胶接

本文通过德国凤凰公司的钢芯输送带在德兴铜矿的具体运用，来阐述凤凰钢芯输送带的结构及其联接头的胶接方式。

According to the practice application of steel-cored conveyer belt made by Phoenix company in German in Dexing copper mine , this article describes the construction and connector cementing methods of Phoenix steel-cored conveyer belt .

胶接结构在使用存储过程中，受热、潮湿、氧、腐蚀介质等环境因素的作用发生老化，导致其强度逐渐下降，不能满足使用要求，甚至完全破坏。

Owing to the effect of heat , humidity , oxygen and corrosive media , cementing structures tend to age during service or storage . As a result , the strength of the structures will decline and failure may occur .

通过在低毒脲醛树脂胶粘剂调制过程中加入低成本API对低毒脲醛树脂胶粘剂进行改性，亦能改善胶合板板坯的预压性能和胶合板的胶接强度。

Adding low cost API to UF resin can also gain the same purpose .

CFRP界面胶接性能的研究

Study on the Interface Adhesion of CFRP

钢/橡胶胶接结构脱粘缺陷Lamb波检测的模式选择

Mode Selection for Detecting Disbonding in Steel / Rubber Adhesive Bonding Structure by Using Lamb Wave stuck-on particle

对水性高分子-异氰酸酯胶黏剂（API）主剂进行改性，以提高API的耐水、耐热及胶接硬木的性能。

Aqueous vinyl polymer-isocyanate adhesive ( API ) was modified to improve its bonding strength , water - and heat-resistance when it was used for hardwood bonding .

用3种低毒脲醛树脂胶粘剂压制胶合板及中密度纤维板试验，对不同固化体系UF树脂胶粘剂的胶接性能和甲醛释放量进行了研究。

The bonding properties and formaldehyde emission of UF resin in different curing systems were studied by pressing plywood and MDF bonded with low toxicity UF resin .

采用3种典型的脲醛（UF）树脂合成方法合成UF树脂，并对合成UF树脂的性能、化学构造、胶接性能、甲醛释放量及其固化历程进行了研究。

The paper discussed the properties , chemical structures , bonding performances , formaldehyde emission and curing mechanism of urea-formaldehyde ( UF ) resins by three typical synthetic technologies .

介绍了航空结构胶接用SY－24中温固化胶接体系的全面胶接性能，该胶接体系的研究及在航空结构件上的使用概况。

All joint properties , survey and use in aeronautical structural joint component of SY - 24 moderate temperature cured adhesive system were introduced .

特别是针对通常情况下低F/U摩尔比UF树脂固化速度慢、胶接性能不理想的问题，可以通过合成工艺和改性剂以及不同固化体系得以解决。

Especially on slow curing speed and unideal glue bond properties UF resin with low molar ratio , it can solved by synthesis technology , modifier and different curing system .

制备了一种有机硅胶粘剂，该胶粘剂主要由苯基硅橡胶与MQ硅树脂组成，对影响该胶粘剂胶接强度的因素进行了研究。

A kind of high - temperature - vulcanization silicone adhesive mainly consisted of phenyl silicone rubber and MQ resin was prepared , and factors having effects on its adhesive strength were investigated .

利用有限元软件ANSYS，首次对单搭接胶接接头进行拓扑优化，结果表明：接头承载较大时门槛值k取0.2较为适宜，承载较小时取0.3较为适宜；

Finite element software ANSYS is applied to optimize the adhesively bonded single lap joint topologically for the first time . The results showed that the threshold values 0.2 and 0.3 are appropriate for joint under low load and large load respectively .

第二代丙烯酸酯胶黏剂（SGA）由于具有室温快速固化和可进行带油表面的胶接等一系列优点，得到极大的推广应用。

The second generation acrylate adhesives have been largely applied in the bonding field just because their advantages such as room temperature curing and suitable for oleic surface bonding .

通过在SY-23B胶粘剂中加入偶联剂KH-550，能使其胶接强度和抗冲击强度得到提高。

Mixed with KH-550 as coupling agent , the pressure shear strength of the adhesive SY-23B is promoted .

胶接修补复合材料层合板失效分析的PDA-CZM方法

PDA-CZM Method for Failure Analysis of Bonded Repair of Composite Laminates

试验结果表明：采用H2O2溶液处理落叶松木材表面可以提高其胶接强度，用H2O2溶液处理过的落叶松表面比未处理过的落叶松素材的常态压缩剪切强度提高15%。

Experimental results showed the treatment could improve bond properties of treated material , and the dry compressing shear strength of Larch specimen trated with H2O2 solution was raised by 15 % comparing with that of untreat one .

结果表明：该胶粘剂对铝有较好的胶接强度，其剪切强度与MQ树脂的结构有很大关系，随MQ树脂用量的增加而提高，催化剂的种类和用量对胶接强度也有影响。

The results showed : this kind of adhesive had high adhesive strength for Aluminium , the adhesive strength related to the structure Of MQ resin , the content of MQ resin , the type and the amount of catalysis .

因此选择S0和A0模式兰姆波进行检测，能够增强深层回波信号能量，为胶接质量分析提供更有效的信息。

As a result , deep-interface echo signal energy can be strengthened and effective bond quality information can be obtained when S0 or A0 mode for testing is chosen .

对胶接接头中的AU信号进行了时频分析，分析了接头中信号的Lamb波组成，AU信号通过胶接接头后各信号分量经历了不同程度的衰减，并伴随有Lamb波的模式转换。

The AU signals in adhesive joint were analyzed by time-frequency method and the Lamb modes were separated in time-frequency space from AU signal . The components of AU signals attenuated sharply and accompanied by mode conversions when they passed the overlap regions of adhesive joints .

试验研究表明，偶联剂KH-550可显著地提高环氧胶粘涂层的胶接强度。耐磨性和耐水性。

In this paper , the strengh , abrasion resistance and waterproof of the epoxy bonding coating can be strengthened by adding the coupling agent KH-550.The optimal amount of KH-550 is presented .

讨论了水基聚氨酯木材胶粘剂的反应机理和影响其胶接性能的主要因素，进行了SR－100木材结构胶制备集成材的应用试验。

Preparation of Water based polyurethane high-frequency welding adhesive The reaction mechanism and application properties of water based polyurethane adhesives were studied . SR - 100 structural adhesive for wood was used for manufacture of glued laminated timber from spruce , Siberian elm , Manchurian ash mongolian oak .

本文选取SY-H2糊状胶粘剂，综合对比了胶接试样、铆接试样和胶铆试样的力学性能和耐疲劳性能。

SY-H2 paste adhesive have been selected in this paper to study the mechanical and fatigue properties of bonded , riveted and bond-riveted samples .

最后讨论了SYH2糊状胶粘剂固化温度对胶接试样剪切强度的影响，在固定的固化时间内升高固化温度有助于提高胶接强度，最佳固化工艺参数为130～140℃固化2h。

Finally , influence of cure temperature on shear strength of SY H2 paste adhesive was discussed . Increase of cure temperature in a given time can improve the bonding strength . Optimal curing parameter was suggested to be from 130 ℃ to 140 ℃ for two hours .

研究了Uron树脂及其使用方法对降低脲醛树脂胶粘剂游离甲醛含量及胶接胶合板甲醛释放量的作用与效果。

The effects of different formaldehyde / urea molar ratio Uron resins and different using methods on reducing free formaldehyde content of UF resins and formaldehyde emission value of its bonded plywood were studied .

介绍了用于不锈钢管增强的SY-ZQ增强带的力学性能及加速老化性能、胶接工艺和典型件的疲劳性能。

In this paper , mechanical and accelerated aging properties of SY-ZQ adhesive bonding reinforced strap which is used to strengthen the welding line of stainless steel tube , bonding process and fatigue properties of representative pieces were introduced .

导出了纤维金属胶接层板双面裂纹搭接剪切（DCLS）试样分层尺寸和柔度之间的线性关系式，提出了DCLS试样分层尺寸的柔度测量法，并与用光测法测得的分层尺寸进行了对比。

For a modified Double Crack Lap Shear ( DCLS ) specimen of fiber reinforced metal laminates , an expression which relates its delamination size and its compliance is derived . A method for determining the delamination size in DCLS by compliance test is developed .

利用模拟空间热循环温度场设备对太阳能电池中石英玻璃盖片/硅橡胶粘合剂/硅晶片胶接结构进行了真空热循环试验（123～403K，10-5Pa）。

The vacuum thermal cycling tests ( 123 ~ 403K , 10 - 5 Pa ) were carried out on the bonding structure of quartz glass cover / silicon rubber adhesive / silicon crystalline in solar battery , using the system simulating the temperature filed of thermal cycling in space .

热熔涂塑&胶接技术的一种新工艺

Hot Melt Plastic Coating & A New Process of Bonding Technology

飞机结构损伤的复合材料胶接修补技术研究进展

A Review on Composite Bonded Repair Technique for Damaged Aircraft Structures

高含水率单板胶接工艺的研究

Study on the Bonding Process of Veneer with High Moisture Content