孪晶面

Al4C3相是以（003）为孪晶面，以[001]方向为旋转轴的180°二次旋转孪晶。

The Al_4C_3 phases are 180 ° secondary rotation twins with ( 003 ) as twinning plane and direction as twinning axis .

沉积原子处于hcp位置时体系的能量比fcc位置时要高，其增量决定了孪晶面出现几率。

When atoms deposited at hcp positions , the energy of the system is higher than that at fcc positions . The increment decides the probability of twin formation .

选区电子衍射证实，孪晶结构的孪晶面为{111}。

The twin crystal face was measured to be { 111 } by SAED technique .

五重孪晶结构是具有面心立方结构的金属纳米晶体中的重要种类，当它们的{100}面被保护起来的时候，它们可以各向异性生长成纳米线。

Five-fold twinned structures are a class of important members in the family of metallic nanocrystals with face-centered cubic ( fCC ) structures , which can anisotropically grow into nanowires when their { 100 } facets are protected .

我们确认了两种孪晶/双晶结构，它们的孪晶面分别是（0113）和（2112）面。

Two types of twin / bicrystal structures with twining planes as ( 0113 ) and ( 2112 ) have been identified .

发现Al4C3相以孪晶方式存在，六方晶系中存在以（003）面为孪晶面，以[001]方向为旋转轴的180°二次旋转孪晶。

The twinned Al_4C_3 phases exist in hot-dip aluminized steel . In hexagonal system , there is 180 ° secondary rotation twin with ( 003 ) as twinning plane and direction as twinning axis .