木棉纤维

  • 网络Kapok Fiber
木棉纤维木棉纤维
  1. 通过实验表征了国产木棉纤维的基本结构和性能。

    The structures and performances of the native kapok fibers were studied .

  2. 直接染料对木棉纤维的染色吸附特征

    Dyeing and adsorption character of kapok fiber with direct dyes

  3. 棉与木棉纤维含量测定的不确定度评定

    Evaluation of uncertainty in determination of fiber content in cotton / kapok blends

  4. 天然的保暖纤维&木棉纤维

    Kapok Fiber : A Green Natural Thermal Fiber

  5. 木棉纤维性能及其可纺性的探讨

    On Characteristics and Spinnability of Kapok Fiber

  6. 木棉纤维的基本结构和性能

    Structures and performances of the kapok fiber

  7. 木棉纤维的特征与应用前景

    Characters and Application Prospects of Kapok Fiber

  8. 木棉纤维结构和性能及其集合体的浸润与浮力特征研究

    Structures and Properties of Kapok Fiber and the Wettability and Buoyancy Characteristics of Kapok Fibrous Assemblies

  9. 木棉纤维壁薄,具有高达97%的中空率,壁厚不均匀,纵向表面有微小凸痕。

    The kapok fiber has thin wall and huge lumen , the hollow ratio can reach 97 % .

  10. 木棉纤维的微细结构研究&胞壁层次结构与原纤尺度

    Study on the Fine Structure of the Kapok Fiber & The Structure of Cell Walls and the Sizes of Fibrils

  11. 新型木棉纤维集合体的浮力性能(英文)GB15359-1994中国海区灯船和大型浮标制式

    The buoyancy performance of new-type fibrous assemblies of kapok " Maritime light vessels and large buoys system , China "

  12. 通过对木棉纤维和涤纶单中空纤维中空率、圆整度进行测试,证明本技术具有良好的保形性能。

    The hollowness and circularity measuring from the slices of hollow polyester fiber and kapok proved this method has best form-keeping .

  13. 所测木棉单纤维密度达0.30gcm3,主要由纤维素和木质素组成,结晶度为35.9%,双折射率为0.017,其胞壁结构较棉纤维疏松。

    The bulk density of the fiber is 0 ^ 30 g / cm3.The kapok fiber mainly consists of cellulose and lignin , the crystallization degree is 35 ^ 90 % and the specific birefringence is 0 ^ 017.The structure of the cell wall is looser than that of cotton .

  14. 该工艺方法目前很容易实现工业化生产;(3)木棉/粘结纤维的一次成形块体有很好的浮力性能,而且不产生边角料,制成率高。

    It is easy to make it real for industrial production ;( 3 ) The first forming block made by Kapok / tacky fiber has a good floating performance , and no scrap material is left , so the producing ratio is high .

  15. 木棉基活性炭纤维的结构与吸附性能

    Structure and adsorptive properties of kapok-based activated carbon fiber

  16. 最后对木棉和涤纶中空纤维截面树脂切片和哈氏切片的显微图像及其纤维截面特征参数和分布进行对比,并给出部分纺织纤维截面切片图像。

    The micrographs of resin slice and Hardy ′ s thin cross-sections of hollow polyester fiber and kapok are obtained and their cross-section characteristic parameters are compared . And micrographs of cross-sections of some textile fibers are presented .

  17. 东印度群岛的一种木棉树,生产次于木棉的纤维。

    East Indian silk cotton tree yielding fibers inferior to kapok .

  18. 介绍了木棉的基本特性,并就成纱质量、纺纱加工方法探讨了木棉纤维的可纺性,最后对木棉纺织产品作了简要介绍。

    This paper introduces the basic characteristics of kapok fiber , discusses its spinnability from two aspect of yarn quality and spinning process method and ended with a brief introduction of the kapok fiber textile products .