tbsi

  • 网络促进剂;次磺酰亚胺;次磺酰胺;酰亚胺;苯并噻唑次磺酰亚胺
tbsitbsi
  1. Study on Application of New Accelerator TBSI in Butadiene Acrylonitrile Rubber

    新型硫化促进剂TBSI在丁腈橡胶中的应用研究

  2. Synthesis and Application Prospects of Rubber Accelerator TBSI

    橡胶促进剂TBSI的合成及其应用前景

  3. Mice in the TBSI group were fixed under anesthesia and shielded with lead bricks .

    全身屏蔽照射组麻醉固定,用铅砖屏蔽全身。

  4. Reading Comprehension Synthesis of accelerator TBSI

    促进剂TBSI合成研究

  5. The application of TBSI accelerator in upper bead filler and carcass compounds of BTR tire was investigated .

    研究促进剂TBSI在全钢载重子午线轮胎上三角胶和胎体胶中的应用。

  6. The vulcanization behavior , storage stability of novel cure accelerator TBSI in SBR 1500 and the mechanical properties of its vulcanizate were studied .

    研究了新型硫化促进剂TBSI在丁苯橡胶中的硫化特性、贮存稳定性及其硫化胶的物理机械性能。

  7. The application of accelerator TBSI in carcass ply compound of TBR tire was experimentally investigated and compared to those of accelerator TBBS or DCBS by equal weight or less weight respectively .

    试验研究促进剂TBSI在全钢子午线轮胎胎体胶中的应用效果,并分别与促进剂NS和DZ进行等量和减量对比。

  8. And the scorch time extended , t_ ( 90 ) reduced , the permanent tensile set decreased and the H pull-out changed little using 1 phr of TBSI instead of 1.25 phr of DCBS in the carcass compound .

    在胎体胶配方中以1份促进剂TBSI替代125份促进剂DZ,胶料的焦烧时间延长,t90缩短,硫化胶的拉断永久变形减小,H抽出力相当。

  9. The ability of vulcanization reversion resistance of TBSI / TMTD was better than that of NS . After 4h over cure , their modulus at 300 % elongation was retentive of about 80 % and less than 60 % respectively .

    经4h过硫化反应后,TBSI/TMTD体系的300%定伸应力保持约80%,而NS不足60%。