结果表明，PS降解程度越大，接枝率和接枝效率越好，产品的外观、粘度和剪切强度等性能也越好。

The result indicated that , PS degeneration degree bigger , stem grafting rate and stem grafting efficiency better , performance and so on outward appearance , viscosity and shearing strength is better , namely also confirms the original intention which we tests .

结果表明，BPO用量为wt.1.0%，单体用量为wt.8.0%，反应温度为80～90℃，反应时间为3小时左右时，接枝效果最好。

The result indicated that , when the BPO amount used is wt. 1.0 % , the monomer amount used is wt.8.0 % , the reaction temperature is 80 ~ 90 ° C , the reaction time is about 3 hours , the stem grafting effect is best .

利用水溶性的染料（结晶紫和罗丹明B）对接枝后的聚丙烯板进行了染色，并测定了吸收光谱和荧光光谱。

Certain water-soluble dyes ( crystal violet and rhodamine B ) showed a strong affinity for the grafted surface .

高分子量PP接枝产物接枝率的测定

High Molecular Weight PP Graft Products Graft Rate Measurement

X射线衍射测试表明，接枝膜结晶度随接枝率的升高而降低。

X-ray test found that the grafted membranes show a decrease in crystallinity depending on the grafting yield .

利用远程Ar等离子体引发聚四氟乙烯膜接枝丙烯酸的研究

Graft of Acrylic Acid onto Polytetrafluoroethylene by Ar Remote-Plasma

马来酸酐接枝POE改性SAN树脂的制备与性能研究

Study on Preparation and Property of SAN Resin Modified by POE-g-MAH

甲基丙烯酸甲酯与SBS接枝聚合动力学的研究

Study on Kinetics of Graft Copolymerization of SBS and Methyl Methacrylate

替代PVA的接枝变性淀粉浆料的研究

Research on the Starch Graft Copolymer as Warp Size to Replace PVA

国产CR与MMA接枝聚合研究

Research on Graft copolymerization of domestic CR with MMA

马来酸酐接枝ABS及其应用

Maleic Anhydride Grafted ABS and Its Application

HDPE预辐射接枝NIPA/AAc的性能研究

Characteristic study of pre-irradiated HDPE grafted with NIPA / AAc

探讨以正庚烷/甲苯混合物为溶剂，采用共聚法制备EPDM接枝聚苯乙烯丙烯腈（EPDMgSAN）的反应条件。

The copolymerization of EPDM-g-SAN using n - heptane / toluene as solvent was investigated .

温度和pH敏感性壳聚糖接枝物对辅酶A的控制释放

Temperature and pH Sensitivity of Acrylic Acid and Poly ( N-isopropylamide ) Graft Chitosan Polymer and Its Controlled Delivery on Coenzyme A

淀粉在CH3OH-H2O溶液中与MA进行接枝共聚的研究

Study on the Graft Copolymerization of Starch and Methyl Acrylate in the CH_3OH-H_2O Solution

KPS-Na2S2O3引发丙烯酸丁酯与玉米淀粉接枝共聚合反应的研究

Study on KPS-Na_2S_2O_3 Initiated Graft Copolymerization of Butyl Acrylate onto Corn Starch

高胶ABS粉料的研制ⅠABS乳液接枝聚合的研究

Study on ABS powder of high rubber content ⅰ Study on ABS of emulsion graft polymerization

丙烯酸接枝改性PS沥青防水涂料

Acrylic graft-modified PS asphalt water-proof coatings

用毛细管流变仪和DSC方法研究了马来酸酐接枝改性的聚丙烯（PPgMA）对PP/PPgMA共混体系流变性和热行为的影响。

The effect of PP-g-MA on rheological behaviour and thermal properties has been studied with capillary rheometer and DSC method .

马来酸酐紫外辐照接枝POE的研究

Study of Maleic Anhydride Grafted on POE Induced by UV Irradiation

通过改变碱处理的时间，可以得到不同接枝率的复合膜。通过红外光谱（FTIR）、光电子能谱（XPS）、扫描电镜（SEM）等分析手段证实了膜表面接枝共聚物的存在。

Grafted copolymers on the surface of composite membrane were verified by FTIR , XPS and SEM .

LDPE片材的共辐射接枝改性及其表面粘接性

Mutual irradiation grafting of LDPE plate and its surface adhesivity

表面接枝高分子季铵盐的纳米SiO2应用于抗菌塑料的制备

Preparation of Antimicrobial Plastics Containing Nano-meter SiO_2 Grafted High-molecular Quaternary Ammonium Salt

POE与马来酸酐的反应挤出接枝

Grafting of maleic anhydride on POE by reactive extrusion

分子筛表面接枝TDI的研究

Study of Graft TDI on the Surface of Molecular Sieve

DSC研究表明辐照接枝产物的熔融温度和结晶温度均降低。

The DSC results showed both the melting temperature and crystallization temperature of the grafting products were decreased .

用马来酸酐（MAH）对聚丙烯（PP）进行接枝改性，制得改性PP膜。

It modified the PP through grafting MAH onto PP , and then prepared the modified PP film .

双亲性无规-类接枝共聚物PAF的合成及表征

Synthesis and Characterization of an Amphiphilic Random Copolymer of PAF

接枝SAN分子量对ABS树脂性能和形态结构的影响

The Effect of the Molecular Weight of SAN Copolymer Grafted onto PB Rubber Particles on Morphology and Property of ABS Resins

随接枝率的增大，接枝HDPE与水的接触角下降，亲水性增加。

As the grafting degree increase , the contact angle to water of AA-grafted HDPE powder decreases .