T92 / HR3C dissimilar steel welded joints is completely suitable under the conditions of high-capacity ultra-supercritical unit ( USC ) .
T92/HR3C异种钢焊接接头在大容量超超临界机组(USC)条件下服役是完全安全可靠的。
-
Through hardness test , impacting test , SEM of failure surface and microstructure observation , the relationship between the toughness and its microstructure of welding joint of T92 steel was studied .
通过硬度试验、冲击试验、断口扫描和金相组织观察,研究了T92钢焊接接头的韧性与组织的关系。
-
The detailed research contents and results are summarized as follows : 1 . T92 / HR3C , T92 / Super304H dissimilar materials joints are obtained by gas tungsten arc welding ( GTAW ) process .
本文具体研究工作及结果如下:1.采用钨极氩弧焊(GTAW)焊接工艺对T92与奥氏体钢HR3C,Super304H分别进行焊接,获得T92/HR3C,T92/Super304H异种钢焊接接头。