Ways to low painting cost of electrophoresis coatings fluororesin coatings

降低电泳涂装成本的途径氟树脂涂料及其应用

Fluororesin Emulsion Based Multilayer Coatings

氟树脂乳液复层涂料的研制

Fluororesin coatings are becoming more and more popular for their excellent properties .

氟树脂涂料由于其优良的各项性能而越来越受到人们的青睐。

Research Situation and Prospect of the Anticorrosive Coating of Fluororesin / PPS by Mixing Modification

氟树脂/聚苯硫醚共混改性防腐涂层的研究现状及展望三溴苯基缩水甘油醚对聚醚聚氨酯的阻燃改性

Study on Acrylic Acid Polyurethane Paint with Seawater Resistance and High Weatherproofing Modified by Fluororesin

氟树脂改性丙烯酸聚氨酯耐海水高耐候面漆研究

An undercoat for fluororesin coating based on epoxy resin and polyamide hardener .

聚氨酯固化的环氧树脂涂料，氟树脂面漆的配套用中间漆。

Room temperature curable fluororesin coatings

常温固化型氟树脂涂料

Super Weather Resisting Fluororesin Coating

超耐候性氟树脂涂料

The mechanical properties , chemical resistance and weathering performance of a white enamel based on this resin are similar other fluororesin coatings . ATMOSPHERIC WEATHERING PERFORMANCE OF ENGINEERING PLASTICS

配成白色磁漆后，机械性能、耐介质性能及耐候性与其他含氟树脂所制磁漆相当。工程塑料自然老化试验研究

Productions and Applications of Fluororesin and Fluoroplastics

氟树脂及塑料生产与应用

Paint remover Fluororesin Coatings

氟树脂涂料及其应用

Anti-corrosion and weatherability of fluororesin paint

氟树脂涂料耐腐蚀及耐老化性能

The results show that during the curing of fluororesin , the fluorinated groups have strong tendency and stretch to the interface of air and polymer , which protect the inner molecule of polymer better .

试验结果表明：通过分子设计合成的氟树脂成膜时产生了较大趋向作用，含氟基团向空气/聚合物界面伸展，对聚合物内部分子形成很好的保护作用；

The characteristics and applications of common heavy duty anticorrosion coatings have been described and some new types of coatings are recommended such as flake glass coating , solvent-free polyurethane coating and fluororesin coating .

论述了重防腐蚀常用的各类涂料的特性和应用。推荐了一些新型重防腐蚀涂料，例如玻璃鳞片涂料、无溶剂型聚氨酯涂料和氟树脂涂料。

While fluororesin is used as the core of POF , it can reduce the loss of POF , im - prove the temperature resistance , bandwidth and permanence of POF .

氟树脂用作POF芯材时，可降低POF的传输损耗，提高POF的耐温性、POF的传输带宽和POF的耐老化性能等，透明氟树脂是优异的POF芯皮材。

The results indicated that the poor adhesion of fluororesin coatings to metallic substrates was changed obviously by PPS , the bonding strength of single coating of blended PPS / FEP ( interlayer 1 ) was 8.31MPa ;

结果表明，PPS明显改善了单纯氟树脂涂层对金属的不粘性，PPS/FEP共混单层涂层（中间层1）的结合强度可达831MPa；

The effect of silane coupling agents , emulsion composition and glass cloth on flexural strength of composites was studied . Furthermore , the effect of glass cloth content on peel strength of composites and effect of fluororesin content on dielectric of composites were also investigated .

实验中考察了偶联剂的种类和用量、乳液配比、玻璃布的种类对覆铜板弯曲强度的影响，玻璃布含量对剥离强度的影响，以及树脂含量对电性能的影响。