胶衣树脂

随搅拌时间的延长，抗菌胶衣树脂的抗菌率也有所增加，搅拌时间为1h时抗菌率为94%。

With the more mixing time , the antibacterial rate increased , and the antibacterial rate was 94 % for one hour mixing .

以双酚A型不饱和聚酯、胶衣树脂为基体树脂，玻璃纤维表面毡、玻璃布、短玻璃纤维毡为增强材料，制备了玻璃纤维增强塑料（GFRP）填料塔。

The glass fiber reinforced plastics have been prepared with bisphenol A unsaturated polyester and gel coating resin as the matrix resins , glass fiber mat and glass cloth as the reinforcing materials .

本文介绍了TM-36手湖喷涂两用型胶衣树脂的研制及性能。

The preparation and characteristics of the TM-36 # gel coat resin for spray up and hand lay-up are introduced in this paper .

本文以硅溶胶为载体，通过负载金属银离子、TiO2、ZnO以及Al2（SiO3）3于硅溶胶中，制备了复合无机抗菌剂，并将其加入到胶衣树脂中制备了抗菌胶衣树脂。

The inorganic antibacterial compound was prepared using silicon sol as carrier with Ag ~ + , TiO_2 , ZnO and Al_2 ( SiO_3 ) _3 in this paper . The antibacterial agent was added to make the antibacterial gel coat resin .

本文对耐水型胶衣树脂的合成工艺和性能作了介绍。

This paper introduces synthesis technology of water resistant gel coat resin .

胶衣树脂的结构与特性

Structure and characteristics of unsaturated polyester resins for gel coat

耐候性阻燃胶衣树脂的研究

Research of a Weatherproof Flame Retardant Gel Coat Resin

紫外光固化胶衣树脂

Curing of Gel - Coating Resin by UV Light

喷涂用胶衣树脂的特性研究

Study on characteristics of coating resin for spray-up

气相二氧化硅在胶衣树脂中的应用研究

Application Study of fumed silica in gel coating

胶衣树脂合成研究

Study on gel coat resin

内外表面采用耐老化、耐腐蚀、不褪色、抗紫外线性能优良的胶衣树脂喷涂。

Spray gel coat resin that is of weather resistance , corrosion prevention , fadeless , uvioresistance and of good performance .

以此树脂为基体，研制开发了耐候性阻燃胶衣树脂，并列出了此胶衣树脂的耐候性数据。

On the basis of this resin as a matrix , a weatherproof flame retardant gel coat resin was developed and datum of weatherproof ability was given .

实际试用结果表明，该树脂不仅适用于喷涂、手糊成型工艺要求，而且是良好的模具胶衣树脂。

The resin is not only suitable for spray up and hand lay-up processes , but also a good kind of gel coat resin for mould making .

本文介绍了邻苯二甲酸型、间苯二甲酸型和双酚A型不饱和聚脂树脂（以下简称聚酯树脂）以及乙烯基酯树脂型胶衣树脂的结构与特性。

In this paper are introduced the structure and characteristics of o-phthalic anhydride type , m-phthalic anhydride type and bisphenol A type unsaturated polyester resins and vinyl ester resins for gel coat .

主要研究了抗菌剂的制备参数、含量及种类和抗菌胶衣树脂的制备参数对胶衣树脂抗菌性能的影响。

The effect of the preparation parameters , content and type of antibacterial agents and preparation parameters of the gel coat resin on the antibacterial performance of antibacterial gel coat resin was studied .

以不饱和聚酯树脂为基体，无碱玻璃布和短切玻璃毡为增强剂，过氧化甲乙酮为固化剂，环烷酸钴为促进剂，并使用模具用胶衣树脂，研制了不饱和聚酯复合材料模具。

The mould of fiber reinforced composites was developed with unsaturated resin as matrix , E-glass cloth and chopped strand glass mat as reinforcing agent , mthyl ethyl ketone peroxide as hardener , cobalt naphthenate as promotor .

RTM模腔内温度变化与形变的测试结果表明：模腔内树脂的放热峰可以通过改变固化剂的含量适当调节，模腔表面胶衣及表面层树脂应能承受120℃的热疲劳冲击；

The measuring of temperature change and distortion in RTM moulds shows that the exothermic peak of resin in the cavity can be adjusted through catalyst contents . The cracking and softening of surface resins result in the mould failure .

若胶衣收缩比加强树脂收缩量大，将导致部件的胶衣面上将有更多凹面。

Gel coat shrinks more than fiber reinforced resin , resulting in parts that are more concave on the gel coat side .