CHDM

  • 网络环己烷二甲醇;环己二甲醇;二甲醇酯;环已烷二甲醇;环己二醇
CHDMCHDM
  1. Chemical Structural Characterization of PETG and Measurement of CHDM Content

    PETG化学结构的表征和CHDM含量的测定

  2. The crystallization ability of PETG copolyester and its fiber strength decrease with the increasing of CHDM content .

    随CHDM含量的增加,共聚酯结晶性能下降,纤维强度下降。共聚酯纤维具有优异的弯曲回弹性和染色性能,且随CHDM含量的增加而提高。

  3. The effects of CHDM content and isomer ratio on the thermal properties of PETG were studied by DTA and DSC .

    采用DTA,DSC等手段研究了不同CHDM含量及其异构体比例对PETG热性能的影响。

  4. When the content of CHDM in PECT copolyester increased the copolyester Tg increased in line , Tm , Tc decreased , crystal speed become quick .

    PECT共聚酯随着CHDM含量的增加,Tg线形增加,Tm下降,冷结晶温度Tc降低,结晶速率变快。

  5. Series of 1,4-cyclohexane dimethanol ( CHDM ) and IPA modified poly ( ethylene terephthalate ) copolymers were synthesized according to different IPA and CHDM content .

    采用1,4-环己烷二甲醇(CHDM),间苯二甲酸改性PET,按照不同的CHDM,IPA含量合成出了一系列共聚酯。

  6. Partially substituting for ethylene glycol ( EG ), 1,4-cyclohexanedimethanol ( CHDM ) was copolymerized with terephthalic acid ( PTA ) to produce copolyesters ( PETG ) .

    以1,4-环己烷二甲醇(CHDM)部分替代乙二醇(EG)与对苯二甲酸(PTA)共聚合成共聚酯(PETG)。

  7. The cooling crystallization peak of PETG could be observed at the temperature of 185-120 ℃ when the molar fraction of CHDM was not more than 13 . 6 % , and only at the cooling rate of 2 ℃ / min could the crystallizing exothermic peak be observed .

    CHDM的摩尔分数不高于13.6%时,在185-120℃范围内可以观察到PETG的冷却结晶峰,而且只有在2℃/min冷却速率下才能观察到结晶放热峰。