聚己内酰胺

以原位复合方法合成的稀土发光聚己内酰胺（PA6）为研究对象，用差示扫描量热仪（DSC）研究了其结晶行为。

The crystallization behavior of rare-earth luminous polycaprolactam ( PA6 ) prepared through in-situ polymerization was investigated by DSC .

综述聚己内酰胺（PA6）纤维及其单体己内酰胺（CPL）的国内外生产、消费现状。

The domestic and international production and consumption of polycaprolactam fiber and caprolactam ( CPL ) were reviewed .

合成了14种由三种含喹（哑心）啉环的芳香化合物改性的聚己内酰胺（MC尼龙），并对其形态、抗冲击强度、吸水性及熔融行为等进行了表征。

Fourteen MC nylons ( polycaprolactam ) modified by three aromatic compounds containing quinoxaline ring were prepared . Their morphology , impact strength , water absorbency and melting behaviour were characterized .

聚己内酰胺切片萃取水回用直接聚合工艺探讨

Discussion on direct polymerization process for recovery extract water of polycaprolactam chip

聚己内酰胺切片生产中干燥工艺的研究

Drying Process in the Production of Polycaprolactam 6 Chip

影响聚己内酰胺质量的主要因素

Main Factor Affecting the Quality of Polycaprolactam

聚己内酰胺-锌盐相互作用的研究

Interaction between Polyamide and Zinc Salt

芳纶浆粕是聚己内酰胺的α成核剂，复合材料的维卡热变形温度大幅度提高，熔体粘度增加，但粘流活化能不变。

PPTA pulp is a good a crystal nucleus of nylon 6 . The hot deformation temperature of the compound increases , the viscosity of the melt of the compound increases , but the activation energy is constant .

在改性聚磷酸铵中加入聚己内酰胺（PA6），可显著提高由它们组成的膨胀型阻燃剂（IFR）对聚丙烯（PP）的阻燃作用，PA6在其中主要起成炭剂的作用。

The flame retardation of an modified ammonium polyphosphate based intumescent flame retardant ( IFR ) on polypropylene ( PP ) can be greatly improved by incorporating with polycaprolactam ( PA6 ) . In the IFR , PA6 acts as a charring agent .