通过微型电炉实验、差热分析（DSC）和热失重分析（TG），研究了烷基磷酸酯胺盐的酯化率对超薄型钢结构防火涂料的影响。

The effect of the esterification degree of amine salt of alkyl phosphate on the intumescent coating was studied through the small scale fire tests , TG and DSC method .

阐述钢结构防火保护的重要性，介绍了目前常用的超薄型钢结构防火涂料的组成、作用原理，并采用热分析、XRD对涂料的作用过程进行了分析。

This article presents the importance of steel structure fireproofing protection and introduces the compositions and func - tioning principle of the present super-thin fireproofing coatings . Functioning process of the coatings are analyzed with thermo - analysis and XRD method .

用正交优化工艺制备的防火涂料，涂覆比10kg/m2时，耐火时间超过2h，可作超薄型钢结构防火涂料使用。

The preparation technology was optimized by orthogonal experiment , and it was found that as coating ratio was 1 0 kg / m 2 , the fireproof time was over 2 h , which proved that the coating could be used as ultra filmy steel structure fireproof .

树脂基料对水性超薄型钢结构防火涂料性能的影响

Effects of matrix resins on the super-thin coatings for steel structures

超薄型钢结构防火涂料阻燃体系的研究

The study on fire-resistant system of ultra-thin fireproof coating for steel structure

硅丙乳液超薄型钢结构防火涂料的制备

Preparation of Silicone-acrylate Emulsion Ultrathin Steel Structural Fireproofing Coating

硅溶胶改性水性超薄型钢结构防火涂料的研究

Study on water-borne ultra-thin fire resistive coating modified by silica solution for steel structure

烷基磷酸酯胺盐的酯化率对超薄型钢结构防火涂料的影响

Influence of Esterification Degree of Amine Salt of Alkyl Phosphate on Thin Film Intumescent Coating

丙烯酸树脂用作超薄型钢结构防火涂料基料的研究

The Study of Acrylic Resin as the Binder of Super-thin Fire Retardant Coatings for Steel Structures

用热重对溴碳酚醛环氧超薄型钢结构防火涂料进行了动力学分析，并确定了动力学方程同时对阻燃机理进行了探讨。

Additionally , we used thermogravimetric to analyze dynamic equation for fireproofing coating of bromine-carbon phenol epoxy resin with extra-thin steel structure .

超薄型钢结构防火涂料防火效率高、用量少、施工方便且具有很好的装饰性能，近年来取得了广泛的应用。

For high efficiency of fireproofing , decoration and facilitation of using , Ultra-thin steel structure fire retardant coating has been on a wide range of application in recent years .

TBA环氧树脂超薄膨胀型钢结构防火涂料的研究

The Synthesis of TBA Epoxy Resin Based Super - thin Intumescent Fire - Retardant Coatings for Steel Structure

水性超薄膨胀型钢结构防火涂料的制备与性能

Preparation and Properties of Water-Based Intumescent Ultrathin Fireproof Coating for Steel Structure

室内用超薄膨胀型钢结构防火涂料

Super Thin Intumescent Coatings for Interior Steel Structure

一种超薄膨胀型钢结构防火涂料的研制

Development of Ultra-thin Intumescent Coatings for Steel-structure

成膜物对水性超薄膨胀型钢结构防火涂料的综合性能起到重要的作用。

Film former plays the key role in waterborne ultra-thin intumescent fireproof coating for steel structures .

改性膨润土作为防渗材料的可行性研究水性超薄膨胀型钢结构防火涂料的制备与性能

Research on Feasibility of Modified Bentonite as Impermeability Material ; Preparation and Properties of Water-Based Intumescent Ultrathin Fireproof Coating for Steel Structure

结果表明，添加适量的聚有机硅氧烷乳液后，水性超薄膨胀型钢结构防火涂料的炭化层状态、防火性能、膨胀倍率都有很大改善。

The experimental results show that the state of charring layer , fire retardant properties and intumescent rate of the coatings are improved by the addition of proper content of silicone emulsion .

当基料中聚有机硅氧烷乳液用量为32.9%（质量分数，下同），基料用量为16.7%时，水性超薄膨胀型钢结构防火涂料的综合性能最好。

The coating has the superior properties when the content of silicone emulsion in the binder is32.9 % ( by mass ) and the content of binder was16.7 % ( by mass ) .

超薄型钢结构防火防腐蚀涂料的研制这种全新的结构型式，火灾时能够真正起到防火隔烟的作用。

Development of fire proof and anticorrosion paint for ultra thin steel structure This type fire door can work in case of fire .

超薄型溴碳酚醛钢结构防火涂料的研制GB1404-1995酚醛模塑料

Preparation of Bromine Carbon Phenolic Resin Ultra-thin Fire-retardant Coatings for Steel Structure

室外膨胀超薄型氯醚树脂钢结构防火涂料

Chlorinated Polyether Resin Based Extra - Thin Dilatant Fire Proofing Coatings for Outdoor Steel Structures

超薄型饰面膨胀型钢结构防火涂料的研制（I）

Development of ultra - thin ornamental expansion - type fireproof paint for steel structures ( I )