纤维平均长度
- 网络Average fiber length;m m
![纤维平均长度](../cache/1178129.jpg)
-
纤维平均长度由于细小级分流失有所增加;
The average fiber length increased due to fines loss .
-
纤维平均长度及其仪器法测定结果分析
Average Fiber Length and Its Instrumental Measurement Result Analysis
-
实验表明,与桉木浆相比,麦草浆有较大的比表面积,纤维平均长度小,羧基含量稍低,电导率与阳离子需求量较高。
Bleached chemical wheat straw pulp has larger specific surface area , shorter length weighted length , lower carboxyl content , higher conductivity , and more an-ionic trash than the eucalyptus pulp .
-
纤维平均长度约为1.0mm,长度分布较为均匀,杂细胞含量相对较少。
The fiber length of the palm thread was relatively short with fiber average length of about 1.0 mm , however fiber length distribution was relatively uniform . The non-fiber cell content was relatively low .
-
断裂比强度除了与纤维上半部平均长度、伸长率有极显著关系外,和铃重、衣分也呈极显著的负相关。
The fibre specific breaking strength was also significantly correlative with fiber elongation , and presented significantly negative correlation with boll weight and lint percentage .
-
Al2O3纤维的平均直径和长度分别为3~5μm和数百μm,比相同直径的细磨粒具有较大的结合面积和强度。
The average diameter of Al 2O 3 fibers is about 3 ~ 5 μ m and their length in the range of several hundred μ m , thus have relatively larger bonding areas and strength .
-
随着纤维含量的增加,纤维的平均长度增加,并且没有发生断裂的纤维的含量越来越多;
With the increase of diameter , the rupture velocity of short fibers becomes slow and their average length increases .
-
细小纤维含量和纤维扭结指数降低,纤维平均长度和纤维粗度增加。
The fines content and kink index of fiber obviously decreased while the fiber length and fiber coarseness increased .