氢脆

qīng cuì
  • hydrogen embrittlement;hydrogen brittleness
氢脆氢脆
氢脆[qīng cuì]
  1. Ni-Fe奥氏体合金的氢脆及成分影响

    Hydrogen embrittlement in Ni-Fe FCC alloys and effect of composition

  2. Fe-Ni基合金氢脆的正电子湮没寿命谱研究

    Study of hydrogen embrittlement of Fe-Ni base alloy by positron annihilation lifetime spectroscopy

  3. H、O联合作用下的V合金表现出了很强的氢脆敏感性。

    The alloys showed much stronger sensitivity to hydrogen embrittlement when hydrogen acts synergistically with oxygen .

  4. 高强度螺栓在H2S环境下氢脆敏感性分析

    Analysis of Hydrogen Embrittlement Sensitivity of High-strength Bolt Under H_2S Environment

  5. 有序化对(Fe,Ni)3V合金环境氢脆的影响

    Effect of Ordering on Environmental Embrittlement of ( Fe , Ni ) _3V

  6. 高强钢电镀低氢脆Zn-Ni合金工艺的研究

    Study of Low Hydrogen Embrittlement Zn-Ni Alloy Electroplating on High Strength Steel

  7. Ni2Cr合金室温环境氢脆的研究

    Study on the environmental embrittlement of ni_2cr alloy at room temperature

  8. 硼对有序态Ni3Fe合金氢气环境中氢脆敏感性的影响

    Effect of boron on the environmental embrittlement of ordered Ni_3Fe alloys in gaseous hydrogen

  9. C-Mn钢焊接热影响区氢脆敏感性的研究

    A Study on Hydrogen Embrittlement of C-Mn Steel Welded HAZ Metals

  10. Fe3Al系合金环境氢脆研究

    Environmental embrittlement in fe_3 Al based alloys

  11. 有序态和无序态Ni3Mn的环境氢脆

    Environmental Embrittlement of Ordered and Disordered Ni_3Mn

  12. 结果表明:不同有序度的(Fe,Ni)3V均不存在空气中水气诱发的环境氢脆;

    The results show that there is no moisture-induced environmental embrittlement for the disordered and ordered ( Fe , Ni ) _3V when tested in air .

  13. Ti-Mo合金薄膜的储氢特性和抗氢脆能力

    Hydrogen storage and hydrogen em - brittlement of Ti-Mo Alloy Films

  14. 为改善钒合金的抗氢脆性能,应选用原子尺寸与V接近的合金元素,如W和Re等。

    Thus it is recommended that the alloying elements in the alloy should have close atom size in comparison with V to improve its properties against hydrogen embrittlement , such as W and Re .

  15. Al-Li-Cu-Mg-Zr合金的氢脆敏感性

    Hydrogen Embrittlement Susceptibility of a Al-Li-Cu-Mg-Zr Alloy

  16. ADI水脆化是由于水分解的氢使ADI基体组织中的应力诱变产生马氏体引起氢脆而导致的。

    ADI water embrittlement was attributed to the decomposed hydrogen originated from water , resulting in hydrogen embrittlement of stress induced martensite in ADI matrix .

  17. 稀土元素对氢、氧、硫等具有很强的亲合力,La和Ce加入到合金后,进一步降低了合金中氢元素的含量,减弱了氢脆的作用;

    The earth elements have stronger affinity to hydrogen , oxygen and sulfur than other elements . The hydrogen content in alloys has reduced further so as to lower the effect of hydrogen embrittlement ;

  18. 低氢脆(LHE)刷镀镉工艺

    Low Hydrogen Embrittlement Brush Cd Plating

  19. 800H和690合金的氢渗透及氢脆研究前瞻

    Prospects of Research on Hydrogen Permeation and Hydrogen Embrittlement in 800H and 690 Alloys

  20. 用光滑和缺口拉伸试件,对C-Mn钢的焊态和焊接热影响区的热模拟态进行氢脆敏感性指数的研究,并进行了金相与断口的SEM,TEM,AES的微区分析。

    Hydrogen embrittlement index ( 1 % ) of welds and heat affected zone ( HAZ ) of C-Mn steel welded joints are studied by means of smooth and notched tensile specimen .

  21. 结果表明,TiAl的氢脆是由于固溶氢减弱了含氢TiAl晶胞主干键并降低了解理能引起的。

    The analysis shows that hydrogen embrittlement in TiAl results from solute hydrogen weakening main bonds in TiAl crystal cell containing hydrogen , which causes the decrease of cleave enegy .

  22. 不同热处理状态40Cr钢的氢脆敏感性判据

    A Criterion of Hydrogen Embrittlement Sensitivity of 40 Cr Steel in the Different Heat Treatment States

  23. 充氢后的堆焊层经630℃×4h去氢处理可消除氢脆现象,使塑韧性恢复。

    After dehydrogenation at 630 ℃ for 4 hours , the ductility and toughness of the overlay which was initially charged with hydrogen is recovered and hydrogen embrittlement is eliminated .

  24. 翻修要求的低氢脆(LHE)镀镉应当在部件不在翼的状态下进行。

    Rework that requires low-hydrogen embrittlement ( LHE ) cadmium stylus plating should be performed when the component is not loaded .

  25. GH907合金疲劳蠕变和氢脆的显微分析

    Microstructure Study on the Fatigue Creep and Hydrogen Embrittlement

  26. 介绍了一种新的EAM理论,它表述简单,而且已经成功地用于金属的氢脆、点缺陷(杂质和空位)、表面重构、合金的表面偏析和相稳定的特性的研究。

    Simple as it is , the new embedded atom theory is applicable to metallic hydrogen brittleness , point defects ( impurity and vacancy ), surface reconstruction , surface segregation and phase stabilization of alloys .

  27. Ni-Fe合金镀层具有良好的耐磨性(比同厚度镍镀层高两倍以上),并有低氢脆行为。

    The Ni-Fe coating has excellent wear resistance , about two times as high as that of the pure Ni coating . The properties of Ni-Fe alloy coating are superior to that of the normal all-nickel systems .

  28. 概述了上海石化公司精对苯二甲酸(PTA)装置多年来发现的奥氏体不锈钢设备应力腐蚀开裂、氢脆与腐蚀疲劳开裂事例,对已发生和可能出现的环境敏感断裂原因与对策进行了讨论。

    The stress corrosion cracking , hydrogen embrittlement and corrosion fatigue cracking occur for many years on the austenitic steel equipment in PTA plant in Shanghai Petrochemical Complex . The causes and counter measures for the environment-sensitive cracking which occurred or will possibly occur are discussed .

  29. 水附着拉伸试验中,试样表面附着的水在试样塑性变形时分解出氢使奥贝球铁(ADI)产生氢脆,抗拉强度和伸长率显著下降,发生明显的水脆化现象。

    Tensile strength and elongation of austempered ductile iron ( ADI ) were considerably reduced , resulting in remarkable water embrittlement under water adhesion condition . The water embrittlement was attributed to the hydrogen embrittlement induced by decomposition of water during plastic deformation .

  30. T73和RRA时效处理改善了合金晶界特性,有助于阻止氢脆、减缓晶界阳极溶解速度,提高合金的抗应力腐蚀能力。

    T73 and RRA treatment improve the grain boundary character , which is help to inhibit hydrogen embrittlement and decrease anodic dissolution rate , then to improve the SCCR of the alloy .