耐压强度

加入硅质材料可以降低钢渣的C／S比，使水化产物中的硬硅钙石含量增加，耐压强度提高；

Siliceous material added may decrease the C / S of steel slag , increase the content of xonotlite in hydrates and compressive strength ;

结果表明：PVA的加入量增加使陶瓷膜管的孔隙率和孔半径增大、密度和耐压强度减小、孔径分布变宽，气体渗透量增大；

The results show that porosity and mean pore diameter increase and density and compressive strength reduce with increase of PVA amount ;

抗压强度，耐压强度strength油压强度试验

Compressive strength , compression strength oil pressure test for

并进一步对Yb掺杂的（Ba，Sr）TiO3材料的耐压强度进行了研究。

The withstand voltage properties of Yb-doped ( Ba , Sr ) TiO 3 was investigated also .

基于MSP430单片机开发了一种新型的纸张耐压强度检测系统。

A new type of intensity test system for compression resistance of paper based on MSP430 is developed .

试验结果表明，煅烧石膏和煅烧明矾石单掺和复合双掺的掺入量为5%时，水泥的凝结时间明显缩短，3d耐压强度在各温度下均有显著提高。

Experimental results show that , when calcined gypsum and calcined alunite were added by 5 % alone or synchronously , the setting time of cement decreases remarkably and 3d compressive strength at different temperatures increases remarkably .

通过改变Al2O3的加入量，探讨了Al2O3的加入对烧成镁钙砖的体积密度、显气孔率和耐压强度的影响；

It discussed the effect of Al_2O_3 on volume density , superfical porosity and compressive stregth of the burned magnesia_ calcia bricks through changing the Al_2O_3 content ;

结果表明：在刚玉材料中同时加入锐钛矿和单质Si能降低材料的显气孔率，提高材料的抗折强度和耐压强度，并有钛酸铝和莫来石生成；

The results showed that adding TiO_2 and silicon can obviously enhance the MOR and CCS and decrease the apparent porosity of corundum materials , and accompanying the forming of aluminum titanate and mullite .

结果表明，氯氧镁水泥能明显提高不烧砖（110℃×24h和1600℃×3h）耐压强度；

The results show that magnesium oxychloride cement can improve cold crushing strength ( 110 ℃× 24h , 1600 ℃× 3h ) of unburnt brick significantly .

ZnO的加入使瓷料形成致密的细晶结构，有效地阻止了晶粒过度长大，改善了微观结构，减小了因气孔而造成的击穿，提高了耐压强度。

Doping ZnO made the size of the grain smaller and formed the densified structure , which restrained the over - grown of grain effectively and improved the compressive-strength and microstructure of the ceramics .

对浸渍前后试样的理化性能和孔隙率进行了分析，结果表明：经两种溶胶浸渍后，试样的Cr2O3含量增加，耐压强度和体积密度略有升高，显气孔率显著下降；

The results from pore size distribution and physical-chemical analysis show that Cr_2O_3 contents of specimens increase , cold crushing strength and bulk density of specimens increase a little but apparent porosity decreases markedly after impregnation .

与PZT的发射性能相比，NBT发射电流密度稍低，但NBT具有更低的发射起始阈值，更高的耐压强度和更好的退极化性能。

NBT has lower current density than that of PZT , but the switching threshold of emission is lower and the depolarization property is better .

高炉喷补料受CO破坏的程度与其常温耐压强度的变化相对应，因此，可以用抗CO试验后试样的常温耐压强度变化来定量表征其抗CO破坏能力的强弱。

The destruction degree of the specimens by CO corresponds with the change of crushing strength . Therefore , the resistance to CO of the gunning mix can be quantitatively measured according to the change of cold crushing strength of the specimens .

采用MgCl2·6H2O和ρAl2O3为结合剂时，浇注料1100℃3h热处理后的耐压强度明显下降；

The CCS of the castable after treated at 1100 ℃ for 3 h using MgCl 2 · 6H 2O or ρ - Al 2O 3 as binder decreases apparently .

该材料耐压强度大于50MPa，导热系数小于0.6W／（m·K），热震稳定性＞150次。

The material 's crushing strength > 50MPa , coefficient of heat conductivity < 0 . 6W / ( m. K ), resistance to thermal shock > 150 cycles .

常温耐压强度高达160MPa以上；

Compressive strength at room temperature is as high as 160MPa ;

结果表明，随着α-Al2O3质量分数的增加，经1000℃×3h热处理后，浇注料的线变化率逐渐增大，显气孔率增加，耐压强度提高；

The experimental results show that the permanent linear change , apparent porosity and cold crushing strength of the castable heat-treated at 1 100 ℃× 3 h increase gradually with the increase of α - Al2O3 content .

分别测定了在烘干（110℃×24h）和中温处理（1100℃×3h）后试样的显气孔率，体积密度，抗折强度和耐压强度。

The property of bulk density , apparent porosity , modulus of rupture and cold crushing strength of the specimen after the drying ( 110 ℃× 24h ) and sintering ( 1100 ℃× 3h ) were tested separately .

为了提高镁铬耐火材料的烧结性能，通过考察气孔率、体积密度和常温耐压强度与Al2O3加入量之间的关系，讨论了Al2O3添加剂对两种不同镁铬耐火材料致密化的影响。

For improving the sintering property of magnesia-chrome refractory , the effect of alumina addition on the densification of two types of magnesia-chrome refractories was studied by investigating the relationships between porosity , bulk density and cold crushing strength and the quantity of alumina addition .

另外，与常规的不锈钢相比，317L合金具有更高的延展性、抗应力腐蚀性能、耐压强度及耐高温性能。

In addition , when compared with conventional stainless steel , 317L alloys have higher ductility , resistance should be Corrosion strength , compressive strength and high temperature performance .

通过颗粒级配、结合剂和添加物的选择和加入量的试验，研制出中温（1000℃，3h）耐压强度达50MPa以上的镁质捣打料。

A magnesia ramming mix with 50 MPa compression strength ( 1000 ℃, 3h ) has been developed by grain grading , selecting of binders and additives and performing an experiment on the amount of the additives .

研究α-Al2O3微粉加入量对钢包渣线用镁铝质浇注料线变化率、显气孔率、耐压强度和抗渣性能的影响，借助EDAX分析，探讨了浇注料的渣蚀机理。

The influence of α - Al2O3 micropowder additions on permanent linear change , apparent porosity , cold crushing strength and slag resistance of MgO-Al2O3 based castable is studied in this paper . By EDAX analysis , the mechanism of slag corrosion is investigated .

结果表明：采用SiO2微粉和MgCl2·6H2O为结合剂时，镁质浇注料110℃24h处理后的耐压强度和抗水化性能优于采用ρAl2O3的；

The experimental results show that the CCS and hydration resistance of magnesia based castable ( treated at 110 ℃ for 24 h ) using ultrafine SiO 2 or MgCl 2 · 6H 2O as binder are better than those of using ρ - Al 2O 3 as binder .

焦炭颗粒耐压强度表征方法探讨

A new characterization method for testing the compressive strength of coke particles

提高真空灭弧室沿面耐压强度的软包硅橡胶方法

Study on silicone rubber applied to improve withstand voltage of vacuum interrupter

压缩机壳体耐压强度计算机控制试验系统

Research on the Computer Control Compression Strength Testing System of Compressor Shell

工艺因素影响焦炭颗粒耐压强度的试验研究

Study on technological factors on compressive strength of coke particles

瓦楞纸箱开孔对耐压强度的影响

The Effects of Holing Corrugated Fiber Box on Pressure-resisting Strength

GB/T3997.2-1998定形隔热耐火制品常温耐压强度试验方法

Shaped insulating refractory products & Determination of cold crushing strength

提高电抗器线圈层间绝缘块的工频耐压强度

Improving the Power Frequency Withstand Voltage of the Insulating Piece for the Reactor