红磷

Mg（OH）2与包覆红磷协效阻燃PP/PA6复合材料的研究

Synergetic Fire Retardant Effect of Magnesium Hydroxide and Encapsulated Red Phosphorus for PP / PA6 Composite

Mg（OH）2包覆红磷复配对阻燃聚丙烯力学性能的影响

Influence of Mg ( OH ) _2 Coated Red Phosphorus Flame-Retardant Compound on Mechanical Properties of Polypropylene

β成核剂对红磷阻燃PP材料的影响

Effect of β Nucleate Agent on the Flame Retardant PP with Red Phosphorus

采用包覆红磷作为无卤阻燃剂对聚丙烯（PP）进行了阻燃改性。

Red phosphorus as non-halogen flame-retardant additives for polypropylene ( PP ) were studied .

红磷增效Al（OH）3/Mg（OH）2阻燃的聚丙烯结晶形态

Crystalline Morphology of Flame-Retarding Polypropylene Filled With A1 ( OH ) _3 and Mg ( OH ) _2 Synergized by Red Phosphorus

最后利用锥形量热仪验证了Mg（OH）2/红磷复配体系的协同阻燃效应。

Lastly , the synergistic flame-retarded effect of Mg ( OH ) _2 and red phosphorus was confirmed through the cone calorimeter .

红磷阻燃PP/PA6/纳米SiO2复合材料性能的研究

Study on the Properties of Flame-retardant PP / PA6 / Nano-SiO_2 Composites by Red Phosphorus

介绍了红磷公司HRS循环酸泵的结构和运行情况。

The structure and operation of Honglin 's HRS acid cycling pump are described .

微胶囊红磷在TPU阻燃系统中的应用

Application of Microencapsulated Red Phosphorus in TPU Flame Retarded System

包覆红磷在UPR包覆层耐烧蚀改性中的应用

Application of Coated Red Phosphorus in the Anti-ablative Modification of UPR Inhibitor

结果表明：Mg（OH）2与红磷并用具有良好的协同效应，是LLDPE/LDPE的高效阻燃体系。

The results showed that cooperated red phosphorus and Mg ( OH ) 2 had good synergism effect , and was a high effective flame retardant system for LLDPE / LDPE system .

实验证明，包覆红磷和MCA之间存在协同效应。

Experiments showed that there is a synergic effect between the covering red phosphorus ( CRP ) and MCA .

描述了采用密胺树脂和硼酸锌连续双层包覆微胶囊化红磷（MRP）的最新制备方法。

Microcapsulated red phosphorus ( MRP ) coated with melamine-formaldehyde resin and zinc borate was prepared and characterized by FTIR , XPS and TEM .

结果表明：微胶囊红磷/Mg（OH）2组成的复合阻燃剂质量分数20.0%时，复合材料ABS阻燃效果达到V-0级。

The results show that the flame-retardant effect of ABS composites with 20 . 0 % microcapsule red-phosphorus / Mg ( OH ) 2 reaches V-0 .

结果表明，当微胶囊红磷用量为8phr时，随着环氧树脂用量的增加，HIPS的阻燃性能提高；

The results reveal that the flame-retardant properties of the HIPS enhance with the increase of epoxy content when dosage of micro-capsulated red phosphorus is 8 phr .

以聚丙烯（PP）为基料，通过与纤维级Mg（OH）2、红磷（P）以及其他助剂改性制备阻燃材料。

A flame-retardant material of PP / fibre Mg ( OH ) 2 / P was prepared based on polypropylene ( PP ), fibre Mg ( OH ) 2 , red phosphorus ( P ) and other aid agents .

DSC分析和热老化实验表明，红磷对三元乙丙橡胶材料的热老化稳定性有不良影响，可通过调整配方加以解决

The results of DSC and thermal aging tests indicate that the addition of red phosphorus decreases the thermal aging stability of EPDM . This problem can be resolved by adjusting the components

制备新型的单分子磷-氮类膨胀型阻燃剂（TPA），采用微胶囊化红磷（MRP）与TPA复配阻燃剂，制备具有良好阻燃性能的无卤阻燃ABS。

Novel intumescent flame retardant ( TPA ) was prepared , and halogen-free retardant ABS composites were prepared by microencapsulated red phosphorus ( MRP ) and TPA as flame retardants .

根据Mie散射理论计算了多种直径红磷烟幕粒子对不同波长红外的吸收效率因子、散射效率因子和消光效率因子。

The absorption , mattering and extinction efficiency factors of red phosphorus smoke with different diameters to infrared at different wavelengths were calculated according to Mie scattering theory .

考察了红磷与常用阻燃剂的协同效果，确定了无卤阻燃剂TE3的组成，将其用于PE电缆料，达到了预期的阻燃效果阻燃剂可分为含卤阻燃剂、无卤阻燃剂。

Synergistic effect between red phosphorus and common flame retardant is observed , and the compositions of non halogenated flame retardant TE 3 are determined . Polyethylene cable material with TE 3 as flame retardant is endowed with desired flame retardancy .

在没有经过辐照过的样品中添加红磷，即使掺杂量达到12.5%，都不能很好的提高PA-6的阻燃性。

Red phosphorus contained in non-irradiated polyamide-6 at concentrations up to 12.5 does not significantly improve the fire resistance of the polymer .

本研究以低密度聚乙烯（LDPE）为基础树脂，用多种三元乙丙橡胶（EPDM）作改性剂，研究不同EPDM、无机阻燃剂和红磷对材料性能的影响。

Using LDPE as the base resin , the effects of different EPDM ternary copolymers , as a modifier , and inorganic flame retardants and red phosphor on the properties of this composite were studied .

Lundstrom安全火柴很安全是因为红磷是无毒的；

Lundstrom 's safety matches were safe because the red phosphorus was non-toxic ;

氧指数可达到30以上，垂直燃烧等级为FV-0，添加红磷后材料的氧指数可达到35。

The oxygen index value can be above 30 and its grade of upright combustion was FV-0 .

为改善不饱和聚酯树脂（UPR）包覆层的耐烧蚀性能，在包覆层配方中引入有效阻燃剂包覆红磷。

In order to improve the anti-ablation performance of unsaturated polyester ( UPR ) inhibitor , an effective flame retardant-coated red phosphorus was added into the UPR inhibitor material .

采用白度化红磷对30%玻纤增强PBT进行阻燃改性，研究了白度化红磷对PBT复合材料阻燃性能的影响。

Glass fiber ( 30 % ) reinforced PBT composite was flame retardation modified by whitening red phosphorus , and the effect of the whitening red phosphorus on the flame-retardance of the PBT composite was investigated .

本文简要叙述了红磷形成烟雾的过程及性质，并用Mie理论计算了不同温度条件下红磷烟雾对10.6μm激光的质量消化系数αc和质量散射系数α。

This paper briefly describes the process and nature of the red phosphorus derived smoke , and calculates mass-extinction coefficient α . and mass-scat - tering coefficient α, of the smoke at the different α . relative humidity for 10.6 μ m CO_2 laser from Mie 's theory .

的ZnO就能使微胶囊红磷／环氧树脂质量比为8：15的阻燃HIPS体系垂直燃烧达到UL94V-O级，LOI也可达到29.2%。

Adding 2 phr zinc oxide into the composite , in which the ratio of micro-capsulated red phosphorus to epoxy resin equals to 8 / 15 , can make the flame-retardant HIPS attain vertical combustion level of UL 94 V-0 and LOI of 29.2 % .

结果表明，ATH粉体改性效果越好，阻燃性能越好，ATH与红磷、硼酸锌和硅油等有较好的阻燃协同效应。

The results show that the better modification effects are beneficial for improving the flame resistance performance of ATH powder . ATH has good flame-resistant synergism with red phosphorus , zinc borate , silicone oil .

膨胀型阻燃剂新戊二醇乙撑磷酰胺的合成微胶囊红磷膨胀型阻燃剂的制备及应用

Preparation and Application of Intumescent Flame Retardant of Microencapsulated Red Phosphorus