热定形

涤纶DTY丝热定形后动态力学行为

Dynamic Mechanical Behaviour of DTY PET after Heat Setting

随着热定形温度的提高，WE的热收缩率及弯曲刚度表现出比WP更明显的提高。

The shrinkage and bending rigidity of the WE fabric showed greater increase than WP as the heat setting temperature was increased .

用DSC测定涤纶仿真丝织物的热定形温度

DSC Determination of Thermal Setting Temperature for Polyester Silk-like Fabric

预热定形后，PTT织物的碱减量率比未热定形的织物明显降低；

After pre-setting at150 ℃, the alkali deweighting ratio of PTT fiber was clearly decreased compared with the fabric without heat-setting .

本文述及热定形后平纹织物中PEL长丝纤维的形变和力学性能。

The article deals with deformation and mechanical properties of woven PET fabric after heat-setting .

对测试结果进行分析和比较，找出了PTT针织物较佳的热定形温度和时间。

The experimental results wre analyzed and compared , and the best temperature and time of thermal setting for PTT knitted fabric was determined .

选择适当的温度和拉伸比进行热定形，可提高PTT织物的断裂强力和弹性回复率，但其延伸性变差。

The breaking strength and resilient-elasticity recovery of PTT fabric can be increased under suitable temperature and drawing ratio during heat setting , but its dilatability took worse .

热定形温度升高，色牢度下降；

Color fastness decreased as the heat - setting temperature increased ;

并分析了该方法的加捻、热定形、退捻变形过程；

The process of twisting , heat-setting and untwisting was analysed .

工业控制计算机在纺织物热定形机中的应用

Application of Industrial Personal Computer in Heat Setting Machine for Textile Products

不锈钢衬环热定形工艺探讨

Research on the Stainless Steel Ring gasket Hot set Technology

提高钢带活塞环弹力的新方法&热定形法

New Approaches to Increasing the Elastic Force of Steel Strip Piston Ring

含涤纶织物热定形温度和热溶染色性能的关系

Relation between Heat Setting and Thermosol Dyeing of Polyester Fabric

热定形机上对纺织物测温的研究

Temperature Measurement of Textile Fabrics on a Heat Setting Machine

热定形性，热变定性干熄焦余热锅炉过热器传热特性研究

Study on the characteristics of heat transfer for super-heater in CDQ boiler

织物表面应该洗刷和热定形。

The fabric finish shall be scoured and heat set .

热定形的工艺条件必须十分准确地加以控制。

Heat - setting conditions must be very accurately controlled .

分散常压可染改性涤纶热定形及染色特性探讨

Heat Setting and Dyeing Property of Disperse Dyeable Modified PET under Atmospheric Pressure

采用干法热定形还是湿法热定形取决于纤维的类型。

Either wet or dry heat may be used depending on the fiber .

热定形对聚酯纤维微结构和碱减量整理的影响

The Effects of Heat Setting on the Microstructure and Alkali Peeling of PET Fibers

本文对含涤纶织物热定形工艺和热溶染色性能的关系进行了研究。

The relations between the technologies of heat setting and thermosol dyeability is investigated .

染色采用阳离子染料，染色温度为110℃；热定形温度控制在150℃；

The optimal process condition was dyeing at110 ℃ with cationic dyes and heat-setting at150 ℃ .

涤纶织物碱胺同浴改性前热定形条件选择

Selection of Thermosetting Conditions for Polyester Fabric before One - bath Modification with Alkali and Amine

对于人造纤维来说，热定形是整理过程是一个重要工序。

Heat setting is an essential step in the finishing process for man - made fibers .

这种经过热定形的织物具有极佳的免烫性能，受到社会的热烈欢迎。

These heat - set fabrics with the remarkable no - iron property were enthusiastically accepted .

后整理要严格控制热定形温度，一般以不超过185℃为宜

In the post treatment , setting temperature should be controlled strictly , normally not over 185 ℃

热定形性，热变定性相变蓄热换热强化及蓄热器性能实验相变储热预热式热泵热水器节能特性分析

Heat Transfer Enhancement of Phase Change Thermal Storage and Experimental Research on Characteristics of Phase Change Heat Exchanger

在分开的拉丝机上进行拉伸、热定形、起皱和干燥步骤。

The drawing , thermal setting , creping and drying steps are carried out on a separate drawing bench .

试验结果表明，测温装置适合于热定形机的现场测温。

Test results show that the instrument is suitable for measuring the cloth temperature on a heat setting machine .

热定形的目的是使由这些纤维制成的织物具有一定的尺寸稳定性和一定的形状。

The major reason for heat setting is to give dimensional stability and shape to cloth made from these fibers .