而这些小剂量的邻苯二酚好像对硅酸三钙（C3S）的水化没有影响。

These small dosages of pyrocatechol seem not to affect tricalcium silicate ( C3S ) hydration .

总结了以硅酸三钙（C3S）为主要矿物的熟料烧成研究成果和最新研究进展。

Tricalcium silicate ( C_ ( 3 ) S ) is the largest amount constituent and the best cementing property in portland cement clinker .

两种高活性矿物的共存：但是当熟料中CaF2掺量过高、该体系熟料中很容易形成含氟的硅酸三钙固溶体。

When the content CaF2 doped in the clinker is too high , a solid solution of C3S containing F would be very easily formed .

通过X射线衍射定性及定量分析测定了养护后样品的组成及水泥中硅酸三钙（3CaO·SiO2，C3S）、硅酸二钙（2CaO·SiO2，C2S）的水化率；

The phase composition and the hydration rate of C3S and C2S were tested by X-ray powder diffraction and quantitative analysis .

研究了由于铝率变化，导致液相性质的改变，及其对高硅酸三钙（C3S）含量硅酸盐水泥熟料烧成过程和亚微观结构的影响。

The liquid properties variation caused by alumina modulus ( IM ) and their influence on burning process and microstructures of tricalcium silicate ( C_ ( 3 ) S ) - rich portland clinkers were investigated .

高硅酸三钙硅酸盐水泥熟料组成及性能的研究

Composition and property of a high tricalcium silicate cement clinker

目的：评价硅酸三钙对牙本质小管的阻塞能力。

Objective : To evaluate the tubule occluding ability of tricalcium silicate .

水泥熟料中硅酸三钙晶体结构的研究

Exploration for effect on crystal structure of tricalcium silicate of cement clinker

高硅酸三钙水泥硬化砂浆干缩过程

Drying shrinkage process of hardened high tricalcium silicate cement mortar

铝率及液相性质对高硅酸三钙含量硅酸盐水泥熟料烧成过程的影响

Influence of alumina modulus and liquid properties on burning process of tricalcium silicate-rich Portland clinkers

转炉渣的质量可由硅酸三钙和游离石灰量大体鉴别，以便分级管理和充分利用。

The quality of the slag was graded by its content of tricalcium silicate and free lime .

硅酸三钙阻塞牙本质小管的实验研究经牙本质小管失活牙髓的疗效观察

Occluding Effect of Tricalcium Silicate Cement on Dentinal Tubules Observation on deactivation dental pulp by putting pulp devitalizer into dental pulp via dentinal tubule

热泼法预处理钢渣中含大量不稳定的较大颗粒硅酸三钙相，易析出游离氧化钙，不宜直接资源化利用；

When pretreated by hot splash method , the slag will contain a great amount of instable large tricalcium silicate particles which are apt to release free calcium oxide , and is therefore unsuitable for direct utilization as a resource ;

硅酸三钙在磷渣浸泡液中水化的第一个放热峰明显比在水中水化的第一个放热峰低，而且诱导期延长，推迟了第二个放热峰的出现。

By comparison with the hydration of tricalcium silicate soaking in the water solution , the first exothermic peak of immersing in the phosphate slag solution is obviously lower , and the induction period prolongs , which consequently delays the appearance of the second exothermic peak .