海工混凝土
- 网络Marine concrete;Concrete in sea water
-
基于MonteCarlo随机计算的海工混凝土使用寿命预测
Service life prediction of marine concrete based on Monte Carlo stochastic calculation
-
在早龄期时由于海工混凝土的孔隙率高、孔径大于50nm的大孔数量多,因此其抗氯离子渗透能力较弱;
Owing to high porosity and high proportion of coarser pores ( 50 nm ) in marine concrete at early ages , its chloride-permeation resistances is weaker .
-
通过测试胶凝材料水化热、混凝土的坍落度和氯离子扩散系数、抗裂等级等性能,对C40海工混凝土的配合比进行了优化设计。
The mixture ratio of C40 marine high performance concrete is optimized through test of the hydration heat of binding material , slump , chloride ion diffusion coefficient , anti-crack rand of concrete .
-
东海大桥高性能海工混凝土抗裂性控制技术研究
Research on Crack Resistance of High Performance Concrete in Donghai Bridge
-
粉煤灰和磨细矿渣在海工混凝土中的应用
Application of the fly ash and ground slag on marine concrete
-
热带海洋环境与海工混凝土
On the Tropical Environment and the Concrete for Marine Engineering
-
海工混凝土结构表面涂层暴露试验及应用效果
Analysis of Exposure Experiment and Application of Coatings for Marine Concrete Structures
-
提高海工混凝土抗氯离子渗透性的关键技术
Key Technology for Improving Resistance Against Chloride Ion Penetration of Marine Concrete
-
辽河特大桥海工混凝土钻孔灌注桩冬期施工技术
Construction Technology of Marine Concrete Bored Piles of Liaohe Bridge in Winter
-
耐用期超过25年的海工混凝土表面涂料
Face Coating for Marine Concrete with Durability over 25 Years
-
海工混凝土钢筋锈蚀速率预测模型研究
Forecast Model of Steel Corrosion Rate of Marine Concrete
-
高性能海工混凝土在东海大桥工程中的应用
Application of Marine High Performance Concrete to Donghai Bridge
-
矿物掺合材料在高性能海工混凝土中的应用
Use of Mineral Admixtures in High Performance Marine Concrete
-
海工混凝土防护措施研究
Research on the Protection Materials for Marine Concrete Structures
-
海工混凝土工程耐久性设计探讨
Study on Durability Design of Marine Harbor Concrete Engineering
-
海工混凝土的氯离子扩散性与寿命评估
Life Assessment and Chloride Ion Diffusivity of Marine Concrete
-
聚丙烯纤维对海工混凝土抗氯离子渗透能力的影响
Effect of polypropylene fiber content on chlorine anion penetration resistance of marine concrete
-
海工混凝土现浇施工方法对耐久性的影响
Influence of construction method on durability of marine concrete
-
海工混凝土使用寿命预测研究
Research on Service Life Prediction of Marine Concrete
-
海工混凝土早龄期抗氯离子渗透性能的研究
Variation of Chloride-Permeation Resistance of Concrete for Ocean Construction with Time at Early Ages
-
超长大直径海工混凝土桩基冬季施工技术
Winter Construction Technique of the Super Long and Large Diameter Piles of Marine Concrete
-
华南地区两个码头海工混凝土结构耐久性调查
The Investigation of the Durability of Marine Concrete Structures of Two Quays in South China
-
高性能掺合料改善聚丙烯纤维海工混凝土性能的研究
Study on improvement of characteristics of polypropylene fibre reinforced marine concrete with high performance admixture
-
辅助胶凝材料和外加剂对海工混凝土耐腐蚀性的影响
Effect of different admixtures and SCMs on the corrosion resistance of concrete for marine engineering
-
高性能海工混凝土灌注桩施工问题及方案改进措施研究
Research on the solutions of high performance marine concrete piles construction and the improvement measures
-
对防止钢筋腐蚀提高海工混凝土结构的耐久性具有重要意义。
It is important to prevent corrosion of reinforcement for durability of marine concrete structures .
-
海工混凝土结构的防腐蚀
Corrosion prevention of marine concrete structures
-
海工混凝土结构钢筋表面去钝化时间的预估方法
Prediction Method for the Time of Destroying Reinforcement Protective Film of Concrete Structure in Marine Environment
-
磨细高炉矿渣对海工混凝土抗冻性和氯离子扩散性能的影响
Effect of ground granulated blastfurnace slag on both frost-resistance and chloride ions diffusion properties of marine concrete
-
基于环境的海工混凝土耐久性试验与寿命预测方法研究
Study on Methods of Accelerated Testing of Marine Concrete Durability Based on Simulating Environment and Service Life Prediction