尼龙薄膜

  • 网络NYLON;nylon film;BoPa;BOPA Film
尼龙薄膜尼龙薄膜
  1. 双向拉伸尼龙薄膜

    Bi-directional Extented Nylon - film

  2. 本文用DSC研究了等温熔体结晶尼龙1010薄膜试样的熔融。

    The melting process of the isothermal crystallizing film samples of Nylon 1010 from the melt have been studied by DSC .

  3. 流涎尼龙&6薄膜的试制

    Trial-produce of casting nylon - 6 film

  4. 退火与极化温度对尼龙11薄膜驻极体内陷阱能级分布的影响

    Effect of annealing and polarizing temperature on the trap level distribution in nylon 11 film electrets

  5. 为进一步认识分子链运动与晶型之间的关系,用熔融、冰水淬火和退火等方法制备了α和δ′两种晶型的尼龙11薄膜试样。

    Two crystal forms (α and δ′ form ) of nylon 11 were prepared by melting , ice-water bath quenching and annealing .

  6. 这些参数进一步表明,淬火尼龙11薄膜驻极体内存在四个空间电荷的陷阱能级,极化温度升高对它们的分布情况影响不大;

    The results further proved that there were four trap levels of space charge in a quenched electret and the trap level distribution changed little when the polarization temperature increased ;

  7. 用Coγ射线对尼龙6复合薄膜(五层共挤出复合薄膜,尼龙6/粘接聚乙烯/聚乙烯/粘接聚乙烯/尼龙6)60进行辐射改性。研究了辐照剂量对材料性能的影响。

    Nylon composite films , with five layers of nylon-6 , adhesive PE , PE , adhesive PE and nylon-6 , were crosslinked by Co γ - ray irradiation to 10 & 50kGy . Effects of irradiation dose on properties of the nylon-6 composite 60 films were studied .

  8. γ&射线辐射对尼龙6复合薄膜性能的影响

    Studies on γ ray radiation effect of the nylon 6 composite film

  9. 结果表明:在10&50kGy的辐射剂量范围内,尼龙6复合薄膜仍然保持其原有地良好的阻隔性能;同时,材料的力学性能得到大大的提高;

    The results showed that the nylon ― 6 composite film could keep its original separation properties in irradiation dose of 10 & 50 kGy , the mechanical properties of the nylon ― 6 composite film was successfully improved , the contration ratio was distinctly reduced at the same time .

  10. 利用60Coγ射线对尼龙6/粘接聚乙烯/聚乙烯/粘接聚乙烯/尼龙6五层共挤出复合薄膜(尼龙6复合薄膜)进行辐射交联改性。

    The nylon ― 6 / adhesive PE / PE / adhesive PE / nylon ― 6 composite film ( nylon ― 6 composite film ) was irradiated by Co γ― ray in order to get crosslinking modification .