固溶度

熔体淬火条件下固溶度亚稳扩展的规律（1）&亚稳扩展的机理及其与Seitz元胞电子密度的关系

Meta-stable Extension of Solid Solubility under Melt Quenching & Part ⅰ: The Mechanism and the Influencing Factors

熔体淬火条件下若干轻稀土金属在Ag中固溶度亚稳扩展的研究

Metastable extension of solid solubility of certain light rare-earth metals in Ag

分析认为，0.50%的Sn可以提高Al原子在α（Mg）中的固溶度。

And 0.50 % Sn addition can increase solid solution degree in Al atom .

若干简单金属与类金属在Ag中固溶度亚稳扩展的研究

Metastable extension of solid solubility of certain simple metals or metalloids in Ag

Tb在快速凝固Ag合金中固溶度扩展

Microstructure and solid solubility of rapidly solidified ag-tb alloy

共沉淀MgO（10.4mol%）-ZrO2粉体中MgO的固溶度

Solid-Solubility of MgO in the MgO ( 10.4mol % ) - ZrO_2 Powder Coprecipitated

结果表明：Mg、Cu粉末在机械合金化过程中是互溶的，机械合金化可以大大提高它们之间的固溶度；

The results showed that Mg and Cu powders could dissolve into each other and the dissolution degree became larger after milling .

Fe4N及氮在铁基体中的平衡固溶度公式

Formulae of Equilibrium Solid Solubility of Fe_4N and Nitrogen in Iron Matrix

稀土族Pm和Tm两元素固溶度的抛物线法预测

Prediction of the Solid Solubility of Binary Alloys Based on Pm , Tm Metals Using Parabola Method

然而Er掺杂入硅依然存在着诸如固溶度低，温度猝灭等缺点。

However , problem still remains in Er-doped silicon , such as low solid solubility , temperature quenching and so on .

等价元素锗（Ge），掺入CzSi中后能提高硅中氧的固溶度和形成氧沉淀的临界半径，使得氧沉淀主要以均匀成核方式进行。

Ge doping in CZ Si can rise solubility of oxygen and critical radius of forming oxygen precipitation .

Ca~（2+）离子在BaTiO3晶格中B位的固溶度

Solid solubility of ca ~ ( 2 + ) in the B site of batio_3 lattice

从磁性测量数据导出淬态试样中Mn在Bi中的固溶度扩展至2.4重量%。

The solubility of Mn in solid Bi in as-quenched samples has been deduced to be 2.4 % from the data of magentic measurement .

结果表明：X射线衍射分析方法是一种测定固溶度的理想方法，这种方法还可以广泛用于无机材料固溶度的准确测定。

It showed that X-ray diffraction technique was a good method for measuring solubility of solid solution , by which the solubility of many inorganic materials could be determined accurately .

用磁性分析法精确测定Ce在a-Fe中的固溶度

Determination of Solid Solubility of Cerium in α - Fe by means of Magnetic Analysis

机械合金化诱导Fe-Cu系固溶度的扩展

Extension of solid solubility induced by mechanical alloying in Fe-Cu system

发现Ru在（NdPd3）中有高达13at%的固溶度。

It was found that the solid solubility of ruthenium in NdPd 3 is up to 13at % at 700 ℃ .

结构表明，凝固冷却速度越快，合金的晶粒和第二相化合物越细小，溶质原子在Mg基体中的固溶度增大。

The result indicate that solidified velocity is more fast , the grains and the second-phase compound of alloy is more fine , and the solubility of solute-atom in Mg matrix increase .

大量铁素体形成的同时，未转变奥氏体中富C，降低了Nb的固溶度，增加了析出驱动力，诱发了Nb（CN）的动态析出。

When massive ferrite formed , the untransformed austenite solute more C , so decrease the solid solubility of Nb , induced dynamic precipitation of Nb ( CN ) .

在Co-Cu系合金中，快速凝固使Co在（Cu）相中的固溶度从平衡条件下的7.46%扩展到20%。

For Co-Cu peritectic alloys , the solubility of Co in ( Cu ) phase is extended from 7.46 % under equilibrium condition to 20 % .

La元素在镁基体中具有较大的固溶度极限，而且随温度下降，固溶度下降很大，满足与镁形成时效硬化型合金的必要条件。

Lanthanum element exhibits big solid solubility limit in the magnesium matrix and the solubility considerably decreases with the temperature decreasing , which is satisfied to form the age hardening alloy .

用点阵参数法研究了在熔体淬火条件下若干简单金属与类金属在Ag中固溶度的亚稳扩展。

The metastable extension of solid solubility of certain simple metals or metalloids in Ag has been studied by means of the lattice parameters measurement when the aUoy specimens quenched from melts .

实验结果表明：在功率超声作用下，铸坯的凝固组织得到了细化，Si元素在α（Al）基体中的固溶度及其分布的均匀性得到了提高，溶质偏析得到了抑制。

Experimental results show that under high-intensity ultrasonication the microstructure is refined , the solid solubility and the uniformity of the distribution of Si in α ( Al ) are improved and the solute segregation is suppressed .

α-Mg相的X射线衍射峰的2θ角向小角度有偏移，表明Al在α-Mg相中的固溶度减少，与元素分布能谱测量结果一致。

α - Mg phase of the X-ray diffraction peak of 2 θ angle with the small offset , that Al in solid solution α - Mg phase the decrease of element content with the point of measurement results .

经过快速凝固技术处理，Si-P系合金的微观组织得到细化，一些合金相的固溶度相对增大。

Microstructure of Si-P alloy is refined greatly by rapid solidification processing .

电磁铸造对Al-Zn-Mg-Cu-Zr合金微观组织及晶内固溶度的影响

Effects of electromagnetic casting on as-cast microstructures and solid solubility inside crystals of Al-Zn-Mg-Cu-Zr alloy

约在525℃热处理时，薄膜居里温度出现在室温附近；较高的热处理温度时，薄膜中形成的钙钛矿相中La的固溶度相对较小，反之则La的固溶度较高。

The Curie point is near room temperature when the film is calcined at about 525 . And the solid solubility of La in the perovskite phase decreases with increasing the calculation temperature of the film , and vice versa .

当Ce含量超过某一临界值，矫顽力突然增加，研究发现此临界值即为Ce在α-Fe中的最大固溶度。

As the cerium content increased beyond a critical value , the coercive force increased abruptly . Based on an elaborate investigation and analysis , the critical value was found to be the maximum solubility of Ce in α - Fe .

粉末X射线衍射（XRD）表明过量Mg极易导致绝缘的MgB6和MgO杂相，Mg在MgB2中的固溶度很小，正常态电阻率随Mg过量增加而迅速增大。

The powder X-ray diffraction patterns indicate that the excess amount of Mg lead easily to the insulating MgB_6 and MgO impurities and the solubility of Mg in MgB_2 is limited . The resistivity in normal state increases rapidly with increasing x.

Mg-Al-Ca合金在化学驱动力较小的条件下，可以通过机械驱动力的作用提高Ca、Al在Mg中的固溶度，导致非晶转变的发生。

The formation of the amorphous phases in the Mg-Al-Ca system can be realized by expansion the solubility limit of Ca and Al in Mg via the mechanical driving force , even when the chemical driving force is very small .