粒状

观察到该合金在800℃加热时小尺寸粒状M（23）C6沉淀；

It is observed that small granular M_ ( 23 ) C_6 precipitates at 800 ℃ .

X射线衍射法鉴别粒状贝氏体组织

Granular bainite D is crimination by X-ray diffraction method

PLC及通讯技术在粒状棉生产控制中的应用

Application of PLC and Communication on produce control of loose wool

本研究以酸性红B为对象，进行了粒状活性炭对酸性红B吸附扩散过程的研究。

The adsorption and diffusion kinetic process of acid red B adsorbed by active carbon in aqua was reported .

Al&Si合金在热处理时发生共晶Si的粒状化。

The eutectic silicon in Al-Si alloys can be granulated during heat treatment .

通过加热实验和红外光谱分析、X射线衍射分析揭示粒状黄磷渣在加热过程中所发生的一系列物相演变。

Under heating treatment , the slags showa series of phase transitions by IR and X-ray analysis .

研究发现γ中的固溶Nb和游离态B是粒状贝氏体形成的先决条件。而且B含量对获得完全贝氏体转变强化效果有一个临界值。

Study shows that solid soluble Nb in γ and free B are prerequisites for the formation of granular bainite .

大型DAP装置改产粒状MAP的工艺选择

The transferring process choice of granular MAP production in large scale DAP plant

SEM实验表明，镀层表面形貌为团粒状，颗粒大小较不均匀。

SEM experiment displays that the deposit has a ( surface ) morphology of granular structure with uneven grain sizes .

作者介绍了X线照片均方根值（rootmeansquare，RMS）粒状度的测试原理及方法。

In this paper the principle and method of testing of RMS ( Root Mean Square ) graininess of radiograph were described .

Fe-SiO2和Fe（20）Ni（80）-SiO2粒状固体矫顽力的研究利用趋近饱和定律求出这些粒状固体的有效各向异性常数。

MECHANISM OF THE COERCIVITY FOR THE GRANULAR SOLID The effective magnetic anisotropy is obtained using the law of approach to saturation .

在SEM下其颗粒主要呈粒状、棱角状和碎裂状，大小约2~5μm；

Under SEM , the crystal grains are in granular , angular and cataclastic shapes , with size of 2 ~ 5 μ m.

一种粒状活性炭的RDF研究

Studies on a particulate active carbon

BAF采用多种粒状滤料，具有吸附、过滤、微生物降解等功能。

It also has filtering , adsorption , biodegradation and other functions .

在一定条件下，粒状高能固体火药填充床中，将出现DDT现象。

Under certain conditions , DDT can occur in the high-energy granulated solid propellant beds .

外板展开图程序1000kt/a粒状DAP联产200kt/a粉状MAP扩能方案剖析

Capacity Expansion Plan Analysis of 1000 kt / a Granular DAP with Joint Production of 200 kt / a Powder MAP

在含钨高速钢中加入1.5%Nb，将使晶粒内部弥散的粒状MC型碳化物增加。

Adding 1.5 % Nb into the HSS containing W would increase the amount of granular MC carbides dispersed inside grains .

采用Nb和B合金化，在热轧状态下可得到由贝氏铁素体基体和均匀分布的M/A组元组成的粒状贝氏体组织。

Granular bainitic structure formed by bainitic ferrite matrix and uniformly distributed M / A components can be obtained under hot-rolling state by means of Nb and B alloying .

介绍粒状线性低密度聚乙烯（以下简称LLDPE）在国产单螺杆挤出机加工试验和相应的工艺技术。

The paper introduces the processing test and technique of particle LLDPE on single-screw extruder made in China .

制备了粒状γFe2O3微粉。

The granular γ Fe 2O 3 powders are prepared .

通过添加不同有机模板剂，采用均相沉淀法，制备了粒状、柱状、晶须状、片状、多孔状羟基磷灰石（HAP）。

Granular , cylinder , whisker , flake and porous hydroxyapatites ( HAP ) were synthesized by template-mediated / homogeneous-precipitation .

生产粒状NPK复合肥的改良美国TVA法

Modified TVA process for producing NPK compound fertilizer

冷冻时，食物未冻水相中高浓度的盐作用于粒状体，使其释出低密度脂蛋白（LDL）。

The granules were disrupted by the high concentration of salts in unfrozen phase and release the low density lipoproteins ( LDL ) .

用自装的BET容量法装置测定了几种粒状钛型吸附剂的比表面及其孔径分布。

The determination of the specific surface area and the pore size distribution for Ti-type granular adsorbents was carried out with a home-made apparatus based on BET volumetric methods .

从a带到e带总的趋势是：（1）随着石英斑晶粒径渐大和晶形渐好，岩石结构从等粒状变为似斑状；

General trends from zone a to zone e are : ( 1 ) With quartz phenocrysts progressively larger in size and better in crystal perfectness , the rock texture changes from equigranular to porphyroidal ;

结果表明，玻璃A中的结石主要为氧化铝（αAl2O3）晶体，黄褐色，粒状，晶粒大，来源于耐火材料。

The results show that the granular stones with yellow brown color in glass A are alumina (α Al 2O 3 ), which originate from fireproof material .

通过化学成分的优化，N、Cr等元素的加入和变质处理等措施，得到在稳定性较低的奥氏体基体上弥散分布有粒状碳化物的铸态组织。

By means of optimum chemical compositions , additions of N , Cr into the melt and modification procedure , an as-cast structure with metastable austenite matrix and relatively even distribution of carbide particles was obtained .

实验发现，深过冷NiP共晶合金的凝固组织由粒状的共晶团和棒状的规则共晶所组成。

The experimental results indicated that solidification microstructure of undercooled Ni P eutectic alloy was both particle like eutectic groups and regular eutectic structure .

本文对粒状活性炭吸附法和臭氧一活性炭吸附法两种处理流程（简称C流程和O3+C流程）进行了从饮用水中去除三态氮的对比试验。

In the paper , two different processes , granular activated carbon adsorption (" C " process ) and Ozonation-activated carbon adsorption (" O_3 + C " process ), were studied experimentally for removal of three forms of nitrogen from potable water on a comparative way .

（M-A）相的存在证明102钢正火态组织是粒状贝氏体。

Furthermore , the existance of ( M-A ) phase shows that the normolized microstructure is granular bainite in 102 steel .