酸洗工序，可提高拉伸件的成形质量。

By substituting the trimming between working procedures for intermediate annealing and pickling procedure , the quality of drawins can be improved .

这样可以有效地减少中间退火次数，甚至可以避免中间退火，强化生产过程，大大提高生产率。

Doing this we can effectively reduce the number of intermediate annealing or even avoid the process , strengthen the production process , greatly increase productivity .

重点研究了铝的纯度、均匀化制度、热轧温度、冷轧及中间退火对最终退火后箔材形成立方织构的影响。

The emphasis is put on effect of purity homogenization , hot rolling temperature , cold rolling and medium annealing on cubic texture of finally annealed foil .

采用增加冷轧道次、提高中间退火温度等手段改进了传统高压阳极铝箔的生产工艺，以制备超薄型高压阳极铝箔。

The conventional production technology for aluminum foil was modified by means of increasing cold rolling passes and rising intermediate annealing temperature to prepare ultra-thin high voltage anode aluminum foil .